Preparation method of antibacterial polyvinyl chloride pipe material

A polyvinyl chloride and pipe technology, which is applied in the field of antibacterial polyvinyl chloride pipe preparation, can solve the problems of poor antibacterial properties and easy breaking of PVC pipes, and achieves the effects of not easy to break, strong binding force and good application prospects.

Inactive Publication Date: 2017-10-27
ANHUI LANTONG TECH CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, PVC pipes still have the problems of poor antibact

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A method for preparing an antibacterial polyvinyl chloride pipe, comprising the steps of:

[0017] S1. Mix polyvinyl chloride and neoprene, heat up and stir to obtain the first premix;

[0018] S2. Heat the solid paraffin, add octadecyltrimethylammonium bromide and cotton linters and stir, microwave expansion, adjust the temperature and stir, add copper chloride aqueous solution, adjust the temperature and stir, cool, dry, pulverize, add the first Stir the premix, bentonite, and calcined kaolin evenly, add antioxidants, microcrystalline paraffin, and magnesium hydroxide, stir evenly, cool to room temperature, and stand to obtain the second prefabricated material;

[0019] S3. Putting the second prefabricated material into an extruder and extruding to obtain an antibacterial polyvinyl chloride pipe.

Embodiment 2

[0021] A method for preparing an antibacterial polyvinyl chloride pipe, comprising the steps of:

[0022] S1. Mix 40 parts of polyvinyl chloride and 15 parts of chloroprene rubber in parts by weight, heat up to 155° C. and stir for 10 minutes to obtain the first premix;

[0023] S2. Heat 5 parts of solid paraffin to 90°C in parts by weight, add 1 part of octadecyltrimethylammonium bromide, 40 parts of cotton linters and stir for 2 hours, microwave expansion for 100s, microwave power is 500W, and adjust the temperature to 130 Stir at ℃ for 20 minutes, add 200 parts of copper chloride aqueous solution with a concentration of 2 wt %, adjust the temperature to 70 ° C and stir for 2 hours, cool, dry, pulverize, add 100 parts of the first premix, 5 parts of bentonite, and 20 parts of calcined kaolin and stir evenly. Add 1 part of antioxidant, 3 parts of microcrystalline paraffin, and 20 parts of magnesium hydroxide, stir evenly, cool to room temperature, and let stand for 4 hours to...

Embodiment 3

[0026] A method for preparing an antibacterial polyvinyl chloride pipe, comprising the steps of:

[0027] S1. Mix 80 parts of polyvinyl chloride and 5 parts of chloroprene rubber in parts by weight, heat up to 165° C. and stir for 5 minutes to obtain the first premix;

[0028] S2. Heat 15 parts of solid paraffin to 80°C in parts by weight, add 3 parts of octadecyltrimethylammonium bromide and 20 parts of cotton linters and stir for 4 hours, microwave expansion for 50s, microwave power is 600W, and adjust the temperature to 120 Stir for 50 minutes at ℃, add 100 parts of copper chloride aqueous solution with a concentration of 4wt%, adjust the temperature to 60°C and stir for 4 hours, cool, dry, pulverize, add 50 parts of the first premix, 15 parts of bentonite, and 10 parts of calcined kaolin and stir evenly. Add 3 parts of antioxidant, 1 part of microcrystalline paraffin, and 40 parts of magnesium hydroxide, stir evenly, cool to room temperature, and let stand for 2 hours to o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of an antibacterial polyvinyl chloride pipe material. The preparation method comprises the following steps: mixing polyvinyl chloride and chloroprene rubber, heating and stirring, so that a first premixture is obtained; heating solid paraffin, adding octadecyl trimethyl ammonium bromide and cotton linters, stirring, carrying out microwave expansion, regulating temperature and stirring, adding a copper chloride aqueous solution, regulating temperature and stirring, cooling, drying, smashing, adding the first premixture, bentonite and calcined kaolin, uniformly stirring, adding an antioxidant, microcrystalline wax and magnesium hydroxide, uniformly stirring, cooling to room temperature, and standing, so that a second premix is obtained; and putting the second premix into an extruding machine, and extruding, so that the antibacterial polyvinyl chloride pipe material is obtained. The preparation method of the antibacterial polyvinyl chloride pipe material is simple in operation, raw materials are available, cost is low, the obtained polyvinyl chloride pipe material has excellent antibacterial property and good mechanical properties, toughness and hardness reach the equilibrium, and the antibacterial polyvinyl chloride pipe material is difficult to break.

Description

technical field [0001] The invention relates to the technical field of polyvinyl chloride, in particular to a method for preparing an antibacterial polyvinyl chloride pipe. Background technique [0002] As one of the products of the development of science and technology, PVC pipes can be seen in daily life. The late 1990s was a period of rapid development of PVC pipes in mainland China. During this period, some factories with an annual production capacity of more than 50,000 tons have been built and put into operation, and there are more than 30 PVC pipe factories with an annual production capacity of more than 10,000 tons. The annual production capacity of plastic pipes is 2 million tons. However, at present, PVC pipes still have the problems of poor antibacterial properties and easy breakage, which need to be improved urgently. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a met...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L11/00C08L91/06C08L1/02C08K13/02C08K5/19C08K3/34C08K3/22B29C47/92B29C48/92
CPCC08L27/06B29C48/92B29C2948/9258B29C2948/92704C08K2003/2224C08K2201/014C08L2203/18C08L2205/025C08L2205/035C08L2205/16C08L11/00C08L91/06C08L1/02C08K13/02C08K5/19C08K3/346C08K3/22
Inventor 谭中全
Owner ANHUI LANTONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap