Processing technology of corrosion-resistant hollow glass

A processing technology and corrosion-resistant technology, applied in the processing technology field of insulating glass, can solve the problems of low strength, poor corrosion resistance, easy to break, etc., to achieve improved corrosion resistance and strength, uniform coating adhesion, use long life effect

Inactive Publication Date: 2017-04-26
苏州富艾姆工业设备有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] There are still many problems in the existing insulating glass, such as poor corrosion resistance, low strength, and easy to break, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The processing technology of the corrosion-resistant hollow glass of the present embodiment comprises the following steps:

[0028] (1) Ingredients: the mass percentage of each component in the corrosion-resistant hollow glass is: Al 2 o 3 : 1.12%, CeO 2 : 0.18%, SnO 2 : 0.15%, ZnO: 0.13%, ZrO 2 : 0.02%, TiO 2 : 0.43%, La 2 o 3 : 0.17%, Gd 2 o 3 : 0.02%, Bi 2 o 3 : 0.03%, WO 3 : 0.01%, Nd 2 o 5 : 0.01%, P 2 o 5, : 0.05%, Fe 2 o 3 : 0.01%, CaO: 1.25%, MgO: 2.35%, R 2 O: 0.35%, the balance is SiO 2 ;

[0029] (2) Load the glass to be processed through a fully automatic glass loading device;

[0030] (3) Scribing by glass automatic scribing device;

[0031] (iv) Make the frame and upper frame, calculate the length of the aluminum frame according to the size of the glass and the depth of the glue, and then bend the frame on the automatic frame bending machine;

[0032](5) Perform ion treatment on the bent aluminum frame, as follows:

[0033] A. Polyan...

Embodiment 2

[0040] The mass percent of each composition in the corrosion-resistant insulating glass of the present embodiment is: Al 2 o 3 : 1.19%, CeO 2 : 0.21%, SnO 2 : 0.19%, ZnO: 0.19%, ZrO 2 : 0.04%, TiO 2 : 0.56%, La 2 o 3 : 0.26%, Gd 2 o 3 : 0.05%, Bi 2 o 3 : 0.07%, WO 3 : 0.06%, Nd 2 o 5 : 0.08%, P 2 o 5, : 0.11%, Fe 2 o 3 : 0.14%, CaO: 1.58%, MgO: 3.42%, R 2 O: 0.56%, the balance is SiO 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing technology of corrosion-resistant hollow glass. The processing technology includes the following steps: 1), preparing materials; 2), loading to-be-processed glass; 3), cutting the glass into sheets; 4) preparing frames, framing, and bending the fames with an automatic frame-bending machine; 5) conducting ion treatment on the bent aluminum frames; 6) conducting electroplating; 7) filling a drying agent in the electroplated aluminum frames, connecting the filled aluminum frames with pins for forming, aligning the prepared aluminum frames, coating butyl rubber, and conducting framing: 8) bonding the glass sheets; 9) sealing the bonded glass sheets with glue, and conducting overturn packaging on the glass with an overturn packaging device. The processing technology is simple, the waste of raw materials is little, the production efficiency is improved, at the same time, the product has a good anti-condensation property, reduces cold emission and has a certain degree of security, the excellent sealing property of the hollow glass is ensured, sealing hidden danger which may occurs at four corners in an existing processing technology is eliminated, and the overall stability of the hollow glass is greatly increased.

Description

technical field [0001] The invention relates to a processing technology of corrosion-resistant insulating glass, which belongs to the technical field of glass processing. Background technique [0002] Glass is formed by melting together sand and other chemicals (mainly produced from: soda ash, limestone, quartz). A silicate-based non-metallic material that forms a continuous network structure during melting, and gradually increases in viscosity and hardens during cooling to cause it to crystallize. The chemical composition of ordinary glass is Na 2 O CaO 6SiO 2 , the main component is silicon dioxide, which is an amorphous solid with irregular structure. Widely used in buildings, used for wind and light transmission, belongs to the mixture. There are also colored glass that is mixed with certain metal oxides or salts to show color, and tempered glass made by a special method. [0003] At present, in order to meet various needs in production and life, people carry out de...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C3/06C03C27/10C25D5/44C25D3/56
CPCC03C3/06C03C27/10C25D3/565C25D5/44
Inventor 翁华明
Owner 苏州富艾姆工业设备有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com