A kind of magical glazed tile and production method thereof

A production method and magic glaze technology, applied in the field of building ceramic materials, can solve the problems of single decorative effect, high flexural strength, and weak pattern three-dimensional effect, and achieve the effect of enhanced three-dimensional effect, strong three-dimensional effect and clear pattern edge.

Active Publication Date: 2019-06-04
广东协进陶瓷有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to overcome the problems of the existing candy glaze ceramic tile product decoration, which only depends on spraying candy glaze on the inkjet printing pattern, resulting in a single decorative effect and not strong three-dimensional effect of the pattern. Magic glazed tiles with super strong feeling and production method thereof, the obtained magic glazed tiles have higher bending strength, can effectively avoid cracks on the brick surface, have higher water absorption rate, and can fully absorb the water in cement mortar and solidify when laying , form a greater grip on the wall, prevent falling off, and have good comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of magical glazed tile and production method thereof
  • A kind of magical glazed tile and production method thereof
  • A kind of magical glazed tile and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of production method of magic glazed tile, the steps are as follows:

[0052] 1) Preparation of the ceramic tile body: choose ordinary glazed tile body powder, distribute the material through the material distribution device 11, press and form it through the press device 12, and form a powder base with a thickness of 10.0 mm, and send the powder base to the first firing In system 13, bisque firing is carried out at 1020° C., the firing cycle is 60 minutes, and the thickness of the ceramic tile body obtained after firing is 7.0 mm.

[0053] The chemical composition of the ordinary glazed brick body powder is: silicon dioxide 62wt%, aluminum oxide 17wt%, potassium oxide 0.5wt%, sodium oxide 0.5wt%, calcium oxide 6wt%, magnesium oxide 4wt%, trioxide Ferrous 1wt%, titanium oxide 2wt%, loss on ignition 7wt%;

[0054] 2) Application of bottom glaze and top glaze: apply 110 g of bottom glaze on the ceramic body in step 1) through the first glaze pouring device 21 , and...

Embodiment 2

[0069] A kind of production method of magic glazed tile, the steps are as follows:

[0070] 1) Preparation of the ceramic tile body: choose ordinary glazed tile body powder, distribute the material through the material distribution device 11, press and form it through the press device 12, and form a powder base with a thickness of 15.0mm, and send the powder base to the first firing In system 13, bisque firing is carried out at 1150° C., the firing cycle is 45 minutes, and the thickness of the ceramic tile body obtained after firing is 12.0 mm.

[0071] The chemical composition of the ordinary glazed brick body powder is: silicon dioxide 55wt%, aluminum oxide 19wt%, potassium oxide 3wt%, sodium oxide 3wt%, calcium oxide 6wt%, magnesium oxide 4wt%, ferric oxide 1wt%, titanium oxide 1wt%, ignition loss 8wt%.

[0072] 2) Bottom glaze and top glaze application: 120g of bottom glaze is applied on the ceramic ceramic body through the first glazing device 21 , and 200g of top glaze ...

Embodiment 3

[0089] A kind of production method of magic glazed tile, the steps are as follows:

[0090] 1) Preparation of the ceramic tile body: choose ordinary glazed tile body powder, distribute the material through the material distribution device 11, press the press device 12 to form a powder base with a thickness of 12.0mm, and send the powder base to the firing system 13, Biscuit firing is carried out at 1030° C., the firing cycle is 58 minutes, and the thickness of the ceramic tile body obtained after firing is 9.0 mm.

[0091] 2) The raw materials used in the ordinary glazed brick body powder can be set as the powder in step 1) of Example 1.

[0092] 3) Bottom glaze and top glaze application: 114g of bottom glaze is applied on the ceramic body through the first glazing device 21 , and 196g of top glaze is applied on the bottom glaze through the second glazing device 22 .

[0093] 4) Inkjet printing: inkjet print two-dimensional planar patterns on the surface glaze in step 2) by i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a magical glazed tile and a production method thereof; the production method is to successively spread a bottom glaze and a top glaze on a biscuit fired ceramic body through a glaze pouring device, and ink-jet print on the top glaze by an inkjet printer pattern, and then print matte convex glaze and bright convex glaze on the pattern sequentially through the first and second screen printing devices that are continuously arranged. When the inkjet printing ink does not contain scarlet ink, the third screen printing device Red glaze is printed on the pattern at fixed points, and candy glaze is applied on the brick surface; the invention can obtain glazed bricks with both matte and glossy patterns on the brick surface. The three-dimensional effect is strong, and the pattern is soft and bright. On the brick surface, the matte convex glaze and the bright convex glaze are highly overlapped with the pattern, and the edges are clear. With the embellishment of bright red, the pattern is lifelike. Under the gloss of candy glaze, the four decorative effects make the pattern of the brick surface clear and vivid. The whole brick The surface presents a slightly magical decorative effect.

Description

technical field [0001] The invention relates to the field of building ceramic materials, in particular to a production method of magic glazed tiles and glazed tiles prepared by the method. Background technique [0002] At present, architectural ceramics occupy a pivotal position in the decorative building materials market. Among the architectural decoration materials, glazed tiles are widely favored by the architectural ceramics market. Because of their rich patterns, changeable colors, diverse styles, anti-seepage, convenient cleaning, and good craftsmanship and aesthetics, they are widely used in daily life. in various occasions. [0003] In recent years, candy-glazed tile products have appeared on the market. The tile surface is like a starry sky embellishing the night sky, crystal bright, shining under the light, and has a visual impact. However, most of the candy glaze products on the market just spray a layer of candy glaze on the inkjet printing pattern to achieve a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/14C04B41/89C03C8/12C03C8/02C03C8/04
CPCC03C8/02C03C8/04C03C8/12C04B35/14C04B41/009C04B41/52C04B41/89C04B2235/3201C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3232C04B2235/327C04B2235/96C04B41/504C04B41/5022C04B41/4543C04B41/4572C04B41/4574
Inventor 王辉煌饶平根姚志安蔡翔吉旖陈鹏程
Owner 广东协进陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com