Bismuth oxybromide and nano zinc stannate heterojunction and preparation method thereof

A nano-zinc stannate, bismuth oxybromide technology, applied in chemical instruments and methods, chemical/physical processes, physical/chemical process catalysts, etc., can solve the problem that the catalytic activity of visible light and the low recombination probability of photogenerated electrons and holes have not yet been seen. , high electron mobility and quantum efficiency, to achieve excellent photocatalytic performance, good light absorption performance, small band gap value

Inactive Publication Date: 2017-03-15
LUOYANG INST OF SCI & TECH
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Zinc stannate (Zn 2 SnO 4 ) As a new type of photoelectric material, its electron mobility and quantum efficiency are high, and the probability of recombination of photogenerated electrons and holes is low. In particular, it should be pointed out that nanostructured zinc stannate has excellent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bismuth oxybromide and nano zinc stannate heterojunction and preparation method thereof
  • Bismuth oxybromide and nano zinc stannate heterojunction and preparation method thereof
  • Bismuth oxybromide and nano zinc stannate heterojunction and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A preparation method of bismuth oxybromide and nano-zinc stannate heterojunction, the heterojunction has a chemical formula and structure of Zn 2 SnO 4 / BiOBr nano powder, the particle size is 20-30nm. The preparation method comprises the following steps:

[0029] Step 1. Weigh a certain amount of sodium hydroxide powder, dissolve it completely in the solvent, stir and dissolve it fully to obtain a sodium hydroxide solution with a concentration of 6mol / L, which is marked as solution A and set aside; the solvent in it It is a mixture of deionized water and absolute ethanol with a volume ratio of 4:1;

[0030] Step two, weigh a certain amount of SnCl 4 ·5H 2 O and Zn(OAc) 2 2H 2 O is dissolved in the solvent to form a mixed solution, and the Sn in the mixed solution prepared after fully stirring and dissolving 4+ with Zn 2+ Concentrations are 0.4mol / L and 0.8mol / L respectively, marked as solution B, for later use; the solvent is a mixture of deionized water and ab...

Embodiment 2

[0039] A preparation method of bismuth oxybromide and nano-zinc stannate heterojunction, the heterojunction has a chemical formula and structure of Zn 2 SnO 4 / BiOBr nano powder, the particle size is 20-30nm. The preparation method comprises the following steps:

[0040] Step 1. Weigh a certain amount of sodium hydroxide powder, dissolve it completely in the solvent, stir and dissolve it fully to obtain a sodium hydroxide solution with a concentration of 6mol / L, which is marked as solution A and set aside; the solvent in it It is a mixture of deionized water and absolute ethanol with a volume ratio of 5:1;

[0041] Step two, weigh a certain amount of SnCl 4 ·5H 2 O and Zn(OAc) 2 2H 2 O is dissolved in the solvent to form a mixed solution, and the Sn in the mixed solution prepared after fully stirring and dissolving 4+ with Zn 2+ Concentrations are 0.4mol / L and 0.8mol / L respectively, marked as solution B, for later use; the solvent is a mixture of deionized water and ab...

Embodiment 3

[0048] A preparation method of bismuth oxybromide and nano-zinc stannate heterojunction, the heterojunction has a chemical formula and structure of Zn 2 SnO 4 / BiOBr nano powder, the particle size is 20-30nm. The preparation method comprises the following steps:

[0049] Step 1. Weigh a certain amount of sodium hydroxide powder, dissolve it completely in the solvent, stir and dissolve it fully to obtain a sodium hydroxide solution with a concentration of 6mol / L, which is marked as solution A and set aside; the solvent in it It is a mixture of deionized water and absolute ethanol with a volume ratio of 6:1;

[0050] Step two, weigh a certain amount of SnCl 4 ·5H 2 O and Zn(OAc) 2 2H 2 O is dissolved in the solvent to form a mixed solution, and the Sn in the mixed solution prepared after fully stirring and dissolving 4+ with Zn 2+ Concentrations are 0.4mol / L and 0.8mol / L respectively, marked as solution B, for later use; the solvent is a mixture of deionized water and ab...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a bismuth oxybromide and nano zinc stannate heterojunction and a preparation method thereof. The heterojunction is nano powder of which the chemical formula structure is Zn2SnO4/BiOBr, and the particle size of the heterojunction is 20-30nm. The preparation method comprises the following steps: preparing a solution A, preparing a solution B, preparing a solvent heat product, preparing Zn2SnO4 nano powder, preparing a suspension C, and preparing the Zn2SnO4/BiOBr nano powder. The nano Zn2SnO4/BiOBr heterojunction is synchronized by using a two-step method, the operation is convenient to implement, and a product prepared through synchronization reaction is high in purity, and is excellent in photocatalytic performance under a visible light condition.

Description

technical field [0001] The invention relates to a heterojunction of bismuth oxybromide and nanometer zinc stannate and a preparation method thereof. Background technique [0002] Heterojunction structures are generally composed of two or more different materials, which often produce many new physical properties that a single material does not have. It needs to be pointed out that heterojunctions with specific nanostructures can benefit from the small Physical and chemical properties such as size effect, surface effect, quantum confinement effect, macroscopic quantum tunnel effect and dielectric confinement effect play a greater role. Nano-heterostructures have attracted great attention in luminescence, solar cells, photocatalysis, and gas sensing. In the previous research results, nano-heterojunction photocatalysts showed excellent photocatalytic performance, which can be attributed to the fast separation rate of photogenerated charge carriers, long lifetime of photogenerat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J27/06C02F1/30C02F101/30
CPCB01J27/06B01J35/004C02F1/30C02F2101/308
Inventor 贾铁昆李继利刘明闵志宇余东升赵军伟付芳孙中亮刘文彬
Owner LUOYANG INST OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap