Bonding agent for starch-based corrugated paper and preparation method thereof

A technology based on corrugated paper and adhesives, applied in the direction of starch adhesives, adhesive types, polysaccharide adhesives, etc., can solve the problems of low viscosity, poor water resistance, etc., and achieve the effect of high bond strength

Inactive Publication Date: 2017-05-31
苏州纳贝通环境科技有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And starch adhesive itself also has some deficiencies, such as poor water resistance, low viscosity, etc., which brings certain problems to the preparation and use of starch adhesive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An adhesive for starch-based corrugated paper, prepared from the following ingredients in parts by weight: 30 parts of starch, 180 parts of water, 1 part of borax, 3 parts of sodium hydroxide, 12 parts of hydrogen peroxide, 0.8 parts of sodium sulfite, and tributyl phosphate 0.2 parts, 5.5 parts of modified urea-formaldehyde resin, 1.2 parts of ethyl oleate, 0.05 parts of ammonium oxide, 1.5 parts of modified konjac gum, 3.8 parts of modified carrageenan, and 0.01 part of preservative.

[0019] The preparation method of the above-mentioned adhesive for starch-based corrugated paper is as follows: (1) configure sodium hydroxide with a concentration of 8% and a hydrogen peroxide solution with a concentration of 30%, and oscillate evenly with ultrasonic waves; (2) put potato starch into a clean and dry reaction In the container, add water and stir for 10 minutes, the stirring speed is 160 rpm until the mixture is uniform; (3) Add ferrous sulfate and hydrogen peroxide soluti...

Embodiment 2

[0021] An adhesive for starch-based corrugated paper, prepared from the following ingredients in parts by weight: 40 parts of starch, 220 parts of water, 0.4 parts of borax, 7 parts of sodium hydroxide, 8 parts of hydrogen peroxide, 1.6 parts of sodium sulfite, tributyl phosphate 0.5 parts, 2.5 parts of modified urea-formaldehyde resin, 3.6 parts of ethyl oleate, 0.12 parts of ammonium oxide, 4.5 parts of modified konjac gum, 1.5 parts of modified carrageenan, and 0.12 parts of preservative.

[0022] The preparation method of the above starch-based corrugated paper adhesive is as follows: (1) configure sodium hydroxide with a concentration of 12% and hydrogen peroxide solution with a concentration of 20%, and oscillate evenly with ultrasonic waves; (2) put potato starch into a clean and dry reaction In the container, add water and stir for 15 minutes, the stirring speed is 80 rpm until the mixture is uniform; (3) Add ferrous sulfate and hydrogen peroxide solution, stir and reac...

Embodiment 3

[0024] An adhesive for starch-based corrugated paper, prepared from the following ingredients in parts by weight: 38 parts of starch, 210 parts of water, 0.8 parts of borax, 6 parts of sodium hydroxide, 11 parts of hydrogen peroxide, 1 part of sodium sulfite, and tributyl phosphate 0.3 parts, 3.5 parts of modified urea-formaldehyde resin, 1.8 parts of ethyl oleate, 0.08 parts of ammonium oxide, 2.5 parts of modified konjac gum, 3 parts of modified carrageenan, and 0.08 parts of preservative.

[0025] The preparation method of the above-mentioned adhesive for starch-based corrugated paper is as follows: (1) configure sodium hydroxide with a concentration of 10% and hydrogen peroxide solution with a concentration of 25%, and oscillate evenly with ultrasonic waves; (2) put potato starch into a clean and dry reaction In the container, add water and stir for 12 minutes, the stirring speed is 140 rpm until the mixture is uniform; (3) Add ferrous sulfate and hydrogen peroxide solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a bonding agent for starch-based corrugated paper and a preparation method thereof. The preparation method comprises the following steps: (1) preparing 8 to 12 percent sodium hydroxide and a 20 to 30 percent hydrogen peroxide solution, and performing ultrasonic oscillation to mix uniformly; (2) placing potato starch into a clean and dry reaction vessel, adding water, and stirring for 10 to 15 minutes at a speed of 80 to 160 revolution / minute until uniform mixing; (3) adding ferrous sulfate and the hydrogen peroxide solution, stirring for reacting for 10 to 20 minutes, adding the sodium hydroxide solution while stirring, and stirring and pasting until the shape of the solution does not change any more; (4) adding sodium borate and tributyl phosphate, and stirring continually for 20 to 30 minutes; (5) adding modified urea resin, ethylis oleas, ammonium oxide, modified konjac glucomannan, modified carrageenan and a preservative, and uniformly mixing to obtain the bonding agent. The bonding agent for the starch-based corrugated paper has very high viscosity and water resistance.

Description

technical field [0001] The invention relates to the field of adhesive manufacturing for packaging, in particular to an adhesive for starch-based corrugated paper and a preparation method thereof. Background technique [0002] Corrugated cartons are the most widely used packing boxes. In addition to the cardboard itself, the adhesive used is also an important factor affecting the quality of corrugated cartons. Although the sodium silicate aqueous solution adhesive used for many years has a simple operation process, it has disadvantages such as poor moisture resistance, slow bonding speed, and heavy carton. With the in-depth development of science and technology, the adhesive materials of corrugated cardboard and corrugated boxes are constantly updated and improved, and the sodium silicate solution that has been continuously used is no longer suitable for the needs of rapid packaging. After 1984, starch adhesives were widely used in my country, and such starch adhesives were ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J103/02C09J161/32C09J105/02C09J105/00C09J11/04C09J11/06
CPCC09J103/02C08L2205/02C08L2205/035
Inventor 潘明华
Owner 苏州纳贝通环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com