Fullerol containing organic type engine liquid coolant and preparation method thereof

A technology of engine coolant and fullererol, which is applied in the field of engine coolant, can solve the problems of solder and aluminum alloy anti-corrosion effect, not dense, etc., and achieve the effect of long service life, slow consumption and good compatibility

Active Publication Date: 2017-05-10
QINGDAO COPTON TECH +2
View PDF9 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the adsorption film formed by the organic acid corrosion inhibitor is thin (only a few nanometers) and not dense, which leads to its unsatisfactory anti-corrosion effect on solder and aluminum alloys, especially heat transfer corrosion of cast aluminum and aluminum pump cavitation corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fullerol containing organic type engine liquid coolant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Mix and stir 30kg of ethylene glycol and 70kg of distilled water evenly to obtain a cooling liquid base liquid; add 0.25kg of n-heptanoic acid, 0.25kg of adipic acid, and 0.01kg of benzotriazole to the above base liquid, and stir until completely dissolved to obtain The first mixed solution; add 0.01 kg of fullererol containing 18 to 24 hydroxyl groups to the first mixed solution, and stir until it is completely dissolved to obtain the second mixed solution; add 0.001 kg of silicone defoaming solution to the second mixed solution Add 0.01kg of acid lake blue dye to the above clear and transparent mixed solution, stir until it is completely dissolved, and finally obtain the cooling liquid product 1.

[0046]The composition of coolant product 1 is: 30kg of ethylene glycol, 70kg of distilled water, 0.01kg of fullerenol containing 18-24 hydroxyl groups, 0.25kg of n-heptanoic acid, 0.25kg of adipic acid, 0.01kg of benzotriazole, organic Silicon defoamer 0.001kg, acid lake bl...

Embodiment 2

[0048] Mix and stir 45kg ethylene glycol, 50kg propylene glycol and 5kg distilled water evenly to obtain the cooling liquid base liquid; add 2.0 kg adipic acid, 3 kg n-hexanoic acid, 0.5 kg methyl benzotriazole to the above base liquid, and stir fully until Completely dissolve to obtain the first mixed solution; add 2 kg of fullererol containing 32 to 40 hydroxyl groups to the first mixed solution, stir well until completely dissolved to obtain the second mixed solution; add 0.01 kg of organic silicon to the second mixed solution Defoamer, fully stirred, completely dissolved until a clear and transparent solution was obtained; 0.05kg of light yellow dye was added to the above clear and transparent solution, fully stirred until completely dissolved, and finally the cooling liquid product 2 was obtained.

[0049] The composition of coolant product 2 is: 45kg of ethylene glycol, 50kg of propylene glycol, 5kg of distilled water, 2kg of fullererol containing 32 to 40 hydroxyl groups...

Embodiment 3

[0051] Mix and stir 60kg of ethylene glycol and 40kg of distilled water evenly to obtain a cooling liquid base liquid; add 2kg of adipic acid, 1kg of n-octanoic acid, and 0.3kg of methyl benzotriazole to the above base liquid, and stir until completely dissolved to obtain the second A mixed solution; add 0.1kg of fullererol containing 24 to 30 hydroxyl groups to the first mixed solution, stir well until completely dissolved to obtain the second mixed solution; add 0.005kg of organic ether defoamer to the second mixed solution , fully stirred to completely dissolve until a clear and transparent solution is obtained; add 0.03kg of rose bengal dye to the above-mentioned clear and transparent solution, fully stir until completely dissolved, and finally obtain the cooling liquid product 3.

[0052] The composition of coolant product 3 is: 60kg of ethylene glycol, 40kg of distilled water, 0.1kg of fullerenol containing 24 to 30 hydroxyl groups, 1kg of n-octanoic acid, 2kg of adipic a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fullerol containing organic type engine liquid coolant and a preparation method thereof. The liquid coolant comprises the following components in parts by weight: 30 to 95 parts of dihydric alcohol, 5 to 70 parts of deionized water, 0.01 to 2 parts of fullerol, 0.5 to 5.0 parts of organic acid corrosion inhibitor, 0.01 to 0.5 part of azoles corrosion inhibitor, 0.001 to 0.01 part of antifoaming agent, and 0.01 to 0.05 part of dye. Fullerol and organic acid corrosion inhibitor in the liquid coolant can generate a synergistic effect, are adsorbed on the surface of metals, and form a compact fullerol / organic acid protective film, so the liquid coolant has a comprehensive anticorrosion effect on purple copper, yellow copper, carbon steel, cast iron, soldering tin, and cast aluminum and especially has an excellent performance on resisting heat transfer corrosion of cast aluminum and cavitation corrosion of aluminum pump.

Description

technical field [0001] The invention relates to the field of engine coolant, in particular to an organic engine coolant containing fullerenol and a preparation method thereof. Background technique [0002] Engine coolant is an indispensable part to maintain the normal work and operation of the engine. Coolant is the heat transfer medium of the engine cooling system, which plays the role of cooling, anti-corrosion, anti-scaling, anti-freezing and so on. Coolant is usually composed of water, antifreeze, corrosion inhibitor, scale inhibitor, colorant, defoamer, etc. According to the composition of corrosion inhibitors, engine coolants can be divided into inorganic type coolants based on inorganic salt corrosion inhibitors and organic type coolants based on organic acid corrosion inhibitors. [0003] At present, inorganic type coolants are mostly used in China, and the main inorganic salt corrosion inhibitors used are silicates, borates, molybdates, phosphates, etc. Inorganic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/20
CPCC09K5/20
Inventor 朱海涛韩军英吴大雄孙俊淼梁焕喜
Owner QINGDAO COPTON TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap