A kind of preparation method of wax remover

A wax remover and a technology for preparation steps, applied in the field of wax remover preparation, can solve the problems of corrosion of metal workpieces, slow wax removal rate, poor wax removal effect, etc. The effect of wax efficiency

Active Publication Date: 2019-12-03
SUZHOU YUANLIAN SCI & TECH PIONEER PARK MANAGEMENT CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention: Aiming at the problems that traditional wax removers have slow wax removal rate, poor wax removal effect and corrosiveness to metal workpieces, a preparation method of wax remover is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0018] First select 5kg of tea seed meal, grind it and pass through an 80-mesh sieve, then mix the sieved tea seed meal with petroleum ether at a mass ratio of 1:10, ultrasonically vibrate at 300W for 15min, and then heat it at 50°C Heat in a water bath for 2 hours, filter to obtain a filter cake, dry the filter cake at 80°C for 8 hours, and prepare dry defatted tea seed meal; mix the dry defatted tea seed meal with deionized water at a mass ratio of 1:10, and heat to boiling Insulate and heat for 2 hours. After the heat preservation and heating are completed, then rotatively evaporate at 80°C to dryness to obtain modified water-extracted tea seed meal powder; then select 400g of calcium oxide and 800g of graphite and mix them in a ball mill tank, at 500r / min Put down the ball mill for 5 hours, after the ball milling is completed, pass through a 100-mesh sieve to obtain the mixed powder, weigh 600g of the mixed powder and place it in a resistance furnace, keep it for calcinatio...

example 2

[0021]First select 3kg of tea seed meal, grind it and pass through an 80-mesh sieve, then mix the sieved tea seed meal with petroleum ether at a mass ratio of 1:10, ultrasonically vibrate at 200W for 10min, and then heat it at 45°C Heat in a water bath for 1 hour, filter to obtain a filter cake, dry the filter cake at 80°C for 8 hours, and prepare dry defatted tea seed meal; mix the dry defatted tea seed meal with deionized water at a mass ratio of 1:10, and heat to boiling Insulate and heat for 1 hour. After the heat preservation and heating are completed, then rotate evaporate to dryness at 75°C to obtain modified water-extracted tea seed meal powder; then select 300g of calcium oxide and 600g of graphite and mix them in a ball mill tank. Put down the ball mill for 3 hours, after the ball milling is completed, pass through a 100-mesh sieve to obtain the mixed powder, weigh 500g of the mixed powder and place it in a resistance furnace, heat-preserve and calcinate at 1800°C for...

example 3

[0024] First select 4kg of tea seed meal, grind it and pass through an 80-mesh sieve, then mix the sieved tea seed meal with petroleum ether at a mass ratio of 1:10, ultrasonically vibrate at 250W for 12min, and then heat it at 47°C Heat in a water bath for 2 hours, filter to obtain a filter cake, dry the filter cake at 77°C for 7 hours, and prepare dry defatted tea seed meal; mix the dry defatted tea seed meal with deionized water at a mass ratio of 1:10, and heat to boiling Insulate and heat for 2 hours. After the heat preservation and heating are completed, then rotatively evaporate at 77°C to dryness to obtain modified water-extracted tea seed meal powder; then select 350g of calcium oxide and 700g of graphite and mix them in a ball mill tank. Put down the ball mill for 4 hours, and after the ball milling is completed, pass through a 100-mesh sieve to obtain the mixed powder, weigh 550g of the mixed powder and place it in a resistance furnace, heat-preserve and calcinate at...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method for a wax removing agent, and belongs to the technical field of metal cleaning. The method comprises the steps that firstly oil-tea-cake middle grease is removed by utilizing petroleum ether, dried and degreased oil-tea-cake is obtained through filtering and drying, then the dried and degreased oil-tea-cake and water are mixed, heated and rotated and evaporated till the oil-tea-cake is dried, and modified aqueous-extract oil-tea-cake powder is obtained; calcium oxide and graphite are mixed, ball-milled and calcined, mixed modified powder is obtained, then sepiolite particles are taken as raw materials, and sepiolite fiber serous fluid is prepared and obtained; and the sepiolite fiber serous fluid and the modified aqueous-extract oil-tea-cake are mixed and heated, oleic acid is added and ammonium hydroxide is added drop by drop, separation is conducted, after lower layer sediment is grinded and dried, the lower layer sediment and the mixed modified powder are mixed and ball-milled, and then the wax removing agent can be obtained. According to the preparation method for the wax removing agent, the wax removing efficiency of the wax removing agent prepared by the method is high, wax scale can be effectively removed, any corrosion substance is not generated in the using process, non-corrosiveness to metal workpieces is achieved, and the using range of the wax removing agent prepared by the method is widened.

Description

technical field [0001] The invention relates to a preparation method of a wax remover, belonging to the technical field of metal cleaning. Background technique [0002] In recent years, with the continuous improvement of people's living standards and industrial technology, various metal products, electronics, precision industry and other products have been widely used in industrial production and people's daily life, and the market demand is also relatively large; various metal and Metal alloys have excellent physical and chemical properties and surface treatment characteristics, and are widely used. In order to improve their comprehensive performance, surface finish and decorative effect, surface finishing treatment must be carried out. Among them, mechanical polishing with special polishing wax is the first step in surface finishing treatment. Effective surface polishing process; for example, car glazing wax and polishing agent are used to protect, clean and polish the out...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23G1/14
CPCC23G1/14
Inventor 李广薛洋王艳芹
Owner SUZHOU YUANLIAN SCI & TECH PIONEER PARK MANAGEMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com