Preparation method of mud pottery sand inorganic thermal insulation mortar
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of inorganic thermal insulation mortar and ceramic sand, which is applied in the production and application of clay products and ceramic materials, and can solve the problems of polluting the marine environment, occupying farmland, and easily polluting the surrounding environment, so as to avoid secondary pollution and make good use of it. Effect
Inactive Publication Date: 2017-06-13
SHANGHAI ERSHIYE CONSTR CO LTD
View PDF2 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The ocean dumping method will pollute the marine environment and is increasingly restricted by various aspects; landfilling sludge will occupy farmland and easily pollute the surrounding environment, resulting in deterioration of the ecological environment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] A preparation method of silt pottery sand inorganic thermal insulation mortar, which comprises the following steps:
[0027] (a) Dry the sludge: the drying method is to place the sludge in a dry place, dry it in the sun or dry it in a dry, cool and ventilated place
[0028] (b) Sludge roasting: roasting the sludge at high temperature, the roasting time is not less than 30min, and the roasting temperature is not lower than 1000°C;
[0029] (c) After roasting, crush and sieve the residue to obtain pottery sand with a particle size below 2mm;
[0030] (d) Preparation of cement slurry: mix cement slurry according to a certain water-cement ratio;
[0031] (e) Mortar preparation: the pottery sand obtained in step (c) is used instead of fine sand to be mixed into cement slurry, and the pottery sand inorganic thermal insulation mortar is prepared after stirring evenly.
[0032] In the step (b), the calcination time is 30 minutes to 60 minutes, and the calcination temperature ...
Embodiment 2
[0036] Take pond silt and dredging silt to prepare silt ceramic sand inorganic thermal insulation mortar as an example:
[0037] 1. Expose pond silt, dredging silt, etc. in the sun;
[0038] 2. Transport the sun-dried sludge to the rotary kiln, and roast in the rotary kiln at 1100°C for 60 minutes;
[0039] 3. After roasting, crush and sieve the residue, and take pottery sand with a particle size below 2mm;
[0040] 4. According to the construction conditions and design requirements, mix cement slurry and add water reducing agent;
[0041] 5. Mix the clay sand into the cement slurry and stir evenly;
[0042] 6. Add polypropylene thermal insulation fiber to ceramic sand thermal insulation mortar and stir evenly.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a preparation method of mud pottery sand inorganic thermal insulation mortar. The method comprises the steps of (a) carrying out drying treatment on mud; (b) carrying out mud sintering, and roasting the mud at high temperature, wherein the roasting time is not less than 30min and the roasting temperature is not lower than 1,000 DEG C; (c) after roasting, crushing and sieving residues and taking pottery sand of which the particle sizes are smaller than 2mm; (d) preparing cement paste, stirring the cement paste at a certain water cement ratio; and (e) preparing the mortar, doping the pottery sand obtained in the step (c) into the cement paste instead of fine sand, stirring evenly and then preparing the mud pottery sand inorganic thermal insulation mortar. The mortar is mixed by using proper pottery sand instead of the fine sand according to the actual requirements of thermal insulation mortar preparation and the method provided by the invention; and the pottery sand inorganic thermal insulation mortar is nontoxic, tasteless, free of radioactive contamination and free of harm to a human body, and no harmful gas is discharged even if in a high-temperature environment generated by long-term direct irradiation of the sunlight.
Description
technical field [0001] The invention belongs to the technical field of mortar preparation, in particular to a preparation method of silt pottery sand inorganic thermal insulation mortar. Background technique [0002] A large amount of silt will be produced in port projects, reclamation projects, and river and lake dredging projects. In addition, in vast rural areas, a large amount of silt is also produced in old wells, ponds, and river courses. How to deal with these sludges is an urgent problem to be solved. The current disposal methods for these silts are mainly ocean dumping (coastal areas) and landfilling (inland areas). The ocean dumping method will pollute the marine environment and is increasingly restricted by various aspects; landfilling sludge will occupy farmland and easily pollute the surrounding environment, resulting in deterioration of the ecological environment. [0003] Compared with traditional cement mortar, ceramic sand insulation mortar only needs to ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more