Liquid crystal display device and polarizing plate
A technology of liquid crystal display devices and polarizers, applied in optics, polarizing elements, nonlinear optics, etc., can solve the problems of expensive TAC film, inability to obtain mechanical strength, deterioration of moisture permeability, etc., and achieve good visibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment
[0105] Hereinafter, the present invention will be described in more detail with reference to the examples, but the present invention is not limited by the following examples, and can also be implemented with appropriate changes within the scope of the gist of the present invention, which are all included in the protection of the present invention. in range. In addition, the evaluation method of the physical property in the following Example is as follows.
[0106] (1) Refractive index of polyester film
[0107] Using a molecular orientation meter (manufactured by Oji Scientific Instruments Co., Ltd., MOA-6004 molecular orientation meter), the slow axis direction of the film was obtained, and a 4 cm × 2 cm film was cut out so that the slow axis direction was parallel to the long side. Rectangular, as a sample for measurement. For this sample, the refractive index (refractive index in the slow axis direction: Ny, fast axis ( The refractive index in the direction perpendicular...
manufacture example 1
[0122] (Manufacturing example 1-polyester A)
[0123] The esterification reaction tank was heated up, and when it reached 200°C, 86.4 parts by mass of terephthalic acid and 64.6 parts by mass of ethylene glycol were added, and 0.017 parts by mass of antimony trioxide and magnesium acetate tetrahydrate were added as catalysts while stirring. 0.064 parts by mass, 0.16 parts by mass of triethylamine. Next, after pressurizing and raising temperature, and carrying out pressurized esterification reaction on gauge pressure 0.34MPa, 240 degreeC conditions, the esterification reaction tank was returned to normal pressure, and phosphoric acid 0.014 mass part was added. Furthermore, it heated up to 260 degreeC over 15 minutes, and added 0.012 mass parts of trimethyl phosphates. Then, 15 minutes later, dispersion treatment was performed with a high-pressure disperser, and 15 minutes later, the obtained esterification reaction product was transferred to a polycondensation reaction tank, a...
manufacture example 2
[0125] (Manufacturing example 2-polyester B)
[0126] 10 parts by mass of dry ultraviolet absorber (2,2'-(1,4-phenylene)bis(4H-3,1-benzoxazin-4-one), PET (A) not containing particles (Intrinsic viscosity is 0.62dl / g) 90 parts by mass were mixed, and a polyethylene terephthalate resin (B) containing an ultraviolet absorber was obtained using a kneading extruder. (hereinafter abbreviated as PET (B))
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle size | aaaaa | aaaaa |
| temperature | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |