Corrosion-resisting and waterproof flame-retarding cable material

A flame-retardant cable material and corrosion-resistant technology, which is applied in the direction of circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problem that cable materials cannot take into account high temperature resistance and corrosion resistance at the same time, and achieve a good protective effect

Inactive Publication Date: 2017-11-24
ANHUI HUANENG CABLE GRP
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current cable materials generally cannot take into account both high temperature resistance and corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A corrosion-resistant, waterproof and flame-retardant cable material composed of the following raw materials in parts by weight: 40 parts of chlorinated polyethylene, 20 parts of fluorine rubber, 13 parts of zinc borate, 16 parts of modified polyurethane, 10 parts of calcium carbonate, and 20 parts of carbon black , 8 parts of methyl oleate, 6 parts of benzyl silicone oil, 4 parts of magnesium hydroxide, 1 part of benzotriazole, 2 parts of dibutyltin oxide, 1 part of hexafluoroacetylacetone, 2.2 parts of zinc stearate And 0.2 parts of accelerator.

Embodiment 2

[0014] A corrosion-resistant, waterproof, flame-retardant cable material composed of the following raw materials in parts by weight: 50 parts of chlorinated polyethylene, 30 parts of fluorine rubber, 21 parts of zinc borate, 22 parts of modified polyurethane, 15 parts of calcium carbonate, 24 parts of carbon black , 12 parts of methyl oleate, 9 parts of benzyl silicone oil, 9 parts of magnesium hydroxide, 2 parts of benzotriazole, 5 parts of dibutyltin oxide, 2 parts of hexafluoroacetylacetone, 4.6 parts of zinc stearate And 0.6 parts of accelerator.

Embodiment 3

[0016] A corrosion-resistant, waterproof, flame-retardant cable material composed of the following raw materials in parts by weight: 45 parts of chlorinated polyethylene, 25 parts of fluoro rubber, 17 parts of zinc borate, 19 parts of modified polyurethane, 13 parts of calcium carbonate, 22 parts of carbon black , 10 parts of methyl oleate, 8 parts of benzyl silicone oil, 6 parts of magnesium hydroxide, 1.5 parts of benzotriazole, 4 parts of dibutyltin oxide, 1.5 parts of hexafluoroacetylacetone, 3.5 parts of zinc stearate And 0.4 parts of accelerator.

[0017] The corrosion-resistant and fire-resistant cable material of the present invention has the advantages of corrosion resistance and high temperature resistance, is suitable for complex environments, and has a good protective effect on conductors inside the cable.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion-resisting and waterproof flame-retarding cable material. The corrosion-resisting and waterproof flame-retarding cable material is prepared from the following raw materials in parts by weight: 40 to 50 parts of chlorinated polyethylene, 20 to 30 parts of fluororubber, 13 to 21 parts of zinc borate, 16 to 22 parts of modified polyurethane, 10 to 15 parts of calcium carbonate, 20 to 24 parts of carbon black, 8 to 12 parts of methyl oleate, 6 to 9 parts of phenylmethyl silicone oil, 4 to 9 parts of magnesium hydroxide, 1 to 2 parts of 1H-benzotriazole, 2 to 5 parts of dibutyl tin oxide, 1 to 2 parts of hexafluoroacetylacetone, 2.2 to 4.6 parts of zinc stearate and 0.2 to 0.6 part of an accelerant. The corrosion-resisting and waterproof flame-retarding cable material disclosed by the invention has the advantages of corrosion resistance and high temperature resistance, is suitable for a complicated environment and has a very good protection effect on conductors in cables.

Description

Technical field [0001] The invention relates to the technical field of cables, in particular to a corrosion-resistant, waterproof and flame-retardant cable material. Background technique [0002] With scientific progress and economic development, cables have been used in all aspects. In some high temperature and corrosive environments, to ensure the normal use of cables, corrosion-resistant cable materials are usually used to ensure the safe use of cables. However, the current cable materials generally cannot give consideration to both high temperature resistance and corrosion resistance. Summary of the invention [0003] The purpose of the present invention is to provide a corrosion-resistant, waterproof, flame-retardant cable material to solve the above technical defects. [0004] In order to achieve the above objectives, the present invention provides the following technical solutions: [0005] A corrosion-resistant, waterproof and flame-retardant cable material, which is compose...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L27/12C08L75/04C08L83/04C08K13/02C08K3/38C08K3/26C08K3/04C08K5/098C08K3/22H01B3/44
CPCC08L23/286C08K2003/2224C08K2003/265C08K2003/387C08L2201/02C08L2201/08C08L2203/202C08L2205/035H01B3/441C08L27/12C08L75/04C08L83/04C08K13/02C08K3/38C08K3/26C08K3/04C08K5/098C08K3/22
Inventor 王洁然盛业华宫传播
Owner ANHUI HUANENG CABLE GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com