Sunblock film for window glass and preparation method of sunblock film

A glass and window technology, which is applied in the field of sunscreen film for window glass and its preparation, can solve the problems of unsafe use, low structural strength, and poor effect of sunscreen film on ultraviolet rays, and achieve long service life and high structural strength , the effect of stable performance

Inactive Publication Date: 2017-02-22
ANHUI KATA DOOR & WINDOW
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Existing sun protection films are not effective in isolating ultraviolet rays, their structural strength is not high, and they are not safe to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A sunscreen film for window glass, made of the following materials in parts by weight: 24 parts of polyethylene, 37 parts of polyvinyl chloride, 6 parts of polyvinylidene chloride, 9 parts of benzotriazole, 7 parts of triazine 5 parts of hindered amine, 13 parts of phenyl phthalate, 4 parts of silicon carbide fiber, 12 parts of polyacrylonitrile-based carbon fiber, 2 parts of airgel felt, 14 parts of polyphenylene sulfide, 7 parts of cellulose ester, 6 parts of polyamide, 7 parts of dithiocarbamate, 11 parts of benzoic acid, 4 parts of perlite powder, 7 parts of silica gel, 12 parts of graphene, 1 part of organic antimony, 3 parts of potassium stearate and 3 parts - 1 part of methyl aminocrotonate.

[0022] A preparation method of a sunscreen film for window glass, comprising the following steps:

[0023] 1) 24 parts of polyethylene, 37 parts of polyvinyl chloride, 6 parts of polyvinylidene chloride, 9 parts of benzotriazole, 7 parts of triazine, 5 parts of hindered am...

Embodiment 2

[0029] A sunscreen film for window glass, made of the following materials in parts by weight: 26 parts of polyethylene, 39 parts of polyvinyl chloride, 10 parts of polyvinylidene chloride, 10.5 parts of benzotriazole, 9.5 parts of triazine 6.5 parts of hindered amine, 14.5 parts of phenyl phthalate, 6 parts of silicon carbide fiber, 13 parts of polyacrylonitrile-based carbon fiber, 2.5 parts of airgel felt, 16 parts of polyphenylene sulfide, 11 parts of cellulose ester, 7 parts of polyamide, 8.5 parts of dithiocarbamate, 13 parts of benzoic acid, 5 parts of perlite powder, 7.5 parts of silica gel, 13 parts of graphene, 1.5 parts of organic antimony, 5.5 parts of potassium stearate and 3 - 2 parts of methyl aminocrotonate.

[0030] A preparation method of a sunscreen film for window glass, comprising the following steps:

[0031] 1) 26 parts of polyethylene, 39 parts of polyvinyl chloride, 10 parts of polyvinylidene chloride, 10.5 parts of benzotriazole, 9.5 parts of triazine,...

Embodiment 3

[0037]A sunscreen film for window glass, made of the following materials in parts by weight: 28 parts of polyethylene, 41 parts of polyvinyl chloride, 14 parts of polyvinylidene chloride, 12 parts of benzotriazole, and 12 parts of triazine 8 parts, 8 parts of hindered amine, 16 parts of phenyl phthalate, 8 parts of silicon carbide fiber, 14 parts of polyacrylonitrile-based carbon fiber, 3 parts of airgel felt, 18 parts of polyphenylene sulfide, 15 parts of cellulose ester, 8 parts of polyamide, 10 parts of dithiocarbamate, 15 parts of benzoic acid, 6 parts of perlite powder, 8 parts of silica gel, 14 parts of graphene, 2 parts of organic antimony, 8 parts of potassium stearate and 3 parts - 3 parts of methyl aminocrotonate.

[0038] A preparation method of a sunscreen film for window glass, comprising the following steps:

[0039] 1) 28 parts of polyethylene, 41 parts of polyvinyl chloride, 14 parts of polyvinylidene chloride, 12 parts of benzotriazole, 12 parts of triazine, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sunblock film for window glass. The sunblock film is prepared from, by weight, 24-28 parts of polyethylene, 37-41 parts of polyvinyl chloride, 6-14 parts of polyvinylidene chloride, 9-12 parts of benzotriazole, 7-12 parts of triazine, 5-8 parts of hindered amine, 13-16 parts of phenyl salicylate, 4-8 parts of silicon carbide fibers, 12-14 parts of polyacrylonitrile-based carbon fibers, 2-3 parts of alison aerogel blankets, 14-18 parts of polyphenylene sulfide, 7-15 parts of cellulose esters, 6-8 parts of polyamides, 7-10 parts of dithiocar-bamate, 11-15 parts of benzoic acid, 4-6 parts of perlite powder, 7-8 parts of silica gel, 12-14 parts of graphene, 1-2 parts of organic antimony, 3-8 parts of potassium stearate and 1-3 parts of methyl 3-aminocrotonate. The sunblock film for the window glass is high in ultraviolet isolating effect, high in structural strength and safe to use.

Description

technical field [0001] The invention relates to a sunscreen film for window glass and a preparation method thereof. Background technique [0002] In architecture, a window is an opening made in a wall or roof to allow light or air to enter a room. In fact, the original meanings of window and door refer to window and door respectively, while in modern Chinese, window refers to window only. "Window" is originally "chimney" ("chimney" is a vulgar character), that is, a hole is left on the wall, and the frame is a window lattice, which can transmit light and smoke, and then add the prefix "xue" to form a pictophonetic character. "Shuowen" says: "The wall is called the chimney, and the house is called the chimney. The window, or the hole." The window frame is responsible for supporting the main structure of the window. It can be made of wood, metal, ceramics or plastic materials, and the transparent part is attached to the window. The frame can be paper, cloth, silk or glass ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08L27/08C08L81/02C08L1/08C08L77/00C08K13/04C08K7/10C08K7/06C08K7/22C08K5/3475C08K5/3492C08K5/134C08K3/04C08K5/59C08K5/098C08K5/17
CPCC08L27/06C08J5/18C08J2327/06C08J2423/06C08L2201/08C08L2203/16C08L2205/02C08L2205/035C08L23/06C08L27/08C08L81/02C08L1/08C08L77/00C08K13/04C08K7/10C08K7/06C08K7/22C08K5/3475C08K5/3492C08K5/1345C08K3/04C08K5/59C08K5/098C08K5/175
Inventor 洪长林
Owner ANHUI KATA DOOR & WINDOW
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com