A kind of preparation method of plant polyene bisphenol friction powder

A technology of polyene bisphenol and friction powder, which is applied in the field of plant polyene bisphenol friction powder and its preparation, and can solve problems such as insufficient heat resistance

Active Publication Date: 2019-04-12
常熟耐素生物材料科技有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a preparation method of plant polyene bisphenol friction powder aiming at the technical problem of insufficient heat resistance existing in cashew nut shell oil friction powder, the prepared plant polyene bisphenol friction powder Powder has significantly improved resistance to cashew shell oil friction powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of plant polyene bisphenol friction powder
  • A kind of preparation method of plant polyene bisphenol friction powder
  • A kind of preparation method of plant polyene bisphenol friction powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Add plant polyene bisphenol into the reaction kettle, add 3% sulfuric acid and 3% urotropine accounting for plant polyene bisphenol, polymerize at 100 degrees for 4 hours, test the viscosity of the prepolymer after polymerization, add 8% urotropine The product was added to the prepolymer, cured at 135°C for 4 hours, and cured at 175°C for 3 hours. The acetone extraction rate and the index of weight loss at 370°C were tested. The results are shown in Table 1.

[0027] Table 1

[0028]

Embodiment 2

[0030] Add plant polyene bisphenol into the reaction kettle, add 3% sulfuric acid and 3% urotropine accounting for plant polyene bisphenol, polymerize at 100 degrees for 4 hours, test the viscosity of the prepolymer after polymerization, add 10.65% paraformaldehyde Add it to the prepolymer, cure at 135°C for 4 hours, and cure at 175°C for 3 hours. Test the acetone extraction rate and the index of weight loss at 370°C. The results are shown in Table 2.

[0031] Table 2

[0032]

Embodiment 3

[0034] Add plant polyene bisphenol into the reaction kettle, add 3% sulfuric acid and 3% urotropine accounting for plant polyene bisphenol, polymerize at 100 degrees for 4 hours, test the viscosity of the prepolymer after polymerization, add 33% furfural to the prepolymer In the polymer, it was cured at 135°C for 4 hours, and at 175°C for 3 hours. The acetone extraction rate and the index of weight loss at 370°C were tested. The results are shown in Table 3.

[0035] table 3

[0036]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The preparation method of plants polynexolic phenol friction powder in the present invention is characterized by adding acid and one or any mixing of acid and one or arbitrary aldehyde in plant polylamine bisphenols.Perform the polymerization reactions to generate a prefabricated, measure the viscosity of the polymer to a certain value, and then add one or arbitrary one or any of the Ulot products and aldehyde to the prefabricated to the first temperature.The second curing is then obtained at the third temperature.The plants prepared by the present invention are significantly better than the thermal performance of the lumbar shell oil friction powder. Starting from 200 ° C, the heat loss of lumbar shell oil friction is significantly higher than that of plant polylamine bisphenol friction powder.Essence

Description

technical field [0001] The invention relates to the technical field of friction powder and its preparation, in particular to a plant polyene bisphenol friction powder and a preparation method thereof. Background technique [0002] Friction materials are usually made of reinforced fiber asbestos, phenolic resin adhesive, cashew nut shell oil friction powder and inorganic fillers, etc. by mixing and thermoforming. In addition to mechanical strength, the performance required by it must also have the following four characteristics: ①The friction coefficient is stable within a certain range; ②Low wear rate, long service life; ③Do not scratch the counterpart material; ④Low friction noise. An important factor affecting these characteristics is the composition and proportion of the friction material. For example, the friction material produced only with asbestos and phenolic resin is unstable and has no practical value. However, if modifiers such as cashew nut shell oil friction po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G8/20C09K3/14
CPCC08G8/20C09K3/1454
Inventor 戴志成
Owner 常熟耐素生物材料科技有限公司