Inner wall brick and preparation method thereof

A technology for interior walls and raw materials, applied in building components, buildings, building structures, etc., can solve the problems of poor wall brick strength, reduced arable land resources, easy damage, etc., to achieve a short construction period, remove odor, and improve crack resistance. Effect

Inactive Publication Date: 2017-09-15
合肥市淑芹美装饰工程有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large number of wall bricks are fired with clay, which leads to the reduction of cultivated land resources, and the strength of the produced wall bricks is poor, and it is easy to be damaged if it bears a large weight

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] An interior wall brick, including the following raw materials:

[0030] 55 parts of cement;

[0031] 45 parts of stuffing;

[0032] 25 parts of plant straw;

[0033] 20 parts water glass;

[0034] 20 parts of carboxymethyl cellulose;

[0035] 15 parts of natural colored sand;

[0036] 15 parts of latex powder;

[0037] 10 copies of reinforcing materials;

[0038] 10 parts of starch ether;

[0039] Accelerator 5 parts;

[0040] Foaming agent 5 parts;

[0041] 75 parts of water;

[0042] The filler includes the following raw materials in parts: 15 parts of bentonite, 10 parts of attapulgite, 10 parts of mica powder, 5 parts of tourmaline powder and 2 parts of diatomite.

[0043] Wherein, the cement is ordinary Portland cement, and the natural colored sand is 110 mesh.

[0044] Wherein, the latex powder is renewable latex powder, the reinforcing material is glass fiber, and the sintering aid is TiO 2 Micronized.

[0045] Wherein, the starch ether is hydroxypro...

Embodiment 2

[0058] An interior wall brick, including the following raw materials:

[0059] 65 parts of cement;

[0060] Filling 50 parts;

[0061] 35 parts of plant straw;

[0062] 25 parts of water glass;

[0063] 23 parts of carboxymethyl cellulose;

[0064] 20 parts of natural colored sand;

[0065] 17 parts of latex powder;

[0066] 15 copies of reinforcing materials;

[0067] 13 parts of starch ether;

[0068] Accelerator 10 parts;

[0069] Foaming agent 8 parts;

[0070] 95 parts of water;

[0071] The filler includes the following raw materials in parts: 17 parts of bentonite, 15 parts of attapulgite, 12 parts of mica powder, 8 parts of tourmaline powder and 5 parts of diatomite.

[0072] Wherein, the cement is high alumina cement, and the natural colored sand is 150 mesh.

[0073] Wherein, the latex powder is renewable latex powder, the reinforcing material is carbon fiber, and the sintering aid is Cr 2 o 3 Micronized.

[0074] Wherein, the starch ether is hydroxypro...

Embodiment 3

[0087] An interior wall brick, including the following raw materials:

[0088] 60 parts of cement;

[0089] 47.5 parts of filler;

[0090] 30 parts of plant straw;

[0091] 22.5 parts of water glass;

[0092] 21.5 parts of carboxymethyl cellulose;

[0093] 17.5 parts of natural colored sand;

[0094] 16 parts of latex powder;

[0095] Reinforcing material 12.5 parts;

[0096] 11.5 parts of starch ether;

[0097] Accelerator 7.5 parts;

[0098] 6.5 parts of blowing agent;

[0099] 85 parts of water;

[0100] The filler includes the following raw materials in parts: 16 parts of bentonite, 12.5 parts of attapulgite, 11 parts of mica powder, 6.5 parts of tourmaline powder and 3.5 parts of diatomite.

[0101] Wherein, the cement is high alumina cement, and the natural colored sand is 130 mesh.

[0102] Wherein, the latex powder is renewable latex powder, the reinforcing material is carbon fiber, and the sintering aid is Cr 2 o 3 Micronized.

[0103] Wherein, the starc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an inner wall brick and a preparation method thereof and relates to the technical field of wall bricks. The inner wall brick is prepared from 55 to 65 portions of cement, 45 to 50 portions of a filler, 25 to 35 portions of plant straws, 20 to 25 portions of water glass, 20 to 23 portions of carboxymethyl cellulose, 15 to 20 portions of natural colored sand, 15 to 17 portions of latex powder, 10 to 15 portions of a reinforcing material, 10 to 13 portions of starch ether, 5 to 10 portions of an accelerator, 5 to 8 portions of a foaming agent and 75 to 95 portions of water. The inner wall brick can be directly used for an inner wall, has light weight, high strength and good thermal insulation effects, and has the characteristics of acid and alkali resistance, water resistance, fire resistance, freezing resistance, aging resistance, sound absorption, low installation and use cost and short construction period.

Description

technical field [0001] The invention relates to the technical field of wall bricks, in particular to an interior wall brick and a preparation method thereof. Background technique [0002] In the prior art, the production of wall bricks used for building houses generally has the following steps: digging out the soil and mixing it with water to form it, and sending the green body into a kiln for firing after drying in the shade. Due to the rapid development of the real estate industry, the demand for wall tiles has also increased rapidly. However, a large number of wall bricks are fired with clay, which leads to the reduction of cultivated land resources, and the strength of the produced wall bricks is poor, and it is easy to be damaged if it bears a large weight. Contents of the invention [0003] The purpose of the present invention is to provide an interior wall brick and its preparation method, which can be directly used for interior walls, light weight, high strength a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/10C04B28/04E04C1/00
CPCC04B28/04C04B2111/00017C04B2111/00025C04B2111/40C04B2111/52E04C1/00C04B14/068C04B14/104C04B14/102C04B14/20C04B14/36C04B14/08C04B18/24C04B24/26C04B22/00C04B22/06C04B14/42C04B24/38C04B24/04C04B22/062C04B24/14C04B24/34C04B38/10C04B14/386
Inventor 岳佐梅
Owner 合肥市淑芹美装饰工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com