Safe and environment-friendly type natural stone waterproof alkali-resistant backing adhesive and preparation method thereof

A safe, environmentally friendly and natural technology, applied in the direction of adhesives, adhesive additives, non-polymer adhesive additives, etc., can solve the problems of white flowers, high cost, insufficient bonding strength, etc., and achieve simple preparation methods and mild process conditions , Improve the effect of application value

Inactive Publication Date: 2017-06-30
BNSA NEW MATERIAL SHANGHAI CO LTD
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the dry-hanging method takes up a lot of space and is expensive, and is generally suitable for external walls or office business halls with large spaces; while the wet-pasting method is mainly used for interior decoration of various buildings, and there are two main problems: one is The bonding strength between the back glue used as the adhesive and the natural stone is insufficient, and it is easy to produce hollowing; the second is easy to produce white blooms, causing discoloration of the stone and reducing the aesthetics
But this method has the following problems: 1. Treat the symptoms but not the root cause, and fail to fundamentally avoid the occurrence of the white bloom phenomenon, and it is only suitable for light-colored stone materials, which has poor versatility; 2. The white stone adhesive is based on white cement. Under the same conditions, the strength of white cement is weaker than that of gray cement. In addition, the back of the stone is relatively smooth, and the phenomenon of hollowing will inevitably occur. making it difficult to guarantee the actual effect of the method
[0004] At present, most of the stone adhesives on the market are two-component adhesives compounded by acrylic emulsion and ordinary cement. Because the cement itself is highly alkaline, it is difficult to fundamentally solve the efflorescence of natural stone. problems, reducing the application value of natural stone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Safe and environment-friendly type natural stone waterproof alkali-resistant backing adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A safe and environment-friendly natural stone waterproof and alkali-resistant adhesive, the adhesive includes the following components and contents by weight: 5 parts of liquid mixture, 5 parts of powder mixture, wherein the liquid mixture includes the following components and contents by weight: acrylic acid 400 parts of emulsion, 100 parts of lithium silicate aqueous solution, 2 parts of bactericide, 2 parts of defoamer and 496 parts of water, the powder mixture includes the following components and parts by weight: 450 parts of kaolin, 300 parts of heavy calcium carbonate powder, 250 parts of snow white powder, 2 parts of superplasticizer and 2 parts of cellulose.

[0026] Wherein, the acrylic emulsion is commercially available Bardford RS-2608; in the lithium silicate aqueous solution, the mass percentage of lithium silicate is 35%, and the modulus of lithium silicate is 6; the fungicide is commercially available KATHON LXE; The foaming agent is commercially availab...

Embodiment 2

[0033] A safe and environment-friendly natural stone waterproof and alkali-resistant adhesive, the adhesive includes the following components and contents by weight: 6 parts of liquid mixture, 4 parts of powder mixture, wherein the liquid mixture includes the following components and contents by weight: acrylic acid 420 parts of emulsion, 95 parts of lithium silicate aqueous solution, 3 parts of bactericide, 1 part of defoamer and 550 parts of water, the powder mixture includes the following components and content by weight: 430 parts of kaolin, 320 parts of heavy calcium carbonate powder, 230 parts of snow white powder, 3 parts of superplasticizer and 1 part of cellulose.

[0034] Among them, the acrylic acid emulsion is commercially available Bardford RS-2608; in the lithium silicate aqueous solution, the mass percentage of lithium silicate is 45%, and the modulus of lithium silicate is 8; the bactericide is commercially available KATHON LXE; The foaming agent is commerciall...

Embodiment 3

[0039] A safe and environment-friendly natural stone waterproof and alkali-resistant adhesive, the adhesive includes the following components and parts by weight: 4 parts of liquid mixture, 6 parts of powder mixture, wherein the liquid mixture includes the following components and content by weight: acrylic acid 380 parts of emulsion, 105 parts of lithium silicate aqueous solution, 1 part of bactericide, 3 parts of defoamer and 450 parts of water, the powder mixture includes the following components and parts by weight: 480 parts of kaolin, 280 parts of heavy calcium carbonate powder, 270 parts of snow white powder, 1 part of superplasticizer and 3 parts of cellulose.

[0040]Among them, the acrylic acid emulsion is commercially available Bardford RS-2608; in the lithium silicate aqueous solution, the mass percentage of lithium silicate is 40%, and the modulus of lithium silicate is 4; the bactericide is commercially available KATHON LXE; The foaming agent is commercially avai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a safe and environment-friendly type natural stone waterproof alkali-resistant backing adhesive and a preparation method of the safe and environment-friendly type natural stone waterproof alkali-resistant backing adhesive. The backing adhesive comprises the following components by weight: 4-6 parts of liquid mixture and 4-6 parts of powder mixture, the liquid mixture comprises the following components by weight: 380-420 parts of acrylic emulsion, 95-105 parts of lithium silicate aqueous solution, 1-3 parts of sterilizing agent, 1-3 parts of defoaming agent, and 450-550 parts of water, the powder mixture comprises the following components by weight: 430-480 parts of kaolin, 280-320 parts of heavy calcium carbonate powder, 230-270 parts of snowflake white powder, 1-3 parts of water reducing agent, and 1-3 parts of cellulose; and the various components in the powder mixture are respectively added into the liquid mixture in the preparation process. Compared with the prior art, the lithium silicate aqueous solution and the acrylic emulsion are compounded, the kaolin, the heavy calcium carbonate powder and the snowflake white powder are used as powder materials, the prepared backing adhesive is high in bonding strength, water resistance and alkali resistance, the phenomena of efflorescence, saltpetering and water spotting of the natural stone are solved fundamentally, and the backing adhesive is safe and environment-friendly.

Description

technical field [0001] The invention belongs to the technical field of safe and environmentally friendly pigments and dyes, and relates to a safe and environmentally friendly natural stone waterproof and alkali-resistant back glue and a preparation method thereof. Background technique [0002] Natural stone refers to materials that are mined from natural rock mass and processed into blocks or plates. Natural stones commonly used in architectural decoration mainly include granite and marble. The decoration methods of natural stone are mainly dry hanging method and wet paste method. Among them, the dry-hanging method takes up a lot of space and is expensive, and is generally suitable for external walls or office business halls with large spaces; while the wet-pasting method is mainly used for interior decoration of various buildings, and there are two main problems: one is The bonding strength between the back glue used as the binder and the natural stone is insufficient, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J133/00C09J11/04C09J11/08
CPCC09J11/04C09J11/08C09J133/00C08L1/284C08K13/02C08K3/34C08K3/346C08K2003/265
Inventor 侯进全
Owner BNSA NEW MATERIAL SHANGHAI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap