Anti-aging and anti-cold-shortness wood plastic composite material

A wood-plastic composite material and anti-aging technology, which is applied in the field of wood-plastic composite materials, can solve the problems of small space for users to choose, single variety of plastic-wood materials, and unsatisfactory performance, and achieve the effect of good strength

Inactive Publication Date: 2017-02-01
安徽钰锦生态木材料有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The performance of existing WPC products is still not ideal, and there are still some defects, such as the texture uniformity, density, water absorption and other parameters of WPC panels sti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of anti-aging and anti-cold and brittle wood-plastic composite material, including the following components by weight: 40 kg of maleic anhydride grafted polypropylene, 35 kg of straw, 5 kg of polyethylene, 3.5 kg of polyphenylene ether, 2 kg of benzoin, mica Powder 4kg, zinc borate 2kg, asbestos 5.5kg, walnut shell powder 5kg, camphor wood powder 8kg, ginkgo leaf 6kg, arboria chinensis powder 6kg, agarwood powder 0.1kg, 3-hydroxybenzoic acid 4 ㎏, 1 kg of lauryl alcohol sulfate, 4 kg of plant saponin, 0.1 kg of terpineol, 1 kg of white latex.

[0018] Its preparation method comprises the following steps:

[0019] (1) Graft maleic anhydride to polypropylene 40kg, straw 35kg, polyethylene 5kg, polyphenylene ether 3.5kg, benzoin 2kg, mica powder 4kg, zinc borate 2kg, asbestos 5.5kg, walnut shell Powder 5kg, Camphorwood powder 8kg, Ginkgo biloba leaf 6kg, Alder wood powder 6kg, Agarwood powder 0.1kg, 3-Hydroxybenzoic acid 4kg, Lauryl sulfate 1kg, Plant saponin 4kg ,...

Embodiment 2

[0023] A kind of anti-aging and anti-cold and brittle wood-plastic composite material, including the following components by weight: 65 kg of maleic anhydride grafted polypropylene, 45 kg of straw, 8 kg of polyethylene, 4.5 kg of polyphenylene ether, 3 kg of benzoin, mica Powder 6kg, zinc borate 2.5kg, asbestos 7.5kg, walnut shell powder 7kg, camphor wood powder 10kg, ginkgo leaf 8kg, arboria chinensis powder 8kg, agarwood powder 0.2kg, 3-hydroxybenzoic acid 6 ㎏, Lauryl Sulfate 2㎏, Plant Saponin 6㎏, Terpineol 0.2㎏, White Emulsion 3Kg.

[0024] Its preparation method comprises the following steps:

[0025] (1) Maleic anhydride grafted polypropylene 65kg, straw 45kg, polyethylene 8kg, polyphenylene ether 4.5kg, benzoin 3kg, mica powder 6kg, zinc borate 2.5kg, asbestos 7.5kg, walnut shell Powder 7kg, Camphorwood powder 10kg, Ginkgo biloba leaf 8kg, Alder wood powder 8kg, Agarwood powder 0.2kg, 3-Hydroxybenzoic acid 6kg, Lauryl sulfate 2kg, Plant saponin 6kg , 0.2kg of terpineol...

Embodiment 3

[0029] A kind of anti-aging and anti-cold and brittle wood-plastic composite material, including the following components by weight: 50 kg of maleic anhydride grafted polypropylene, 40 kg of straw, 6 kg of polyethylene, 4 kg of polyphenylene ether, 3 kg of benzoin, mica Powder 5kg, zinc borate 2kg, asbestos 6kg, walnut shell powder 6kg, camphor wood powder 9kg, ginkgo leaf 6kg, arboria chinensis powder 6kg, agarwood powder 0.1kg, 3-hydroxybenzoic acid 6 ㎏, 1 kg of lauryl alcohol sulfate, 6 kg of plant saponin, 0.2 kg of terpineol, 1 kg of white latex.

[0030] Its preparation method comprises the following steps:

[0031] (1) 50 kg of maleic anhydride grafted polypropylene, 40 kg of straw, 6 kg of polyethylene, 4 kg of polyphenylene ether, 3 kg of benzoin, 5 kg of mica powder, 2 kg of zinc borate, 6 kg of asbestos, and walnut shells 6kg of powder, 9kg of camphor powder, 6kg of ginkgo biloba, 6kg of alder wood powder, 0.1kg of agarwood powder, 6kg of 3-hydroxybenzoic acid, 1kg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-aging and anti-cold-shortness wood plastic composite material which includes, by weight, 40-65 parts of maleic anhydride grafted polypropylene, 35-45 parts of straw, 5-8 parts of polyethylene, 3.5-4.5 parts of polyphenyl ether, 2-3 parts of benzoin, 4-6 parts of mica powder, 2.0-2.5 parts of zinc borate, 5.5-7.5 parts of asbestos, 5-7 parts of walnut shell powder, 8-10 parts of camphor wood powder, 6-8 parts of folium ginkgo, 6-8 parts of powder of aralia echinocaulis, 0.1-0.2 parts of agalloch powder, 4-6 parts of 3-hydroxybenzoic acid, 1-2 parts of lauryl sulfate, 4-6 parts of plant saponin, 0.1-0.2 parts of terpilenol and 1-3 parts of white latex. The wood plastic composite material can release a delicate fragrance continuously, has high strength and has anti-aging, anti-cold-shortness, corrosion-prevent and mildew-proof performances, can be used both indoor and outdoor, has the anti-aging effect and is free of cracking and deformation.

Description

technical field [0001] The invention belongs to the technical field of wood-plastic material production, in particular to an anti-aging and anti-cold brittle wood-plastic composite material. Background technique [0002] Building materials refer to the general term for various materials used in the field of construction and civil engineering, referred to as "building materials". Building materials in a narrow sense refer to materials used in civil engineering, such as steel, wood, glass, cement, paint, etc. Cement, steel and wood are usually called the three major materials of general construction engineering. Building materials in a broad sense also include materials used in construction equipment, such as wires and water pipes. "Building materials" in the discipline of architecture refers to the discipline that studies the physical and chemical properties of different building materials. [0003] The floor, that is, the surface layer of the ground or floor of the house, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L51/06C08L97/02C08L23/06C08L71/12C08K13/04C08K3/34C08K3/38C08K7/12C08K5/13
CPCC08L51/06C08L2205/025C08L2205/035C08L2205/16C08L97/02C08L23/06C08L71/12C08K13/04C08K3/34C08K2003/387C08K7/12C08K5/13
Inventor 汪漭
Owner 安徽钰锦生态木材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap