Organic anti-cracking glass and preparation method thereof

A technology of plexiglass and impact modifier, which is applied in the field of anti-crack plexiglass and its preparation, can solve the problems of plexiglass texture brittleness, low specific gravity, high strength, etc., to increase flexibility and crack resistance, increase resistance Impact and toughness, the effect of increasing impact resistance

Inactive Publication Date: 2017-03-15
安徽亚克力实业有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Plexiglass is commonly known as acrylic, Zhongxuan acrylic, and acrylic. Plexiglass has smooth surface, bright colors, small specific gravity, high strength, corrosion resistance, moisture resistance, light resistance, good insulation performance, and good sound insulation; Crunchy texture

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of anti-crack organic glass, its raw material comprises by weight: 125 parts of methyl methacrylate, 12.5 parts of ethylene glycol dimethacrylate, 4 parts of tributyl citrate, 15 parts of rubber particles, modified 4 parts of montmorillonite, 0.4 part of azobisisobutyronitrile, 0.4 part of benzoyl peroxide, 4 parts of impact modifier, 3 parts of dodecyl mercaptan.

[0017] The preparation method of above-mentioned anti-crack organic glass, comprises the steps:

[0018] S1. Add ethylene glycol dimethacrylate, tributyl citrate, modified montmorillonite, azobisisobutyronitrile, benzoyl peroxide, and dodecyl mercaptan to methyl methacrylate In the ester, ultrasonically disperse, heat up to 68°C, keep warm and stir for 40min, cool down to 12°C in an ice-water bath, let stand for 1.3h, raise the temperature to 52°C, keep warm for 21h, then raise the temperature to 62°C, keep warm for 21h, then raise the temperature to 82°C, Keep warm for 2.5 hours, finally raise the t...

Embodiment 2

[0021] A kind of anti-crack organic glass, its raw material comprises by weight: 100 parts of methyl methacrylate, 14 parts of ethylene glycol dimethacrylate, 3 parts of tributyl citrate, particle diameter is 5 μ m polybutylene acrylate 13 parts of ester particles, 3 parts of vinyltrimethoxysilane modified montmorillonite with a particle size of 120nm, 0.5 parts of azobisisobutyronitrile, 0.3 parts of benzoyl peroxide, methyl methacrylate-butadiene- 5 parts of styrene copolymer, 2 parts of dodecyl mercaptan.

[0022] The preparation method of above-mentioned anti-crack organic glass, comprises the steps:

[0023] S1. Ethylene glycol dimethacrylate, tributyl citrate, vinyltrimethoxysilane modified montmorillonite, azobisisobutyronitrile, benzoyl peroxide, dodecyl sulfide Add alcohol into methyl methacrylate, ultrasonically disperse, heat up to 70°C, keep warm and stir for 35min, cool down to 15°C in an ice-water bath, let stand for 1h, raise the temperature to 55°C, keep warm ...

Embodiment 3

[0026] A kind of anti-crack organic glass, its raw material comprises by weight: 150 parts of methyl methacrylate, 11 parts of ethylene glycol dimethacrylate, 5 parts of tributyl citrate, particle diameter is 3 μ m polybutylene acrylate 17 parts of ester particles, 5 parts of vinyltrimethoxysilane modified montmorillonite with a particle size of 100nm, 0.3 parts of azobisisobutyronitrile, 0.5 parts of benzoyl peroxide, methyl methacrylate-butadiene- 3 parts of styrene copolymer, 4 parts of dodecyl mercaptan.

[0027] The preparation method of above-mentioned anti-crack organic glass, comprises the steps:

[0028] S1. Ethylene glycol dimethacrylate, tributyl citrate, vinyltrimethoxysilane modified montmorillonite, azobisisobutyronitrile, benzoyl peroxide, dodecyl sulfide Add alcohol to methyl methacrylate, ultrasonically disperse, heat up to 65°C, keep warm and stir for 45min, cool down to 10°C in an ice-water bath, let stand for 1.5h, heat up to 50°C, keep warm for 22h, then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses anti-cracking organic glass, prepared from, by weight, 100-150 parts of methyl methacrylate, 11-14 parts of diethylene glycol dimethacrylate, 3-5 parts of tributyl citrate, 13-17 parts of rubber particles, 3-5 parts of modified montmorillonite, 0.3-0.5 part of azodiisobutyronitrile, 3-5 parts of an anti-impact modifier, and 2-4 parts of dodecyl mercaptan. The invention also discloses a preparation method of the organic anti-cracking glass. The anti-cracking organic glass has high toughness and good cracking resistance.

Description

technical field [0001] The invention relates to the technical field of organic glass, in particular to a crack-resistant organic glass and a preparation method thereof. Background technique [0002] Plexiglass is a polymer compound polymerized from methyl methacrylate, abbreviated as polymethyl methacrylate, abbreviated as PMMA. Plexiglass is widely used in daily life, industry, construction, aerospace and other aspects. There are four types of plexiglass: colorless and transparent, colored and transparent, pearlescent, and embossed plexiglass. Plexiglass is commonly known as acrylic, Zhongxuan acrylic, and acrylic. Plexiglass has smooth surface, bright colors, small specific gravity, high strength, corrosion resistance, moisture resistance, light resistance, good insulation performance, and good sound insulation; The texture is crisper. In order to meet people's demand for plexiglass, it is necessary to provide a new plexiglass. Contents of the invention [0003] Base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L33/12C08L33/08C08L51/04C08K13/06C08K9/06C08K3/34C08K5/11C08F220/14C08F222/20
CPCC08F220/14C08K2201/003C08L33/12C08L2205/03C08L33/08C08L51/04C08K13/06C08K9/06C08K3/346C08K5/11C08F222/205
Inventor 邹渊博
Owner 安徽亚克力实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com