Environment-friendly antique imitation porcelain with firewood-calcined porcelain imitation texture and production method thereof

A kind of texture and firewood burning technology, which is applied in the field of ceramic manufacturing, can solve the problems of large quantity of firewood, low processing efficiency, and low yield rate, and achieve the effects of good environmental protection, resource saving, and short firing time

Active Publication Date: 2017-01-25
FUJIAN QUANZHOU LONGPENG GROUP
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Wood-burning utensils have a unique artistic effect, but during production, firewood needs to be continuously added to the kiln, and the kiln usually takes three to five days, so it consumes a large amount of firewood, and the processing efficiency is low. The efficiency is low. If modern technology can be used to provide a kind of porcelain with wood-fired texture, it can not only meet people's demand for wood-burning vessels, but also reduce the consumption of firewood, improve production efficiency, and play a positive role in energy conservation and environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0026] Environmentally friendly antique porcelain with wood-fired texture, including the green body and the glaze set on the green body;

[0027] The weight of the glaze is as follows: 26 parts of quartz, 14 parts of potassium feldspar, 13 parts of albite, 13 parts of dolomite, 9 parts of limestone, 10 parts of rutile, 7 parts of iron, 5 parts of barium carbonate, and 3 parts of manganese;

[0028] The weight of the green body is as follows: red loam 38, clay 24, diatomite 21, calcined talc 8, purple clay 8, sodium bentonite 4.

specific Embodiment 2

[0030] Environmentally friendly antique porcelain with wood-fired texture, including the green body and the glaze set on the green body;

[0031] The weight of the glaze is as follows: 28 parts of quartz, 12 parts of potassium feldspar, 14 parts of albite, 14 parts of dolomite, 7 parts of limestone, 8 parts of rutile, 8 parts of iron, 7 parts of barium carbonate, and 2 parts of manganese;

[0032] The weight of the green body is as follows: red loam 32, clay 28, diatomite 25, calcined talc 6, purple clay 7, sodium bentonite 2.

specific Embodiment 3

[0034] Environmentally friendly antique porcelain with wood-fired texture, including the green body and the glaze set on the green body;

[0035] The weight of the glaze is as follows: 25 parts of quartz, 13 parts of potassium feldspar, 11 parts of albite, 15 parts of dolomite, 6 parts of limestone, 6 parts of rutile, 10 parts of iron, 9 parts of barium carbonate, and 5 parts of manganese;

[0036] The weight of the green body is as follows: red loam 35, clay 22, diatomite 28, calcined talc 9, purple clay 5, sodium bentonite 1.

[0037] A kind of manufacture method of the environment-friendly antique porcelain of imitation firewood texture, prepare the environmental protection antique porcelain of imitation firewood texture described in any one of above-mentioned specific embodiment 1 to 3, concrete steps are as follows:

[0038] Step 1, batching and weighing, batching, crushing, and removing impurities according to the raw material components of the environmentally friendly a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of production of porcelains and particularly relates to an environment-friendly antique imitation porcelain with firewood-calcined porcelain imitation texture and a production method thereof. According to the environment-friendly antique imitation porcelain with firewood-calcined porcelain imitation texture and the production method thereof, low-cost raw materials are taken as the raw materials of a blank and a glaze material of the environment-friendly antique imitation porcelain with the firewood-calcined porcelain imitation texture, the raw materials are proportioned and a calcining process is controlled to obtain the environment-friendly antique imitation porcelain, the calcined environment-friendly antique imitation porcelain has the texture like a firewood-calcined porcelain, the surface of the calcined environment-friendly antique imitation porcelain has uneven metallic luster, and through control of the firing temperature and change of the firing atmosphere, the texture change on the surface of each porcelain is unique. The raw materials of the environment-friendly antique imitation porcelain are simple; compared with the firewood-calcined porcelain, the environment-friendly antique imitation porcelain has the characteristics of short calcining time, no combustion of firewood and high environmental friendliness; the environment-friendly antique imitation porcelain is of great significance on reduction of environmental pollution, development of cyclic economy and construction of resource-saving and environment-friendly society.

Description

technical field [0001] The invention relates to the technical field of ceramic manufacturing, in particular to an environment-friendly antique porcelain with wood-fired texture and a manufacturing method thereof. Background technique [0002] Modern wood burning is an ancient and modern technique. It uses natural wood as fuel. The ashes and flames produced by wood burning in the kiln process directly enter the kiln and adhere to the green body. When the temperature reaches above 1200 degrees Celsius At the same time, it will form a warm, glossy and rich-layered natural ash glaze. In the firewood kiln, the melted or unmelted wood ash forms a smooth or rough texture on the surface of the green body, and changes in various colors, which are natural and without whitewashing, showing a kind of simple, simple, and original beauty. , the works will not be repeated and it is difficult to predict the effect after the kiln, each vessel is unique. [0003] Wood-burning utensils have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/18C04B33/13C04B33/04C04B41/86C04B33/34
CPCC03C8/18C04B33/04C04B33/13C04B33/34C04B41/5022C04B41/86C04B2235/3418C04B2235/963C04B41/4535
Inventor 苏康福
Owner FUJIAN QUANZHOU LONGPENG GROUP