Purifying agent for water purification equipment and preparation method thereof

A technology of water purification equipment and purifying agent, which is applied in chemical instruments and methods, other chemical processes, water/sewage treatment, etc. Effective removal of impurities, low processing equipment requirements, and strong adsorption

Inactive Publication Date: 2017-09-01
HEFEI ZHENXUN LOW TEMPERATURE TECH CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent application is only in the stage of laboratory testing. In the embodiment, sulfuric acid should be added to the beaker containing iron oxide waste residue in stages, and the reaction temperature should be controlled at 40-70°C, which is difficult to grasp in actual production. In addition, the production process is not Adding oxidant, ferrous iron cannot be converted into ferric iron, and the polymerization effect cannot be achieved, and the substances in iron slag are impure, solid and liquid are not separated, and the water insoluble content is too high, which affects the water purification effect, and does not have industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A purifying agent for water purification equipment, comprising the following raw materials in parts by weight: 56 parts of attapulgite, 38 parts of zinc oxide, 50 parts of silicon oxide, 40 parts of aluminum oxide and 33 parts of nickel.

[0025] A preparation method for a purifying agent for water purifying equipment, comprising the following steps:

[0026] 1. Dry attapulgite and pulverize into granules, and then pulverize zinc oxide, silicon oxide, aluminum oxide and nickel into granules respectively;

[0027] 2. Add the granular ingredients of step 1 into the blender and stir for 50 minutes to obtain mixture 1, add 30% water according to the weight ratio of mixture 1 for wetting, and obtain mixture 2;

[0028] 3. Roll the mixture two pairs of rollers for 5 times, and control the thickness to 3mm to obtain a sheet;

[0029] 4. Roast the flakes at 800°C for 60 minutes to obtain a semi-finished product;

[0030] 5. Put the semi-finished product into the mill for grin...

Embodiment 2

[0036] A purifying agent for water purification equipment, comprising the following raw materials in parts by weight: 80 parts of attapulgite, 35 parts of zinc oxide, 40 parts of silicon oxide, 50 parts of aluminum oxide and 40 parts of nickel.

[0037] A preparation method for a purifying agent for water purifying equipment, comprising the following steps:

[0038] 1. Dry attapulgite and pulverize into granules, and then pulverize zinc oxide, silicon oxide, aluminum oxide and nickel into granules respectively;

[0039] 2. Add the granular ingredients in step 1 to the blender and stir for 30 minutes to obtain mixture 1. Add 40% water according to the weight ratio of mixture 1 for wetting to obtain mixture 2;

[0040] 3. Roll the mixture two pairs of rollers for 3 times, and control the thickness to 1mm to obtain a sheet;

[0041] 4. Roast the flakes at 600°C for 40 minutes to obtain a semi-finished product;

[0042] 5. Put the semi-finished product into the mill for grinding...

Embodiment 3

[0048] A purification agent for water purification equipment, comprising the following raw materials in parts by weight: 50 parts of attapulgite, 45 parts of zinc oxide, 40 parts of silicon oxide, 30 parts of aluminum oxide and 40 parts of nickel.

[0049] A preparation method for a purifying agent for water purifying equipment, comprising the following steps:

[0050] 1. Dry attapulgite and pulverize into granules, and then pulverize zinc oxide, silicon oxide, aluminum oxide and nickel into granules respectively;

[0051] 2. Add the granular ingredients of step 1 into the blender and stir for 50 minutes to obtain mixture 1, add 40% water according to the weight ratio of mixture 1 for wetting, and obtain mixture 2;

[0052] 3. Roll the mixture two pairs of rollers for 5 times, and control the thickness to 3mm to obtain a sheet;

[0053] 4. Roast the flakes at 800°C for 60 minutes to obtain a semi-finished product;

[0054] 5. Put the semi-finished product into the mill for g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a purifying agent for water purification equipment and a preparation method thereof. The purifying agent is prepared from the following components: attapulgite, zinc oxide, silicon oxide, alumina and nickel. The preparation method comprises the following steps: 1, drying attapulgite, grinding into particles, and respectively grinding the zinc oxide, silicon oxide, alumina and nickel into particles; 2, adding the particles in the step 1 into a stirrer, stirring for 30-50 minutes to obtain mixture 1, and adding water which is 30-40 percent of the weight of the mixture 1 for wetting to obtain mixture 2; 3, rolling the mixture 2 for 3-5 times with a roller, and controlling the thickness to be 1-3mm to obtain flakes; 4, roasting the flakes at 600-800 DEG C for 40-60 minutes to obtain a semi-finished product; and 5, grinding the semi-finished product in a grinder to obtain powder having a particle fineness of less than 50mu m, and packaging for molding. The purifying agent has relatively strong adsorbability, and can be used for effectively removing impurities in water; and the preparation process is simple, is easy to operate, and has low requirements for processing equipment.

Description

technical field [0001] The invention belongs to the technical field of purifying agents, and in particular relates to a purifying agent used in water purification equipment and a preparation method thereof. Background technique [0002] Aluminum and iron polymer inorganic polymer water purifiers are a new type of chemical industry researched and developed from the 1970s to the 1990s, which has played a great role in improving people's quality of life and improving the environment. There are many types of water purifiers, and the production processes are different. At present, the waste residue of the sulfuric acid plant is discharged randomly, causing environmental pollution, which urgently needs to be treated. Chinese patent CN1219507A discloses a "one-step production process of polymeric ferric sulfate solid water purifying agent", which uses iron oxide-containing waste residues from iron and steel plants and sulfuric acid plants to react with oxidants to produce iron-bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J20/12B01J20/30C02F1/28
CPCB01J20/12B01J20/02B01J20/06B01J20/08B01J20/103C02F1/281C02F2303/02
Inventor 周青松
Owner HEFEI ZHENXUN LOW TEMPERATURE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products