High-temperature-resistant ceramic bright red ink and method for preparing same

A technology of high-temperature-resistant ceramics and scarlet, which is applied in the field of high-temperature-resistant ceramic scarlet ink and its preparation, can solve the problems of bright red color becoming lighter, saturation color gamut narrow, and color not bright enough to achieve bright colors, stable performance indicators, Improves the effect of stability, smoothness and color development

Active Publication Date: 2017-08-11
江西禅信新材料科技有限公司
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such tiny particles are easily oxidized under high temperature conditions, and the difficulty of color development can be imagined. At present, there are "cadmium-selenium red-wrapped pigments" that can emit bright red in the world. The particle size is 4-10μm, such as To prepare bright red ink with it, it is necessary to use a sand mill to grind it to below 2 μm, and the coating layer of zirconium silicate will be destroyed during the grinding process, which will lead to the oxidation and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant ceramic bright red ink and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0092] A preparation method of high temperature resistant ceramic scarlet ink, the preparation method comprising:

[0093] The step of preparing the main ingredient: mixing the raw materials for preparing the main ingredient, stirring and dispersing with a dispersing mixer, and then grinding with a grinder using a three-stage flow circulation method to obtain the main ingredient;

[0094] Step of adding ingredients: adding propylene glycol methyl ether, diethylene glycol methyl ether, and diethylene glycol ethyl ether to the main ingredients after grinding, and mixing evenly to obtain a mixture;

[0095] Centrifugation step: the above-mentioned mixture is centrifuged with a centrifuge;

[0096] Multi-stage filtration step: the above-mentioned mixture after centrifugation is filtered through membranes with filter holes of 3 μm, 1 μm, and 1 μm respectively to obtain the finished product of scarlet ink;

[0097] The raw material for preparing the high temperature resistant ceram...

Embodiment 1

[0116] A kind of high temperature resistant ceramic bright red ink, its preparation method comprises:

[0117] The steps of preparing the main ingredient: mix the raw materials for the preparation of the main ingredient and then stir and disperse them with a dispersing mixer. The speed of the dispersing mixer is 1200r / min, and the stirring time is 20min. °C; the grinding time of each stage is controlled to be 1.5 hours, and the rotating speed of the grinding machine is 1400r / min, that is, the main material is obtained;

[0118] Adding batching steps: Add propylene glycol methyl ether, diethylene glycol methyl ether, and diethylene glycol ethyl ether to the above-mentioned main ingredients after grinding, and mix evenly to obtain a mixture. The viscosity of the mixture is 25op / 25°C and the surface tension is 30mN / m. The specific gravity is about 1.3010;

[0119] Centrifugation step: the above-mentioned mixture is centrifuged with a centrifuge, the centrifugation volume is cont...

Embodiment 2

[0134] A kind of high temperature resistant ceramic bright red ink, its preparation method comprises:

[0135] The steps of preparing the main ingredient: mix the raw materials for the preparation of the main ingredient and then stir and disperse them with a dispersing mixer. The speed of the dispersing mixer is 1400r / min, and the stirring time is 30min. °C; the grinding time of each stage is controlled to be 1.2 hours, and the rotating speed of the grinding machine is 1450r / min, that is, the main material is obtained;

[0136] Adding batching steps: Add propylene glycol methyl ether, diethylene glycol methyl ether, and diethylene glycol ethyl ether to the above-mentioned main ingredients after grinding, and mix evenly to obtain a mixture. The viscosity of the mixture is 30op / 25°C and the surface tension is 35mN / m. The specific gravity is about 1.3216;

[0137] Centrifugation step: the above-mentioned mixture is centrifuged with a centrifuge, the centrifugation volume is cont...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Surface tensionaaaaaaaaaa
Surface tensionaaaaaaaaaa
Surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention discloses high-temperature-resistant ceramic bright red ink. The high-temperature-resistant ceramic bright red ink comprises, by weight, 30%-50% of main materials, 10%-30% of propylene glycol monomethyl ether, 20%-50% of diethylene glycol methyl ether and 20%-40% of diethylene glycol diethylether. The main materials include, by weight, 10%-30% propylene glycol monomethyl ether, 10%-30% of diethylene glycol methyl ether, 20%-50% of diethylene glycol diethylether, 5%-10% of a dispersing agent, 0.1%-0.5% of a leveling agent and 20%-50% of inclusion toner. The invention further discloses a method for preparing the high-temperature-resistant ceramic bright red ink. The high-temperature-resistant ceramic bright red ink has pure color development, bright color, wide saturated color gamut and good resistance to high temperature.

Description

technical field [0001] The invention belongs to the technical field of ceramic printing and dyeing, and in particular relates to a high-temperature-resistant ceramic scarlet ink and a preparation method thereof. Background technique [0002] The development history of ceramics is an important part of the history of Chinese civilization. The invention and development of ceramics has unique significance in Chinese history. With the development of modern science and technology, many new ceramic varieties have appeared in the past century. They no longer use or rarely use traditional ceramic raw materials such as clay, feldspar, and quartz, but use other special raw materials. [0003] In order to improve the artistry and grade of ceramic products, ceramic decoration came into being. Ceramic decoration Various ways and techniques of artistic processing on ceramics; traditional ceramic decoration is to glaze the body to form patterns and colors on the ceramics. With the develop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/322C09D11/36
CPCC09D11/322C09D11/36
Inventor 曾繁明黄宾
Owner 江西禅信新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap