Resin composition and its application

A technology of resin composition and epoxy resin, which can be applied in application, epoxy resin glue, and other household appliances, etc., and can solve the problems of low metal-clad peel strength, poor glue, low mechanical strength, etc.

Active Publication Date: 2021-06-01
KUANG CHI INST OF ADVANCED TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problems of low metal-clad peel strength, low mechanical strength, poor moldability of prepreg laying and appearance of bubbles and bad glue spots in the composite material with high molecular weight unsaturated hydrocarbon as the main resin, and provide a A resin composition with high metal adhesion strength, high mechanical strength, good paving formability and good appearance is used in the production of composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin composition and its application
  • Resin composition and its application
  • Resin composition and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0112] Weigh 20 parts by weight of dicyclopentadiene type polyfunctional epoxy resin, 8 parts by weight of MDI modified epoxy resin, 5 parts by weight of epoxy resin containing alicyclic ring, 40 parts by weight of polyphenylene ether, 8 parts by weight of bisphenol A Add cyanotype ester and 0.01 parts by weight of 2-methylimidazole (2-MI) into 122 parts by weight of butanone to form a resin solution with a solid content of 60%.

[0113] Use 8 sheets (200mm*200mm) of 7628 quartz cloth to immerse in the above resin solution for impregnation. Bake in an oven at 80°C / 2 minutes + 130°C / 3 minutes + 175°C / 5 minutes to make a semi-cured adhesive sheet.

[0114] Superimpose and align the above 8 adhesive sheets, with a 35um copper foil on the top and bottom. In the vacuum press, according to the temperature of 210 ℃, the pressure of 25kgf / cm 2 Conditions, pressed for 160 minutes to make a double-sided copper clad laminate with a thickness of 1.6mm.

Embodiment 2

[0116] Take by weighing 35 parts by weight of o-phenyl phenolic type polyfunctional epoxy resin, 15 parts by weight of MDI modified epoxy resin, 10 parts by weight of epoxy resin containing alicyclic ring, 65 parts by weight of polyphenylene ether, 16 parts by weight of dicyclopentadiene Phenolic cyanate resin and 0.05 parts by weight of 2-methylimidazole (2-MI) were added to 212 parts by weight of butanone to form a resin solution with a solid content of 60%.

[0117] Use 8 sheets (200mm*200mm) of 7628 quartz cloth to immerse in the above resin solution for impregnation. Bake in an oven at 80°C / 2 minutes + 130°C / 3 minutes + 175°C / 5 minutes to make a semi-cured adhesive sheet.

[0118] Superimpose and align the above 8 adhesive sheets, with a 35um copper foil on the top and bottom. In the vacuum press, according to the temperature of 210 ℃, the pressure of 25kgf / cm 2 Conditions, pressed for 160 minutes to make a double-sided copper clad laminate with a thickness of 1.6mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to resin composition and its application. Specifically, the present invention relates to a resin composition, which contains: 20 to 35 parts by weight of multifunctional epoxy resin; 8 to 15 parts by weight of isocyanate modified epoxy resin; 5 to 15 parts by weight of difunctional epoxy resin 10 parts by weight; 40-65 parts by weight of polyphenylene ether resin; and 8-16 parts by weight of cyanate resin. The present invention also relates to products of the resin composition, including resin films, adhesive sheets, prepregs, composite materials, laminates and printed circuit boards. Through the combination of different resins, this application realizes the superimposition of product performance, so that the product not only has a good appearance, but also has the comprehensive effects of heat resistance, low dielectric loss and easy processing.

Description

technical field [0001] The present invention relates to resin composition and its application. Background technique [0002] Polyphenylene ether resin has excellent dielectric properties due to its symmetrical molecular structure and low molecular dipole moment, and is favored by many workers engaged in new material development. The resin matrix with modified polyphenylene ether as curing agent has been widely used in composite substrates and high-frequency circuit boards. [0003] The resin composition of the prior art is: high molecular weight polybutadiene resin, containing more than 70wt% of vinyl, the weight average molecular weight MW is greater than 100000, accounting for 0-15wt% of composition weight; low molecular weight polybutadiene resin, containing More than 70wt% of vinyl groups have a weight-average molecular weight MW of 1000-10000, accounting for 10-40wt% of the weight of the composition; modified polyphenylene ether resins have a weight-average molecular w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G59/62C08G59/40C08G59/38C08G59/32C08G59/20C08G59/24C08L63/00C09J163/00B32B15/14B32B27/04
CPCB32B15/14B32B2260/021B32B2260/046B32B2457/08C08G59/20C08G59/245C08G59/3218C08G59/38C08G59/4014C08G59/62C08J5/18C08J2363/00C08L63/00C08L2201/08C08L2203/16C08L2203/20C09J7/00C09J163/00
Inventor 不公告发明人
Owner KUANG CHI INST OF ADVANCED TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com