Aqueous polyester resin paint and preparation method thereof

A technology of water-based polyester resin and deionized water, which is applied in the field of synthetic paint to achieve the effects of improved stability, high fullness, and high environmental protection

Inactive Publication Date: 2017-07-04
滁州市全丰物资有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with the variability of the atmospheric environment and the increase of pollutants, more stringent requirements are put forward for metal antirust coatings. How to...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous polyester resin paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0023] Such as figure 1 Shown, be a kind of waterborne polyester resin paint described in the present embodiment, comprise polyhydric alcohol, polybasic acid, catalyst 8%, curing agent 6%, filler 6% and water 60%;

[0024] Described polyhydric alcohol comprises trimethylolpropane 8%, neopentyl glycol 12%, ethylene glycol 6%, propylene glycol 8%, and described polybasic acid comprises purified terephthalic acid 5%, isophthalic acid 12%, 6% phthalic acid, 10% trimellitic anhydride, 6% hexahydrophthalic acid, 10% maleic anhydride, 5% adipic acid;

[0025] The water-based polyester resin paint also includes 0.1% p-methoxyphenol, 6% ethylene glycol monobutyl ether, 8% dimethylethanolamine, and 60% deionized water.

[0026] More specifically, the preparation method of described waterborne polyester resin paint is as follows:

[0027] (1) Heating reaction: take the first reactor, and add polyhydric alcohol, polybasic acid, p-methoxyphenol, ethylene glycol monobutyl ether, dimethyle...

specific Embodiment 2

[0034] The water-based polyester resin paint of the present invention comprises polyol, polybasic acid, catalyzer 12%, curing agent 9%, filler 8% and water 70%;

[0035] Described polyhydric alcohol comprises trimethylolpropane 10%, neopentyl glycol 18%, ethylene glycol 9%, propylene glycol 10%, and described polybasic acid comprises purified terephthalic acid 10%, isophthalic acid 18%, 9% phthalic acid, 14% trimellitic anhydride, 9% hexahydrophthalic acid, 15% maleic anhydride, 8% adipic acid;

[0036] The water-based polyester resin paint also includes 0.2% p-methoxyphenol, 15% ethylene glycol monobutyl ether, 12% dimethylethanolamine, and 80% deionized water.

[0037] More specifically, the preparation method of described waterborne polyester resin paint is as follows:

[0038] (1) Heating reaction: take the first reactor, and add polyhydric alcohol, polybasic acid, p-methoxyphenol, ethylene glycol monobutyl ether, dimethylethanolamine, and deionized water into the first r...

specific Embodiment 3

[0045] The water-based polyester resin paint of the present invention comprises polyhydric alcohol, polybasic acid, catalyzer 16%, curing agent 12%, filler 10% and water 80%;

[0046] Described polyhydric alcohol comprises trimethylolpropane 12%, neopentyl glycol 24%, ethylene glycol 12%, propylene glycol 12%, and described polybasic acid comprises purified terephthalic acid 15%, isophthalic acid 24%, 12% phthalic acid, 18% trimellitic anhydride, 12% hexahydrophthalic acid, 20% maleic anhydride, 10% adipic acid;

[0047] The water-based polyester resin paint also includes 0.3% p-methoxyphenol, 24% ethylene glycol monobutyl ether, 16% dimethylethanolamine, and 100% deionized water.

[0048] Specifically, the water-based polyester resin paint includes polyol, polybasic acid, catalyst 16%, curing agent 12%, filler 10% and water 80%; the polyol includes trimethylolpropane 12%, neopentyl diethylene glycol Alcohol 24%, ethylene glycol 12%, propylene glycol 12%, said polyacids inclu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aqueous polyester resin paint. The aqueous polyester resin paint comprises polyol, polybasic acid, 8-16% of catalyst, 6-12% of a curing agent, 6-10% of a filler and 60-80% of water; the polyol comprises 8-12% of trimethylolpropane, 12-24% of neopentyl glycol, 6-12% of ethylene glycol and 8-12% of propylene glycol, and the polybasic acid comprises 5-15% of purified terephthalic acid, 12-24% of m-phthalic acid, 6-12% of phthalic acid, 10-18% of trimellitic anhydride, 6-12% of hexahydrophthalic acid, 10-20% of maleic anhydride and 5-10% of adipic acid; and the aqueous polyester resin paint also includes 0.1-0.3% of p-methoxyphenol, 6-24% of ethylene glycol monobutyl ether, 8-16% of dimethylethanolamine and 60-100% of deionized water. The aqueous polyester resin paint improves the stability of the hydrolysis of a polyester main chain in order to improve the aqueous insulation property of the polyester resin paint, can be widely used in aqueous insulation devices, and meets practical use requirements.

Description

technical field [0001] The invention relates to a water-based polyester resin paint and a preparation method thereof, belonging to the technical field of synthetic paints. Background technique [0002] In recent years, water-based environmentally friendly coatings, including high-solid and solvent-free coatings, water-based coatings, powder coatings and radiation-cured coatings, have achieved rapid development. Water-based polyester coating, one of the representative water-based coatings, has the characteristics of high gloss, strong adhesion, high fullness, and excellent impact resistance. It can be formulated with water-soluble amino resin to make water-based baking paint, and can also be used Hydrophilic polyisocyanate is formulated into water-based wood coatings cured at room temperature, so it is widely used in the protection and decoration of metal and wood surfaces; because polyester is easy to hydrolyze, the application of water-based polyester is limited to a certai...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D167/02C09D5/25C08G63/685C08G63/78
CPCC08G63/6858C08G63/78C09D167/02
Inventor 戈建伦
Owner 滁州市全丰物资有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap