Preparation method of butyronitrile gloves

A technology of nitrile gloves and hand molds, applied in gloves, clothing, protective clothing, etc., can solve the problems of increasing nitrile gloves, affecting the accuracy of operation, affecting product performance, etc., and achieving increased cleanliness, convenient wearing, and simplified processing. the effect of the program

Active Publication Date: 2017-02-15
SUZHOU HONBEST CLEAN TECH CO LTD
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are many varieties of nitrile gloves. Nitrile gloves are mainly made by dipping nitrile latex, molding, vulcanization, surface treatment, dust-free cleaning and other processes. They have excellent puncture resistance, chemical resistance, friction resistance and Durable wearing force, chlorine washing is generally required in the demoulding process after nitrile gloves are molded to remove the stickiness of the glove surface and facilitate the wearing of gloves, but this will increase the chlorine content in nitrile gloves, and when the operator wears nitrile gloves When the gloves are used for specific process operations, a small amount of chlorine elements will penetrate into the gloves, which will affect the accuracy of the operation; in addition, dust particles will adhere to the surface of the nitrile gloves during preparation, and the falling of dust particles will also have a great impact on the performance of the produced products. Great impact, so the cleanliness of nitrile gloves also need to be strictly controlled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In parts by weight, weigh 50 parts of nitrile latex, 0.6 parts of potassium hydroxide, 40 parts of deionized water, 1 part of sulfur, 1.5 parts of zinc oxide, 0.3 parts of accelerator, 1 part of antistatic Agent, 0.2 parts of anti-aging agent, 2 parts of stabilizer, 0.3 parts of titanium dioxide, and 1 part of defoamer are used as latex raw materials for nitrile gloves; adjust the production line to make it run normally, start production, and acidify the hand mold Washing, first water washing, alkali washing, second water washing, and then drying the hand model; placing the cleaned hand model in chlorine water with a mass concentration of 3% for 20 minutes, and then washing the hand model after chlorine The mold is dipped in a calcium nitrate coagulant solution with a mass concentration of 4%; after drying, place the dipped hand mold in the latex raw material of nitrile gloves for dipping; wash the dipped film with pure water , after drying, put it in DI water with a co...

Embodiment 2

[0034] In parts by weight, weigh 30 parts of nitrile latex, 0.8 parts of potassium hydroxide, 35 parts of deionized water, 1.5 parts of sulfur, 1 part of zinc oxide, 0.2 parts of accelerator, 2 parts of antistatic Agent, 0.1 part of anti-aging agent, 1.2 part of stabilizer, 0.2 part of titanium dioxide, and 1.6 part of defoamer are used as latex raw materials for nitrile gloves; adjust the production line to make it run normally, start production, and acidify the hand mold Washing, the first water washing, alkali washing, the second water washing, and then drying the hand model; placing the cleaned hand model in chlorine water with a mass concentration of 2.7% for 30 minutes, and then washing the hand model with chlorine The mold is dipped in a calcium chloride coagulant solution with a mass concentration of 5%; after drying, place the dipped hand mold in the latex raw material of nitrile gloves for dipping; soak the dipped film with pure water After cleaning and drying, place...

Embodiment 3

[0036]In parts by weight, weigh 60 parts of nitrile latex, 1 part of potassium hydroxide, 45 parts of deionized water, 0.5 parts of sulfur, 1.5 parts of zinc oxide, 0.5 parts of accelerator, 1.8 parts of antistatic Agent, 0.3 part of anti-aging agent, 1 part of stabilizer, 0.1 part of titanium dioxide, and 1.7 part of defoamer are used as latex raw materials for nitrile gloves; adjust the production line to make it run normally, start production, and acidify the hand mold washing, the first washing with water, alkali washing, the second washing with water, and then drying the hand model; placing the cleaned hand model in chlorine water with a mass concentration of 3.5% for 30 minutes, and then washing the hand model with chlorine The mold is dipped in a calcium nitrate coagulant solution with a mass concentration of 3%; after drying, place the dipped hand mold in the latex raw material of nitrile gloves for dipping; wash the dipped film with pure water , after drying, put it i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
electrical resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of butyronitrile gloves, and belongs to the technical field of butyronitrile gloves. The preparation method comprises following steps: a rubber latex raw material of the butyronitrile gloves is prepared; a hand mould is subjected to acid pickling, a first time of water washing, alkali washing, a second time of water washing, drying, and chlorine washing, is immersed in a coagulating agent solution for immersion, and is subjected to impregnation in the rubber latex raw material; and obtained rubber film is subjected to washing and demoulding. According to the preparation method, only one time of chlorine washing is carried out before hand mould impregnation, so that the surfaces of the butyronitrile gloves obtained via impregnation moulding are smooth, the butyronitrile gloves are convenient to wear, no adhesion is caused, processing process is simplified, and the chlorine content of the butyronitrile gloves is reduced greatly; and in addition, DI water is used for washing so as to remove particles and surface ions on the surfaces of the butyronitrile gloves, and the cleanliness of the butyronitrile gloves is improved.

Description

technical field [0001] The invention relates to the technical field of nitrile gloves, in particular to a preparation method of nitrile gloves. Background technique [0002] With the improvement of precision requirements of high-tech products, more and more products are required to be produced, packaged and tested in a dust-free environment, so operators need to wear special dust-free clothing and accessories to ensure a clean environment. As an important part of dust-free clothing and accessories, gloves are widely used in clean rooms. They can not only protect products and production areas from pollution, but also protect operators from harmful components in the production process. Among them, nitrile gloves have many advantages such as adhesion, good ductility, no protein, and no allergies, etc., and are widely used. [0003] At present, there are many varieties of nitrile gloves. Nitrile gloves are mainly made by dipping nitrile latex, molding, vulcanization, surface tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L13/02C08K13/02C08K3/06C08K3/22A41D19/015
CPCA41D19/0062C08K3/06C08K3/22C08K13/02C08K2003/2296C08L2201/04C08L13/02
Inventor 陈建宝
Owner SUZHOU HONBEST CLEAN TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap