Novel antibacterial fabric and preparation method thereof

An antibacterial fabric, a new technology, applied in the processing of textile materials, liquid/gas/vapor textile material processing, textile and other directions, can solve the problems of mosquito repellent performance, flame retardant performance and anti-wrinkle performance are not ideal, and achieve good resistance. The effect of flammability, scientific and reasonable proportioning, and high breaking strength

Active Publication Date: 2017-02-22
BEIJING SUKENO RISHENG SOCKS
View PDF7 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, the technical problem to be solved by the present invention is to overcome the defects that the antibacterial fabrics in the prior art are not ideal in terms of moisture-wicking and sweat-wicking performance, mosquito repellent performance, flame-retardant performance and anti-wrinkle performance, thereby providing a new type of antibacterial fabric and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel antibacterial fabric and preparation method thereof
  • Novel antibacterial fabric and preparation method thereof
  • Novel antibacterial fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1. Preparation of antibacterial finishing agent masterbatch:

[0030] (1) Take 13 parts of titanium dioxide according to the following ratio; 10 parts of magnesium oxide; 13 parts of nano-silver; 5 parts of zeolite; 17 parts of o-hydroxybenzoate; mixture;

[0031] (2) Get 9 times the weight of the first mixture of polyethylene terephthalate, blend with the first mixture, extrude with a screw extruder, pelletize, and prepare antibacterial masterbatches, for subsequent use, where blending The temperature is 250-270° C., and the screw rotation speed is 100-200 rpm.

[0032] 2. Preparation of new antibacterial fabrics:

[0033] Take 17 parts of pearl fiber in the following parts by weight; 20 parts of wool fiber / chitin fiber / milk fiber; 21 parts of soybean protein fiber / corn protein fiber / peanut protein fiber; 13 parts of modal fiber; 25 parts of coconut charcoal fiber; 15 parts of tea fiber part; 15 parts of antibacterial finishing agent, add 110 parts of water, mix and...

Embodiment 2-5

[0037] The preparation method of embodiment 2-5 is with embodiment 1, and the proportioning of each component is as follows:

[0038] The distribution ratio of each component of the antibacterial agent in embodiment 2-5 sees the following table 1:

[0039] Each component distribution ratio of the antibacterial agent in table 1 embodiment 2-5

[0040] Example / parts by weight 2 3 4 5 Titanium dioxide nanoparticles (particle size 10-30nm) 10 15 12 14 Magnesium oxide nanoparticles (particle size 10-30nm) 13 11 7 9 Nano silver (particle size 10-30nm) 10 19 16 9 Zeolite 8 2 6 4 phthalates / 2,3-dihydroxybenzophenone 20 25 11 15 N,N-di and phenylacetamide 23 15 27 19

[0041] The distribution ratio of each component of the novel antibacterial fabric in Examples 2-5 is shown in the following table 2:

[0042] Each component distribution ratio of the novel antibacterial fabric in the embodiment 2-5 of table 2

[004...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel antibacterial fabric and a preparation method thereof and belongs to the field of functional textiles. The novel antibacterial fabric comprises, by weight, 10-25 parts of pearl fiber, 11-27 parts of wool fiber, 10-30 parts of corn protein fiber, 8-17 parts of modal fiber, 12-35 parts of coconut charcoal fiber, 8-21 parts of tea fiber and 10-19 parts of antibacterial finishing agent. The novel antibacterial fabric has the functions of comfort, bacterium prevention, mosquito dispelling, moisture conduction, sweat permeability, warmth keeping and the like. Meanwhile, the fabric also has good flame resistance, high crease elasticity and high breaking strength.

Description

technical field [0001] The invention relates to the field of functional textiles, in particular to a novel antibacterial fabric. Background technique [0002] In recent years, people have higher and higher requirements for the comfort, health, safety and environmental protection of clothing fabrics, and more and more functional requirements for safe and efficient antibacterial clothing; in life, people are inevitably exposed to various Under suitable external conditions, these microorganisms will multiply rapidly and spread diseases through contact, etc., affecting people's health and normal work, study and life. Fiber is a porous material, and after superposition and weaving, it will form a multi-layer body with numerous voids, so the fabric is easier to absorb fungi. Antibacterial finishing is to make the fabric have the function of inhibiting the growth of fungi, maintain a hygienic clothing and living environment, and ensure human health. The application of antimicrobi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D04B1/14D04B21/00A41D31/00D02G3/04D02G3/40D06B3/10D06B15/00D06M11/46D06M11/44D06M11/83D06M11/79D06M13/224D06M13/415D06M23/00D06M101/06D06M101/12D06M101/40D03D15/20D03D15/225D03D15/233D03D15/50
CPCA41D31/00D02G3/04D02G3/40D03D15/00D04B1/14D04B21/00D06B3/10D06B15/00D06M11/44D06M11/46D06M11/79D06M11/83D06M13/224D06M13/415D06M16/00D06M23/00D06M2101/06D06M2101/12D06M2101/40D10B2101/12D10B2211/02D10B2211/20D10B2211/26D10B2201/01D10B2201/22
Inventor 陈娟芬陈国强陈东生
Owner BEIJING SUKENO RISHENG SOCKS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com