Process for preparing PVC (Polyvinyl Chloride) wood-plastic composite decorative board

A preparation process and wood-plastic composite technology, which is applied in the field of material processing, can solve the problems that the foaming effect needs to be optimized, and there are many factors affecting the wood-plastic composite foam material, so as to improve the fixing effect, improve the modification effect, and ensure the comprehensive characteristics. Effect

Inactive Publication Date: 2017-10-10
安徽吉美装饰材料有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are various foaming processes for wood-plastic composite materials, there are many factors affecting wood-plastic composite foam materials, and the improvement of foaming effect still needs to be optimized.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A preparation process of PVC wood-plastic composite decorative board includes the following steps:

[0028] (1) Wood flour drying treatment:

[0029] The rubber wood powder is dried first, and dried until the overall water content is 4%, and then screened until the mesh size is 40-60 meshes for use;

[0030] (2) Wood flour modification treatment:

[0031] a. Put the rubber wood powder treated in step (1) into a steam explosion machine for steam explosion treatment, take it out and then immerse it in the silane coupling agent aqueous solution for 40 minutes, and finally take it out and dry it for use;

[0032] b. Immerse the rubber wood powder treated in operation a into the modified aqueous solution, and filter it out for use after immersion treatment for 25 minutes. The substances and their weight percentages in the modified aqueous solution are: 5% nano titanium dioxide, 0.8% Sodium hydroxide, the balance is water;

[0033] (3) Mixing and extrusion:

[0034] Mix the rubber wood ...

Embodiment 2

[0044] A preparation process of PVC wood-plastic composite decorative board includes the following steps:

[0045] (1) Wood flour drying treatment:

[0046] The rubber wood powder is dried first, and dried until the overall water content is 5%, and then screened until the mesh size is 40-60 meshes for use;

[0047] (2) Wood flour modification treatment:

[0048] a. Put the rubber wood powder processed in step (1) into a steam blaster for steam explosion treatment, take it out and immerse it in the silane coupling agent aqueous solution for 45 minutes, and finally take it out and dry it for use;

[0049] b. Immerse the rubber wood powder treated in operation a into the modified aqueous solution, and filter it out for use after immersion for 28 minutes. The substances and weight percentages in the modified aqueous solution are: 7% nano titanium dioxide, 1.2% Sodium hydroxide, the balance is water;

[0050] (3) Mixing and extrusion:

[0051] Mix the rubber wood powder treated in step (2) wi...

Embodiment 3

[0061] A preparation process of PVC wood-plastic composite decorative board includes the following steps:

[0062] (1) Wood flour drying treatment:

[0063] The rubber wood powder is dried first, and dried to a total water content of 6%, and then screened to a mesh size of 40-60 meshes for use;

[0064] (2) Wood flour modification treatment:

[0065] a. Put the rubber wood powder treated in step (1) into a steam explosion machine for steam explosion treatment, take it out and then immerse it in the silane coupling agent aqueous solution for 50 minutes, and finally take it out and dry it for later use;

[0066] b. Immerse the rubber wood powder treated in operation a in the modified aqueous solution, and filter it out for use after immersion for 30 minutes. The substances in the modified aqueous solution and their weight percentages are: 8% nano titanium dioxide, 1.5% Sodium hydroxide, the balance is water;

[0067] (3) Mixing and extrusion:

[0068] Mix the rubber wood powder treated in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a process for preparing a PVC (Polyvinyl Chloride) wood-plastic composite decorative board. The process comprises the following steps: (1) performing wood flour drying treatment; (2) performing wood flour modification treatment; and (3) mixing extrusion. According to the process disclosed by the invention, the raw materials are modified, the process is optimized, the overall characteristics of the PVC wood-plastic composite decorative board are well improved, the characteristics such as flame-retardant property, wear resistance, bending strength, board nail-holding ability and the like are well improved, the soaking swell rate is reduced, the comprehensive usage value is high, and the market competitiveness is high.

Description

Technical field [0001] The invention belongs to the technical field of material processing, and specifically relates to a preparation process of a PVC wood-plastic composite decorative board. Background technique [0002] Wood-plastic composite material is a new type of environmentally friendly material. It uses plant wood powder or wood fiber as a reinforcing filler. After pretreatment, it is mixed with thermoplastics (1 or more), and some other additives are added at the same time. After hot pressing , Extrusion, injection molding and other methods. Wood-plastic composite material has the dual characteristics of wood and plastic, and can be processed into a variety of colors. The texture and processing performance are similar to wood. At the same time, it also has stable chemical properties, high strength, good insect resistance, and can be recycled. The advantage is that it is an ideal substitute wood material. Excellent comprehensive properties make wood-plastic composite m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08K3/22C08K3/34C08K3/30C08K3/26C08J9/10C08J9/08
CPCC08J9/08C08J9/103C08J2203/02C08J2203/04C08J2327/06C08J2497/02C08K2003/2241C08K2003/265C08K2003/3045C08K2201/011C08L27/06C08L2201/02C08L2203/14C08L2205/03C08L97/02C08K3/22C08K3/34C08K3/30C08K3/26
Inventor 胡其飞
Owner 安徽吉美装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com