Novel preform body for bone porcelain and preparation process of preform body

A bone china and blank technology, applied in the field of ceramics, can solve the problems affecting the popularization and use of bone china, poor thermal shock resistance, etc., and achieve the effects of reducing the expansion coefficient, improving thermal shock resistance, and increasing bulk density

Inactive Publication Date: 2017-08-11
ANHUI QINGHUAFANG FINE BONE PORCELAIN
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the temperature difference in water exchange of bone china products produced in China is mostly below 140 °C, and some are even below 100 °C. Even high-quality bone china products can only exchange temperature differences in water of 160 °C, and their thermal shock resistance is poor. Influenced the promotion and use of bone china

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A new blank for bone china, containing the following components in weight percent: bovine bone powder 54%, kaolin 26%, quartz 10%, feldspar 8.8%, lithium china stone 0.46%, zircon sand 0.14%, nano trioxide Dialuminum 0.6%.

[0021] The particle size of the above-mentioned kaolin is 1-10 μm, the particle size of feldspar is 0.5-5 μm, the particle size of lithium china stone is 1-10 μm, and the particle size of zircon sand is 2-8 μm; Quartz composition with particle size: 10% quartz sand with a particle size of 25-35μm, 15% quartz sand with a particle size of 15-20μm, 50% quartz sand with a particle size of 5-10μm, and quartz sand with a particle size of 1-4μm 25%.

[0022] The preparation process of the blank for the above-mentioned novel bone china comprises the following steps:

[0023] (1) take each raw material by weighing above-mentioned formula ratio;

[0024] (2) Put the bovine bone meal into an oven and dry it at 70°C, then put it into a high-temperature calci...

Embodiment 2

[0026] A new blank for bone china, containing the following components in weight percent: 55% bovine bone powder, 26% kaolin, 9% quartz, 8.2% feldspar, 0.4% lithium china stone, 1% zircon sand, nano trioxide Dialuminum 0.4%.

[0027] The particle size of the above-mentioned kaolin is 1-10 μm, the particle size of feldspar is 0.5-5 μm, the particle size of lithium china stone is 1-10 μm, and the particle size of zircon sand is 2-8 μm; Quartz composition with particle size: 5% quartz sand with a particle size of 25-35μm, 10% quartz sand with a particle size of 15-20μm, 55% quartz sand with a particle size of 5-10μm, and quartz sand with a particle size of 1-4μm 30%.

[0028] The preparation process of the blank for the above-mentioned novel bone china comprises the following steps:

[0029] (1) take each raw material by weighing above-mentioned formula ratio;

[0030] (2) Put the bovine bone meal into an oven and dry it at 70°C, then put it into a high-temperature calciner, r...

Embodiment 3

[0032] A new blank for bone china, containing the following components in weight percent: 50% bovine bone meal, 27% kaolin, 11% quartz, 10% feldspar, 0.52% lithium china stone, 0.98% zircon sand, nano trioxide Dialuminum 0.5%.

[0033] The particle size of the above-mentioned kaolin is 1-10 μm, the particle size of feldspar is 0.5-5 μm, the particle size of lithium china stone is 1-10 μm, and the particle size of zircon sand is 2-8 μm; Quartz composition with particle size: 10% quartz sand with a particle size of 25-35μm, 15% quartz sand with a particle size of 15-20μm, 50% quartz sand with a particle size of 5-10μm, and quartz sand with a particle size of 1-4μm 25%.

[0034] The preparation process of the blank for the above-mentioned novel bone china comprises the following steps:

[0035] (1) take each raw material by weighing above-mentioned formula ratio;

[0036] (2) Put the bovine bone meal into an oven and dry it at 65-70°C, then put it into a high-temperature calci...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a novel preform body for bone porcelain and a preparation process of the preform body. The novel preform body for bone porcelain comprises the following components in percentage by weight: 50-55% of bone meal, 24-28% of kaolin, 9-11% of quartz, 8-10% of feldspar, 0.38-0.52% of lithium chinastone, 0.8-1.6% of zircon sand and 0.4-0.8% of nano-aluminum oxide. The preparation process comprises the following steps: mixing various ground materials with proper granularity to prepare the preform body, and calcining once again before the bone meal is mixed. The preform body prepared in the invention is good in thermal shock resistance, high in strength, uniform in structure, compact in toughness and excellent in overall performance.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a novel blank for bone china and a preparation process thereof. Background technique [0002] Bone china, formerly known as bone china, is a high-grade porcelain produced in the UK. It is generally referred to as bone china. It is made of traditional ceramic raw materials mixed with animal bone ashes and fired at high temperature. Bone china is a kind of soft porcelain, and the animal ashes used are mostly high-quality bovine bones. Therefore, bone china is fine in quality, smooth in glaze, soft in luster, like fat like jade, very elegant and luxurious, and has a high quality. Transparency and certain mechanical strength. Its owner has the reputation of "thin as paper, bright as mirror, white as jade, and sound like chime". In daily-use ceramics, bone china is widely used, and is recognized as the highest-grade porcelain in the world today, and is deeply loved by consumers. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/135
CPCC04B33/1355C04B2235/3217C04B2235/3248C04B2235/3418C04B2235/3463C04B2235/3472C04B2235/5436C04B2235/5445Y02P40/60
Inventor 裴仕林
Owner ANHUI QINGHUAFANG FINE BONE PORCELAIN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com