PVC artificial leather foaming layer and preparation method thereof

A foamed layer, artificial leather technology, applied in textiles and papermaking, etc., can solve the problems of product dimensional stability, dispersibility, no obvious superiority, poor dimensional stability, and poor control of the toughness and strength of PVC foamed layer. , to achieve the effect of enhanced air permeability, enhanced dimensional stability and good softness

Active Publication Date: 2017-02-22
DONGTAI FUAN SYNTHETIC MATERIAL CO LTD
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Generally, when using PVC to prepare the leather foam layer, some fillers, such as calcium carbonate powder, etc., will be added. The filler mainly plays a role in reducing costs. There is no significant advantage in dispersibility, and the toughness and strength of the prepared PVC foam layer are not easy to grasp, and the dimensional stability is not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A PVC artificial leather foam layer, the foam layer comprises the following components by weight: 98 parts of PVC resin powder, 33 parts of polyphenylene ether ketone, 7 parts of nano-alumina, 32 parts of plasticizer, 2.3 parts of stabilizer part, blowing agent 4.2 parts. The plasticizer can be DOP. A method for preparing a PVC artificial leather foam layer, the steps are as follows: (1) Primary heating and mixing: first, polyphenylene ether ketone and nano-alumina are uniformly mixed in a mixing tank according to parts by weight, and are ready for use. The temperature of the mixing tank was kept at 152°C, and the mixing time was 32 minutes. (2) Secondary mixing: Send PVC resin powder, plasticizer, stabilizer, and foaming agent into the mixing kettle according to parts by weight for uniform mixing, and the mixing time is 22 minutes. (3) Three-stage mixing: send the mixture in step (1) and step (2) into the mixing tank for mixing, and the time for mixing in the mixing ...

Embodiment 2

[0019] A PVC artificial leather foam layer, the foam layer includes the following components by weight: 100 parts of PVC resin powder, 35 parts of polyphenylene ether ketone, 6 parts of nano-alumina, 35 parts of plasticizer, 2.5 parts of stabilizer part, foaming agent 4.5 parts. The plasticizer can be DOP. A method for preparing a PVC artificial leather foam layer, the steps are as follows: (1) Primary heating and mixing: first, polyphenylene ether ketone and nano-alumina are uniformly mixed in a mixing tank according to parts by weight, and are ready for use. The temperature of the mixing tank was kept at 160°C, the temperature was controlled at 160°C, and the mixing time was 35 minutes. (2) Secondary mixing: Send PVC resin powder, plasticizer, stabilizer, and foaming agent into the mixing kettle according to the weight part for uniform mixing, and the mixing time is 25 minutes. (3) Three-stage mixing: send the mixture in step (1) and step (2) into the mixing tank for mixin...

Embodiment 3

[0021] A PVC artificial leather foam layer, the foam layer comprises the following components by weight: 103 parts of PVC resin powder, 38 parts of polyphenylene ether ketone, 8 parts of nano-alumina, 38 parts of plasticizer, 2.7 parts of stabilizer part, blowing agent 4.8 parts. The plasticizer can be DOP. A method for preparing a PVC artificial leather foam layer, the steps are as follows: (1) Primary heating and mixing: first, polyphenylene ether ketone and nano-alumina are uniformly mixed in a mixing tank according to parts by weight, and are ready for use. The temperature of the mixing tank was kept at 168°C, the temperature was controlled at 160°C, and the mixing time was 38 minutes. (2) Secondary mixing: Send PVC resin powder, plasticizer, stabilizer, and foaming agent into the mixing kettle according to parts by weight for uniform mixing, and the mixing time is 28 minutes. (3) Three-stage mixing: send the mixture in step (1) and step (2) into the mixing tank for mixi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a PVC artificial leather foaming layer. The PVC artificial leather foaming layer comprises, by weight, 95-105 parts of PVC resin, 30-40 parts of polyphenylene ether ketone, 5-10 parts of nano aluminum oxide, 30-40 parts of plasticizer, 2-3 parts of stabilizer and 4-5 parts of foaming agent. A preparation method of the PVC artificial leather foaming layer includes the steps of firstly, performing primary heating mixing; secondly, performing secondary mixing; thirdly, performing tertiary mixing; fourthly, performing smelting and open milling; fifthly, rolling, and cooling to obtain the PVC artificial leather foaming layer. The PVC artificial leather foaming layer and the preparation method thereof have the advantages that the dimensional stability, strength and toughness of the whole foaming layer are increased, and the foaming layer is good in softness and has certain strength at the same time, and the breathability of the foaming layer is enhanced comprehensively by the porous-structured nano aluminum oxide.

Description

technical field [0001] The invention relates to PVC foamed artificial leather and a preparation method thereof. Background technique [0002] At present, with the rapid development of the clothing industry, people are very enthusiastic about the pursuit of leather clothing, but the price of genuine leather leather clothing is high and difficult to maintain, so the demand for artificial leather and synthetic leather is gradually increasing, and due to the softness of PU synthetic leather Good texture and strong three-dimensional characteristics, so it is widely used in the manufacture of leather clothing. In the synthetic leather industry, a large part of PU synthetic leather is processed by wet kneading process, but with the hydrolysis of PU synthetic leather, the product price is relatively expensive and technical problems such as the inability to produce coarse grain products have appeared. Since 2005 The production of domestic PU synthetic leather has a certain degree of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/06C08L27/06C08L71/10C08K3/22
CPCC08K2201/011C08L27/06C08L2203/14D06N3/005D06N3/0063D06N3/065D06N2209/103D06N2209/123D06N2209/1628D06N2209/1642D06N2211/28C08L71/00C08K2003/2227
Inventor 刘以东徐广梅崔庆何双跃
Owner DONGTAI FUAN SYNTHETIC MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap