Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Preparation method for anti-insect surface material of hard plastic-wood composite floor

A composite floor, hard technology, applied in the field of wood-plastic floor, can solve the problems of human harm, poor ventilation effect, chemical composition residue, etc., to achieve the effect of improving the duration, good repelling effect, and improving the effect of repelling insects.

Inactive Publication Date: 2017-08-22
ZHEJIANG YUANSENTAI FURNITURE
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional insect control method for indoor furniture mostly uses chemically synthesized pyrethroid insect repellent. Although the insect repellant is effective, in some specific occasions, such as hotels, due to safety considerations, the window openings are small, and the indoor ventilation effect is very poor. , these chemical components will remain in a large amount indoors and cause certain harm to the human body, so it is necessary to study a composite floor surface material with an insect-proof effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A preparation method of a hard plastic-wood composite floor surface material with an insect-proof effect is carried out according to the following steps:

[0043] A. Put each raw material into a high-speed mixer for mixing, the temperature is 100°C, the mixing time is 12min, and the mixing speed is 1120rpm;

[0044] B. In the third step, the mixed material is granulated by a special granulator; the temperature is 175°C, and the screw speed is 220rpm;

[0045] C. Use an extruder to extrude the granulated material into shape, and the extrusion temperature is 170°C.

[0046] The raw material in the described step A comprises the composition of following percentage by weight:

[0047] Talc 8%

[0048] Sarin resin 7%

[0049] Wood flour 10%

[0050] Maleic anhydride grafted polyethylene 2%

[0051] Lubricant 1%

[0052] Antioxidant 0.5%

[0053] UV absorber 0.5%

[0054] Natural Plant Modified Insect Repellent 1.5%

[0055] HDPE allowance.

[0056] The particle siz...

Embodiment 2

[0063] A preparation method of a hard plastic-wood composite floor surface material with an insect-proof effect is carried out according to the following steps:

[0064] A. Put each raw material into a high-speed mixer for mixing, the temperature is 80°C, the mixing time is 15min, and the mixing speed is 1000rpm;

[0065] B. In the third step, the mixed material is granulated by a special granulator; the temperature is 180°C, and the screw speed is 150rpm;

[0066] C. Use an extruder to extrude the granulated material into shape, and the extrusion temperature is 180°C.

[0067] The raw material in the described step A comprises the composition of following percentage by weight:

[0068] Talc 10%

[0069] Sarin resin 5%

[0070] Wood flour 12%

[0071] Maleic anhydride grafted polyethylene 1.5%

[0072] Lubricant 1.5%

[0073] Antioxidant 0.3%

[0074] UV absorber 0.6%

[0075] Natural Plant Modified Insect Repellent 1%

[0076] HDPE (High Density Polyethylene) balance. ...

Embodiment 3

[0084] A preparation method of a hard plastic-wood composite floor surface material with an insect-proof effect is carried out according to the following steps:

[0085] A. Put each raw material into a high-speed mixer for mixing, the temperature is 120°C, the mixing time is 10min, and the mixing speed is 1200rpm;

[0086] B. In the third step, the mixed material is granulated by a special granulator; the temperature is 160°C, and the screw speed is 300rpm;

[0087] C. Use an extruder to extrude the granulated material into shape, and the extrusion temperature is 160°C.

[0088] The raw material in the described step A comprises the composition of following percentage by weight:

[0089] Talc 6%

[0090] Sarin resin 8%

[0091] Wood flour 8%

[0092] Maleic anhydride grafted polyethylene 2.5%

[0093] Lubricant 0.8%

[0094] Antioxidant 0.6%

[0095] UV absorber 0.3%

[0096] Natural Plant Modified Insect Repellent 2%

[0097] HDPE (High Density Polyethylene) balance....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method for an anti-insect surface material of a hard plastic-wood composite floor. The surface material mainly comprises talcum powder, sarin resin, wood powder, maleic anhydride-grafted polyethylene, a lubricant, an anti-oxidant, an ultraviolet ray absorber, a natural plant-modified insect repellant and HDPE. The surface material is good in bonding performance, not prone to delamination, resistant to wear, corrosion, skidding, ultraviolet rays and ageing and capable of repelling insects. The surface of the surface material can be subjected to sanding, embossing, polishing, drawing, etc. After molding of the surface material, wood-imitating effect, stone-imitating effect and the like can be obtained after processing, and the surface material is hard. Since cattail wool is used as a main component of the insect repellant, good insect-repelling effect and refreshing and tranquillizing effect are obtained.

Description

technical field [0001] The invention relates to the technical field of wood-plastic flooring, in particular to a method for preparing a hard plastic-wood composite floor surface material with an insect-proof effect. Background technique [0002] Wood-plastic composites (Wood~polymer Composites, abbreviated as WPC) is a new type of material that is made of wood fiber or plant fiber as the main component, which is combined with thermoplastic resin or other materials after pretreatment. This material can give full play to the advantages of each component in the material and overcome the shortcomings of a single material. It can not only improve the physical and mechanical properties and processing properties of the material, reduce costs and expand the application range, but also increase the added value of the material. Since the product is in a multiphase state of crystalline (wood fiber or plant fiber) and disordered state (resin), it has both the high strength and high hard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L51/06C08L97/02C08K13/04C08K7/26C08K3/34C08K5/00E04F15/10E04F15/18
CPCC08L23/06C08L2205/035C08L2205/16C08L2207/062E04F15/10E04F15/181E04F2290/04C08L23/0876C08L51/06C08L97/02C08K13/04C08K7/26C08K3/34C08K5/0058
Inventor 王同文
Owner ZHEJIANG YUANSENTAI FURNITURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com