High-tinting-strength green vulcanized paper for abrasive discs

A kind of tinting strength and green technology, applied in the field of steel paper, can solve the problems of easy fading and fading, and achieve the effect of not easy to absorb moisture and deform, fine surface and good heat resistance

Active Publication Date: 2017-12-01
杭州特种纸业有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Aiming at the problem that the existing steel paper adopts organic dyes which are easy to fade and fade, the purpose of the present invention is to provide a green abrasive steel paper with strong tinting power, which is not

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-tinting-strength green vulcanized paper for abrasive discs

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A green abrasive steel paper with strong coloring power is made of the following components: 100g of cotton fiber, 40g of wood pulp fiber, 4g of inorganic composite pigment, 0.8g of dispersant, 2g of water-soluble chitosan, 2g of insulation enhancer, Heat-resistant enhancer 3g, setting agent 1g.

[0026] Wherein the inorganic composite pigment is made up of glauconite, green serpentine, cobalt green pigment, and the weight ratio of glauconite, green serpentine, cobalt green pigment is 0.8:0.2:0.06, and the weight ratio of glauconite, green serpentine The particle size range is 0.1-1nm, and the glauconite and green serpentine are used after calcining at 500°C for 2 hours. The insulation enhancer is preferably insulating ceramic fiber with a diameter of 1nm, and the heat-resistant enhancer is preferably phenolic with a diameter of 1nm. Fiber, polyphenylsulfoneimide fiber, polyacrylonitrile preoxidized fiber form, and the weight ratio of the three is phenolic fiber: polyph...

Embodiment 2

[0035] A green abrasive steel paper with strong tinting strength, made of the following components: 105g cotton fiber, 47.5g wood pulp fiber, 6g inorganic composite pigment, 0.9g dispersant, 2.5g water-soluble chitosan, insulation enhancer 3g, heat resistance enhancer 4, setting agent 1.5g.

[0036] Wherein the inorganic composite pigment is made up of glauconite, green serpentine, cobalt green pigment, and the weight ratio of glauconite, green serpentine, cobalt green pigment is 0.9:0.275:0.065, and the weight ratio of glauconite, green serpentine The particle size range is 0.1-1nm, and the glauconite and green serpentine are used after calcining at 550°C for 2.5 hours. The insulation enhancer is preferably insulating ceramic fiber with a diameter of 10nm, and the heat-resistant enhancer is preferably phenolic with a diameter of 10nm. Fiber, polyphenylsulfone imide fiber, polyacrylonitrile preoxidized fiber form, and the weight ratio of the three is phenolic fiber: polyphenyl...

Embodiment 3

[0045] A green abrasive steel paper with strong coloring power is made of the following components: 110g of cotton fiber, 55g of wood pulp fiber, 8g of inorganic composite pigment, 1.0g of dispersant, 3g of water-soluble chitosan, 4g of insulation enhancer, Heat-resistant enhancer 5g, setting agent 1.5g.

[0046] Wherein the inorganic composite pigment is made up of glauconite, green serpentine, cobalt green pigment, and the weight ratio of glauconite, green serpentine, cobalt green pigment is 1:0.35:0.07, and the weight ratio of glauconite, green serpentine The particle size range is 0.1-1nm, and the glauconite and green serpentine are used after calcining at 600°C for 3 hours. The insulation enhancer is preferably insulating ceramic fiber with a diameter of 25nm, and the heat resistance enhancer is preferably phenolic with a diameter of 25nm. Fiber, polyphenylsulfone imide fiber, polyacrylonitrile preoxidized fiber form, and the weight ratio of the three is phenolic fiber: p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Particle size rangeaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of vulcanized paper and particularly discloses high-tinting-strength green vulcanized paper for abrasive discs. The high-tinting-strength green vulcanized paper is prepared from, by weight, 100-120 parts of cotton fibers, 40-70 parts of wood pulp cellulose, 4-12 parts of an inorganic composite pigment, 0.8-1.2 parts of a dispersing agent, 2-4 parts of water-soluble chitosan, 2-6 parts of an insulation reinforcing agent, 3-7 parts of a heatproof reinforcing agent and 1-3 parts of a setting agent. The inorganic composite pigment is prepared from glauconite, green serpentine and a cobalt green pigment, a particle size range of glauconite and green serpentine is 0.1-1nm, and glauconite and green serpentine are calcined for 2-3h at 500-600DEG C before use. The green vulcanized paper for the abrasive discs is high in tinting strength, less prone to fading, moisture absorption and deformation, great in heatproof performance, insulating, flame retardant and long in service life, and prepared abrasive discs are high in processing precision due to great surface fineness of the green vulcanized paper.

Description

technical field [0001] The invention belongs to the technical field of steel paper, in particular to a green abrasive steel paper with strong coloring power. Background technique [0002] Steel paper, also known as hardened paper, is a kind of processed paper with high hardness. It is made by expanding and gelling the raw material fiber with zinc chloride solution. It has high wear resistance, corrosion resistance, heat resistance and insulation performance. And mechanical processing performance, the processed products are durable, light and beautiful, and can be made into red, green or gray by adding pigments, which are used for cutting, drilling, grinding and other mechanical processing. However, there are the following problems in the use of steel paper: firstly, organic dyes are added in the preparation of the existing steel paper base paper, and the color fastness is low, which causes the color of the steel paper to fade and fade; secondly, the heat resistance of the st...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H15/10D21H11/12D21H11/00D21H17/68D21H17/24D21H21/18D21H21/14D21H21/08D21H21/28D21H21/34D21H19/10D21H23/32D21H25/06D21H27/00D21F11/00
CPCD21F11/00D21H11/00D21H11/12D21H15/10D21H17/24D21H17/68D21H19/10D21H21/08D21H21/14D21H21/18D21H21/285D21H21/34D21H23/32D21H25/06D21H27/00
Inventor 吴琼华王建业吴安波
Owner 杭州特种纸业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap