Environment-friendly PVC film and preparation method thereof

An environmentally friendly, high-quality technology, applied in the field of PVC film, can solve the problems of limited service life of PVC film, and achieve the effect of long service life, good stability and long life

Inactive Publication Date: 2017-07-21
佛山市宏尔塑胶制品有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the existing PVC film has a limited service life, especially in low temperature and high temperature environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly PVC film and preparation method thereof
  • Environment-friendly PVC film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] Preferred embodiments of the present invention are described below, and it should be understood that the preferred embodiments described here are only used to illustrate and explain the present invention, and are not intended to limit the present invention.

[0021] A kind of environment-friendly PVC film of the present invention, according to mass ratio, comprises: PVC 85 parts, DOP 42 parts, calcium carbonate 3 parts, stabilizer 2.5 parts, soybean oil 6 parts, TiO 2 1 part and 0.3 parts of pigments, also including PVC mass fraction 0.6% graphene, 0.7% protein powder, 2.5% urea, 0.3% hydroxypropyl methylcellulose, 1.5% low-second nitrocellulose, 3.5% of catechins.

[0022] Graphene has super high surface hardness, when evenly distributed in PVC film, it can provide super high wear resistance on product surface.

[0023] Protein powder has air-moisture conductivity, which can give it the function of breathability and moisture absorption.

[0024] Urea has the functio...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides an environment-friendly PVC film and a preparation method thereof. The environment-friendly PVC film comprises, by mass, 80 to 90 of PVC, 40 to 45 of DOP, 2 to 5 of calcium carbonate, 2 to 3 of a stabilizing agent, 5 to 10 of soybean oil, 0.5 to 2 of TiO2 and 0.2 to 0.4 of pigment. The preparation method comprises the following steps: preparing the above substances according to the above ratio and then carrying out uniform mixing under stirring at a rotating speed of 1300 to 1400 rpm; carrying out internal mixing at 140 to 150 DEG C for 4 to 5 min and refining at 160 to 170 DEG C for 6 to 7 min; and then carrying out cooling to 150 to 160 DEG C and successively carrying out extrusion, filtering, calendaring, warm processing, cooling and setting, and trimming. The preparation method is environment friendly and free of pollution; and the PVC film prepared in the invention is durable and has long service life.

Description

technical field [0001] The invention belongs to the technical field of PVC films, and in particular relates to an environment-friendly PVC film and a preparation method thereof. Background technique [0002] Polyvinyl chloride, referred to as PVC in English (Polyvinyl chloride polymer = PVC molecular structure), is a thermoplastic resin polymerized by vinyl chloride under the action of an initiator, and is a homopolymer of vinyl chloride. Vinyl chloride homopolymers and vinyl chloride copolymers are collectively referred to as vinyl chloride resins. PVC is a white powder with an amorphous structure and a small degree of branching. The molecular weight of industrially produced PVC is generally in the range of 50,000 to 120,000, with a large polydispersity, and the molecular weight increases with the decrease of the polymerization temperature; there is no fixed melting point, it starts to soften at 80-85°C, and becomes viscoelastic at 130°C , 160 ~ 180 ℃ began to change into...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08K13/02C08K3/26C08K3/22C08K3/04C08K5/21
CPCC08L27/06C08J5/18C08J2327/06C08J2491/00C08K2003/2241C08K2003/265C08L2201/08C08L2203/16C08L2205/035C08L91/00C08K13/02C08K3/26C08K3/22C08K3/04C08K5/21
Inventor 朱卫忠
Owner 佛山市宏尔塑胶制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap