Chlorosulfonated polyethylene compounded hot-melt butyl sealant for hollow glass and preparation method of chlorosulfonated polyethylene compounded hot-melt butyl sealant

A technology of chlorosulfonated polyethylene and sealants, which is applied in the field of sealants, can solve problems such as the inability to improve the strength and comprehensive performance of butyl sealants, and insufficient bonding performance, and achieve excellent deformation resistance, improved stability, and high Effect of Adhesive Properties

Inactive Publication Date: 2017-03-29
天长市永泰密封材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this product has the defect of insufficient bonding performance, and cannot improve the strength and comprehensive performance of butyl sealant, so it still needs to be improved in practical application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A hot-melt butyl sealant for chlorosulfonated polyethylene composite insulating glass, prepared from the following components by weight (kg):

[0014] Butyl rubber 10, polyisobutylene 30, chlorosulfonated polyethylene 3, binary ethylene propylene rubber 5, silane coupling agent A-151 0.5, furfuryl alcohol resin 5, epoxy octyl soybean oleate 1, dibutyl phthalate Ester 3, heavy calcium carbonate 10, quartz powder 5, polydimethylsiloxane 0.5.

[0015] A preparation method of hot-melt butyl sealant for chlorosulfonated polyethylene composite hollow glass, comprising the following steps:

[0016] (1) Weigh raw materials by weight, first mix furfuryl alcohol resin, octyl soyate, polydimethylsiloxane and dibutyl phthalate at 80°C for 0.5h, then add silane coupling agent A Stir at -151 at 100°C for 10 minutes, and obtain modified furfuryl alcohol resin adhesive after cooling;

[0017] (2) First, blend butyl rubber, polyisobutylene, chlorosulfonated polyethylene and binary eth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a chlorosulfonated polyethylene compounded hot-melt butyl sealant for hollow glass. The sealant is prepared from, by weight, 10-20 parts of butyl rubber, 30-40 parts of polyisobutene, 3-5 parts of chlorosulfonated polyethylene, 5-10 parts of ethylene-propylene rubber, 0.5-1 part of a silane coupling agent A-151, 5-10 parts of furfuryl alcohol resin, 1-2 parts of ethyl hexyl ester of epoxidized soybean oil, 3-5 parts of dibutyl phthalate, 10-15 parts of heavy calcium carbonate, 5-10 parts of quartz powder and 0.5-1 part of polydimethylsiloxane. The chlorosulfonated polyethylene compounded hot-melt butyl sealant for the hollow glass has advantages of high deformation resistance, strength, adhesiveness, water resistance, corrosion resistance, impact resistance, usability and durability.

Description

technical field [0001] The invention relates to the technical field of sealants, in particular to a hot-melt butyl sealant for chlorosulfonated polyethylene composite insulating glass and a preparation method thereof. Background technique [0002] Insulating glass integrates excellent properties such as heat insulation, sound insulation, and lighting. It is an efficient energy-saving product and is widely used in glass curtain walls, automobiles, transportation, and aircraft. As insulating glass enters the field of new buildings in large quantities, people's quality requirements for insulating glass are also getting higher and higher. Insulating glass with long sealing life can not only bring good economic benefits, but also have stronger market competitiveness. Butyl sealant has extremely low water vapor transmission rate and good sealing effect. It is used as the first insulating glass sealant and plays a key role in the comprehensive quality performance of insulating gla...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/20C09J123/22C09J123/34C09J123/16C09J171/14C09J11/04C09J11/06C09J11/08
CPCC08L2205/025C08L2205/035C09J11/04C09J11/06C09J11/08C09J123/22C08L23/22C08L23/34C08L23/16C08L71/14C08L83/04C08K13/02C08K5/1515C08K5/12C08K2003/265C08K3/36
Inventor 刘晓朋
Owner 天长市永泰密封材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap