Graphene-compounded PVA (polyvinyl alcohol) master batch with high performance, application and fiber material

A graphene composite, polyvinyl alcohol mother technology, applied in the direction of fiber chemical characteristics, single-component synthetic polymer rayon, rayon manufacturing, etc., can solve the problem of uneven dispersion of graphene particles, uneven particle size, graphene Low content, etc.

Active Publication Date: 2017-06-13
JINAN SHENGQUAN GROUP SHARE HLDG
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, there are many related products related to polyvinyl alcohol-graphene composites. In view of its wide application, polyvinyl alcohol-graphene is generally made into functional masterbatches, which is convenient for transportation, storage, and It is convenient for subsequent applications, and then according to actual needs, functional masterbatches are used as raw materials to make related products. From this, it is found that the performance of the functional masterbatch itself will directly affect the related performance of subsequent products, but generally produced The graphene content in the functional masterbatch will be relatively low, and the graphene particles will be unevenly dispersed, the particle size will be uneven, and interlayer agglomeration will easily occur. In this way, the stress concentration points caused by graphene materials with different sheet diameters will easily occur. The problem of fracture affects the performance of subsequent products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene-compounded PVA (polyvinyl alcohol) master batch with high performance, application and fiber material
  • Graphene-compounded PVA (polyvinyl alcohol) master batch with high performance, application and fiber material
  • Graphene-compounded PVA (polyvinyl alcohol) master batch with high performance, application and fiber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The preparation method of the high-performance graphene composite polyvinyl alcohol masterbatch is as follows:

[0053] 1) Add graphene oxide in water, and ultrasonically disperse to obtain a stable dispersion. The suspension is centrifuged for the first time at 2000rpm, and the centrifugation time is 20min to remove the bottom sediment. The supernatant is centrifuged for the second time at 5000rpm. , the centrifugation time is 10min to obtain the secondary bottom precipitation, and the secondary bottom precipitation is added with water and ultrasonically obtained 1.5wt% graded graphene oxide sol solution;

[0054] 2) The graphene oxide sol solution with a concentration of 1.5wt% and the PVA aqueous solution with a concentration of 5wt% are premixed (the degree of polymerization is 1700, and the degree of alcoholysis is 99%) to obtain a premix, and the premix is ​​mixed with 10wt% % PVA aqueous solution is mixed again (polymerization degree is 2500, alcoholysis degree i...

Embodiment 2

[0057] The difference from Example 1 is that in step 1), the bottom sediment obtained by first centrifugation at 3000rpm is selected, and water is added to ultrasonic to obtain a 2wt% graded graphene oxide sol solution. In the obtained mixed solution, the concentration of PVA is 16wt%. , solvent evaporation and drying to obtain a functional masterbatch with a graphene oxide content of 1.5 wt%, and the D90 of the graphene-like substance is 70 μm, and the D10 is 3.5 μm.

Embodiment 3

[0059] The difference from Example 1 is that in step 1), the secondary supernatant after centrifuging the supernatant again at a speed of 7000 rpm is selected to prepare a 3wt% graded graphene oxide sol solution, and in the obtained mixed solution , the concentration of PVA is 15wt%, and the solvent is evaporated and dried to obtain a functional masterbatch with a graphene oxide content of 1.5wt%, and the D90 of the graphene-like substance is 30 μm, and the D10 is 5 μm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a graphene-compounded PVA (polyvinyl alcohol) master batch with high performance. The graphene-compounded PVA master batch mainly consists of a graphene matter and PVA, wherein the content of graphene matter is less than 6wt% in the graphene-compounded PVA master batch; the D90 index of the graphene matter is controlled to be less than 100mu m, the D10 index is controlled to be less than 20mu m, and the D90 index is controlled to be less than 20 times of D10 index. A preparation method of the graphene-compounded PVA master batch comprises the following steps of (A) pretreating a graphene matter water solution, so as to obtain a graphene matter particle size graded water solution; (B) mixing and stirring the PVA water solution and the graphene matter particle size graded water solution, so as to obtain a mixing solution; drying, so as to obtain the graphene-compounded PVA master batch. The graphene-compounded PVA master batch has the advantage that although the content is higher, the graphene particles are uniformly dispersed, the particle size is also uniform, and production of any agglomerated particle is avoided.

Description

technical field [0001] The invention relates to the field of processing and preparation of polyvinyl alcohol masterbatches, in particular to a high-performance graphene composite polyvinyl alcohol masterbatch, its preparation method and application, and a fiber material. Background technique [0002] Polyvinyl alcohol (PVA) is a water-soluble polymer with the molecular formula [C 2 h 4 O]n. Due to its good hydrophilicity, impact resistance and good dispersibility in molding processing, polyvinyl alcohol fiber can be used as a reinforcing material for plastics, cement and ceramics, and can also replace carcinogenic asbestos. [0003] Graphene is a two-dimensional material with a honeycomb structure composed of a single layer of sp2 hybridized carbon atoms, which has many excellent properties. Since its discovery in 2004, graphene has become a research hotspot in the scientific community. While studying the physical and chemical properties of graphene, composite materials ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K3/04C08L29/04D01F6/50D01F1/10
CPCC08K3/04C08L2203/12D01F1/10D01F6/50C08L29/04
Inventor 唐一林张金柱张安王文平刘顶
Owner JINAN SHENGQUAN GROUP SHARE HLDG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com