Special anti-rust coating for outer surface of rice machine

An anti-rust coating and exterior surface technology, applied in anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of short anti-rust time, rust peeling, poor anti-rust effect, etc. good rust effect

Inactive Publication Date: 2017-03-08
YUEXI COUNTY HONGSHENG CASTING
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Rice machine is a kind of rice production and processing equipment. The types of rice machines include rice milling machine, rice polishing machine, rice cleaning machine and rice thrashing machine, etc. These rice machines usually need to be coated with paint on the surface before leaving the factory. In order to prevent The surface of the rice machine is oxidized and rusted, but the existing paint has a long shelf life, and the rust will fall off after a period of time, the anti-rust time is short, and the anti-rust effect is poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A special antirust coating for the outer surface of a rice machine, the antirust coating is composed of the following components in parts by weight: 35 parts of resin, 12 parts of antimony trioxide, 6 parts of zinc borate, 4 parts of polyethylene glycol, cisbutene 3 parts of dianhydride, 4 parts of trioctyl phosphate, 2 parts of aluminum silicate, 10 parts of metal powder, 7 parts of talcum powder, 7 parts of iron oxide and 12 parts of water.

[0014] The resin type is water-based acrylic modified epoxy resin.

[0015] The metal powder types are iron powder and aluminum powder.

[0016] The type of water is deionized water.

Embodiment 2

[0018] A special antirust coating for the outer surface of a rice machine, the antirust coating is composed of the following components in parts by weight: 40 parts of resin, 13 parts of antimony trioxide, 7 parts of zinc borate, 6 parts of polyethylene glycol, and cisbutene 4 parts of dianhydride, 5 parts of trioctyl phosphate, 3 parts of aluminum silicate, 11 parts of metal powder, 8 parts of talcum powder, 9 parts of iron oxide and 13 parts of water.

[0019] The resin type is polyamide resin.

[0020] The metal powder types are iron powder and copper powder.

[0021] The type of water is deionized water.

Embodiment 3

[0023] A special antirust paint for the outer surface of a rice machine, the antirust paint is composed of the following components in parts by weight: 45 parts of resin, 14 parts of antimony trioxide, 8 parts of zinc borate, 8 parts of polyethylene glycol, cisbutene 5 parts of dianhydride, 7 parts of trioctyl phosphate, 4 parts of aluminum silicate, 12 parts of metal powder, 9 parts of talcum powder, 11 parts of iron oxide and 14 parts of water.

[0024] The resin type is melamine resin.

[0025] The metal powder types are aluminum powder and copper powder.

[0026] The type of water is deionized water.

[0027] By implementing one, implementing two and implementing three antirust coatings prepared by each component, compared with common rice machine antirust coatings, metal powder is added in the present invention to reconcile to increase the quality of prepared antirust coatings, making rice The surface of the machine will not fall off after a long period of time, the ant...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a special anti-rust coating for the outer surface of a rice machine. The coating comprises the following components in parts by weight: 35-45 parts of resin, 12-14 parts of antimony trioxide, 6-8 parts of zinc borate, 4-8 parts of polyethylene glycol, 3-5 parts of maleic anhydride, 4-7 parts of trioctyl phosphate, 2-4 parts of aluminum silicate, 10-12 parts of metal powder, 7-9 parts of talcum powder, 7-11 parts of ferric oxide and 12-14 parts of water. The metal powder is added for blending to increase the quality of the prepared anti-rust coating, the surface of the rice machine can not fall off after a long period of time, the anti-rust time is long, and the anti-rust effect is good.

Description

technical field [0001] The invention relates to a coating, in particular to a special antirust coating for the outer surface of a rice machine. Background technique [0002] Rice machine is a kind of rice production and processing equipment. The types of rice machines include rice milling machine, rice polishing machine, rice cleaning machine and rice thrashing machine, etc. These rice machines usually need to be coated with paint on the surface before leaving the factory. In order to prevent The surface of the rice machine is oxidized and rusted, but the existing coating has a long shelf life, and the rust will fall off after a period of time, the anti-rust time is short, and the anti-rust effect is poor. Contents of the invention [0003] In view of the above technical problems, the present invention provides a special anti-rust coating for the outer surface of the rice machine, adding metal powder for reconciliation to increase the quality of the prepared anti-rust coat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/10C09D5/10C09D7/12C09D4/06
CPCC09D163/10C08K2201/014C09D4/06C09D5/10C09D5/103C09D7/61C09D7/63C09D7/65C08L71/02C08K13/02C08K3/34C08K5/521C08K3/2279
Inventor 刘扬兵
Owner YUEXI COUNTY HONGSHENG CASTING
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More