Cu2+1O/Cu2Cl(OH)3/TiO2 ternary complex and preparation method thereof
A ternary compound and drying technology, applied in the field of biochemistry, can solve the problems of poor photocatalytic antibacterial effect and narrow photocatalyst spectral response range, and achieve the effects of improved catalytic effect, low cost and large inhibition zone.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0050] Add an appropriate amount of liquid nitrogen to a 100mL beaker, then add 10mL of titanium tetrachloride drop by drop, then add 10mL of deionized water dropwise, shake the beaker constantly to get a yellow colloid, let the colloid stand, and when the temperature rises to room temperature, the colloid Transfer to a 100mL reaction kettle equipped with 0.09g copper sheet, heat to 160°C, and keep it for 24h, take it out, filter under reduced pressure, wash with deionized water and absolute ethanol alternately, dry in an oven at 60°C for 12h, and the target is obtained things.
[0051] Characterize the target and test its antibacterial effect.
Embodiment 2 to 7
[0053] The difference from Example 1 is only the amount of copper added, which are 1.19g, 2.38g, 2.59g, 3g, 4g, 6g respectively, and the rest of the steps are the same.
Embodiment 8
[0055] Add an appropriate amount of liquid nitrogen to a 100mL beaker, then add 10mL of titanium tetrachloride drop by drop, then add 10mL of deionized water dropwise, shake the beaker constantly to get a yellow colloid, let the colloid stand, and when the temperature rises to room temperature, the colloid Transfer to a 100mL reaction kettle with 3g of copper sheet, heat to 100°C, and keep it for 36h, take it out, filter under reduced pressure, wash with deionized water and absolute ethanol alternately, and dry in an oven at 60°C for 12h to obtain the target product .
[0056] Characterize the target and test its antibacterial effect.
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information

- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com