Lightweight heat insulation sheet material containing expanded perlite and silica sand and preparation method thereof

A technology of expanded perlite and thermal insulation boards, which is applied in thermal insulation, manufacturing tools, building components, etc., can solve the problems of flammability, and achieve the effects of non-combustible boards, convenient installation and replacement, and simple preparation processes

Inactive Publication Date: 2017-12-08
绵阳梨坪科技有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The current insulation of building walls mainly includes external insulation, internal insulation, self-insulation, and sandwich insulation. This type of insulation usually uses various insulation materials to achieve the purpose. The materials currently used mainly include molded boards and extruded boards. burning problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A light-weight thermal insulation board containing expanded perlite and silica sand. The thermal insulation board is composed of the following components in parts by weight (Kg): expanded perlite 55, talcum powder 2, silica sand 26, water enhancer 0.5, glass glue 35 .

[0020] The above-mentioned preparation method of the lightweight insulation board containing expanded perlite and silica sand comprises the following steps:

[0021] (a) Stir the above-mentioned raw materials evenly according to the weight ratio at normal temperature;

[0022] (b) the mixture in step (a) is put into the mold and is compression-molded into a plate with a steel wire mesh and a half-hole in the middle of the plate with a press, and the perforation rate is 15%;

[0023] (c) Dry the compression molded plate at 180°C.

Embodiment 2

[0025] A light insulation board containing expanded perlite and silica sand, the insulation board is composed of the following components in parts by weight (Kg): expanded perlite 53, talc powder 5, silica sand 24, water enhancer 0.4, glass glue 32 . The above-mentioned preparation method of the insulating board containing perlite and silica sand comprises the following steps:

[0026] (a) Stir the above-mentioned raw materials evenly according to the weight ratio at normal temperature;

[0027] (b) the mixture in step (a) is put into the mold and is compression-molded into a plate with a steel wire mesh and a half-hole in the middle of the plate with a press, and the perforation rate is 12%;

[0028] (c) Dry the compression molded plate at 150°C.

Embodiment 3

[0030] A light-weight thermal insulation board containing expanded perlite and silica sand. The thermal insulation board is composed of the following components in parts by weight (Kg): 58 expanded perlite, 4 talcum powder, 30 silica sand, 0.6 water enhancer, and 37 glass glue .

[0031] The above-mentioned preparation method of the lightweight insulation board containing expanded perlite and silica sand comprises the following steps:

[0032] (a) Stir the above-mentioned raw materials evenly according to the weight ratio at normal temperature;

[0033] (b) the mixture in the step (a) is put into the mould, and the middle part of the plate is provided with a steel wire mesh and a plate with a half hole, and the perforation rate is 18%;

[0034] (c) Dry the compression molded plate at 180°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a lightweight heat insulation sheet material containing expanded perlite and silica sand and a preparation method thereof. The heat insulation sheet material is prepared form the following components in parts by weight: 50 to 60 parts of the expanded perlite, 2 to 5 parts of talcum powder, 20 to 30 parts of the silica sand, 0.2 to 0.7 part of a moisturizing agent and 30 to 40 parts of sodium silicate. The preparation method of the heat insulation sheet material comprises the following steps: (a) uniformly stirring the raw materials at room temperature according to the weight ratio; (b) putting a mixture in step (a) into a mold and carrying out compression molding on the mixture by adopting a pressing machine to prepare a semi-pore sheet material; (c) drying the sheet material formed by the compression molding at 150 DEG C to 180 DEG C. A steel wire net is arranged at the middle part of the heat insulation sheet material. The perforation percentage of the heat insulation sheet material is 10 percent to 18 percent. According to the sheet material disclosed by the invention, a preparation process is simple and the sheet material is incombustible, has heat insulation and fireproof effects and is convenient to mount and replace; the sheet material can be suitable for an external wall and an internal wall of a common building and is also suitable for heat insulation and fire prevention of high-rise buildings.

Description

technical field [0001] The invention relates to a fire-proof, heat-preserving, environment-friendly and energy-saving material and a preparation method thereof, in particular to a heat-preservation board containing expanded perlite and silica sand and a preparation method thereof. Background technique [0002] Adopting good fireproofing and thermal insulation technology and materials in construction and industry can often get twice the result with half the effort. The use of good heat insulation measures and materials can significantly reduce production energy consumption and costs, improve the environment, and at the same time have better economic benefits. The current insulation of building walls mainly includes external insulation, internal insulation, self-insulation, and sandwich insulation. This type of insulation usually uses various insulation materials to achieve the purpose. The materials currently used mainly include molded boards and extruded boards. burning pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26E04B1/80E04B1/94B28B1/50B28B23/02C04B111/28C04B111/40
CPCC04B28/26B28B1/50B28B23/02C04B2111/00017C04B2111/28C04B2111/40E04B1/80E04B1/942C04B14/185C04B14/042C04B14/06C04B24/42
Inventor 朱德康
Owner 绵阳梨坪科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products