Antistatic reinforced PP/ABS alloy material and preparation method thereof

An alloy material, antistatic technology, applied in the field of antistatic reinforced PP/ABS alloy material, can solve the problems of high surface resistivity, low shrinkage, reduced surface resistivity, etc., to achieve good mechanical properties, low surface impedance, resistance to The effect of high heat temperature

Inactive Publication Date: 2017-11-14
佛山市东丽塑胶有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The PP / ABS alloy modified by utilizing the advantages of PP and ABS can combine the advantages of both. The product has better rigidity and flexibility and lower shrinkage rate, and effectively reduces the surface resistivity of the product. However, PP and ABS The Vicat softening point of ABS itself is not high, so it is difficult to be used in occasions that require high heat resistance, and it is difficult to meet most application requirements due to the high surface resistivity of the material itself.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] A preparation method of antistatic reinforced PP / ABS alloy material, comprising the following steps:

[0028] S1. Dry PP and ABS separately in advance, wherein, the drying temperature of PP is 80~100°C and drying for 3~5H; the drying temperature of ABS is 85~105°C and drying for 3~5H;

[0029] S2. After the drying process is completed, add 35-55 parts of PP and 15-30 parts of ABS to the high-speed mixer by weight, and weigh 2-5 parts of compatibilizer and coupling agent by weight 0.3~0.5 parts, 0.3~0.5 parts of compound antioxidant, 3~5 parts of compound antistatic agent and 0.3~0.5 parts of lubricant are added to the high-speed mixer, and mixed by the high-speed mixer for 10-20 minutes to obtain a mixed material;

[0030] S3. After mixing evenly, add the mixture into the twin-screw extruder, and at the same time, weigh 15-30 parts of glass fiber by weight and add it to the twin-screw extruder, and melt and blend through the twin-screw extruder Extrusion, wherein the ...

Embodiment 1

[0034] An antistatic enhanced PP / ABS alloy material, including the following raw materials in parts by weight: 40 parts of homopolypropylene (PP-H), 8 parts of copolymerized polypropylene (PP-R), 17.4 parts of ABS, POE-g - 3.8 parts of MAH, 0.3 parts of silane coupling agent, 0.3 parts of compound antioxidant, 5 parts of compound antistatic agent, 0.2 part of lubricant, 25 parts of glass fiber.

[0035] The product performance of this embodiment is tested, and concrete data is as follows:

[0036] test

Embodiment 2

[0038] An antistatic enhanced PP / ABS alloy material, including the following raw materials in parts by weight: 40.5 parts of homopolypropylene (PP-H), 8.1 parts of copolymerized polypropylene (PP-R), 18.6 parts of ABS, POE-g - 2 parts of MAH, 0.3 parts of silane coupling agent, 0.3 parts of compound antioxidant, 5 parts of compound antistatic agent, 0.2 part of lubricant, 25 parts of glass fiber.

[0039] The product performance of this embodiment is tested, and concrete data is as follows:

[0040] test

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an antistatic reinforced PP/ABS alloy material and a preparation method thereof. The antistatic reinforced PP/ABS alloy material comprises the following raw materials in parts by weight: 35-55 parts of PP, 15-30 parts of ABS, 2-5 parts of a compatilizer, 0.3-0.6 part of a coupling agent, 0.3-0.5 part of a compound antioxidant, 3-5 parts of a compound antistatic agent, 0.3-0.5 part of a lubricant and 15-30 parts of alkali-free glass fiber. The antistatic reinforced PP/ABS alloy material has the advantages of high heat-resistance temperature, low shrinking percentage, low surface impedance, good mechanical property, wide application range and the like.

Description

technical field [0001] The invention relates to the technical field of plastic alloy materials, in particular to an antistatic enhanced PP / ABS alloy material. Background technique [0002] PP (polypropylene) is a general-purpose plastic with excellent performance. It has the characteristics of good toughness, moderate strength, and light specific gravity. It is widely used in packaging, electronic appliances, and machinery manufacturing. Heat resistance is difficult to apply to the defect of harsh use environment. Secondly, ABS (acrylonitrile-butadiene-styrene copolymer) is an excellent polymer alloy with the advantages of high strength, adjustable toughness and low shrinkage. The PP / ABS alloy modified by utilizing the advantages of PP and ABS can combine the advantages of both. The product has better rigidity and flexibility and lower shrinkage rate, and effectively reduces the surface resistivity of the product. However, PP and ABS The Vicat softening point of ABS itself...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/14C08L55/02C08L51/06C08K13/04C08K7/14C08K5/17C08K5/134C08K5/526
CPCC08L23/12C08K2201/014C08K2201/017C08L2201/04C08L2205/035C08L2205/08C08L23/14C08L55/02C08L51/06C08K13/04C08K7/14C08K5/17C08K5/1345C08K5/526
Inventor 陈志宇何见曾权伍辉
Owner 佛山市东丽塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap