Multifunctional compound cellulose fiber and preparation method thereof

A technology of composite cellulose and cellulose A, which is applied in the direction of artificial filaments made of cellulose derivatives, fiber chemical characteristics, rayon manufacturing, etc. To meet the needs of skin care functions and other issues, achieve the effect of excellent physical and mechanical properties, simple and reliable production process, and low production cost

Active Publication Date: 2017-12-22
山东欣悦健康科技有限公司 +1
View PDF9 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the hygroscopic fibers, antibacterial fibers and skin care fibers disclosed above all have specific functions, they have a single function and cannot meet people's needs for fiber moisture absorption, antibacterial and skin care functions at the same time.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional compound cellulose fiber and preparation method thereof
  • Multifunctional compound cellulose fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] High moisture absorption, antibacterial, skin care multifunctional cellulose fiber with a specification of 1.33dtex×38mm and a preparation method thereof, comprising the following steps:

[0048] (1) Preparation of multifunctional composite additive slurry:

[0049] ① Crush and grind Centella asiatica to obtain powder; weigh Centella asiatica powder and ethanol to meet the mass ratio of 1:10, stir thoroughly, then carry out reflux extraction, and then distill the reflux extraction product processing to obtain Centella asiatica essential oil; the active ingredients in Centella asiatica can be fully extracted by reflux extraction;

[0050] ②Weigh the Centella asiatica essential oil and vitamins respectively to meet the mass ratio of 1:9, and then mix them evenly so that the surface of the vitamins is coated with a layer of Centella asiatica essential oil to prepare oily vitamin mixed slurry: Centella asiatica essential oil in Protect protein and vitamin in water-based sy...

Embodiment 2

[0065] High moisture absorption, antibacterial, skin care multifunctional cellulose fiber with a specification of 1.33dtex×38mm and a preparation method thereof, comprising the following steps:

[0066] (1) Preparation of multifunctional composite additive slurry:

[0067] ① Crush and grind Centella asiatica to obtain powder; weigh Centella asiatica powder and ethanol to meet the mass ratio of 1:10, stir thoroughly, then carry out reflux extraction, and then distill the reflux extraction product , to obtain Centella asiatica essential oil; the active ingredients in Centella asiatica can be fully extracted by reflux extraction;

[0068] ② Weigh Centella Asiatica essential oil and vitamins respectively to meet the mass ratio of 1:9, and then mix them evenly so that the surface of vitamins is coated with Centella Asiatica essential oil to prepare oily vitamin mixed slurry; Centella Asiatica essential oil is mixed with Protect protein and vitamin in water-based system;

[0069] ...

Embodiment 3

[0083] High moisture absorption, antibacterial, skin care multifunctional cellulose fiber with a specification of 1.33dtex×38mm and a preparation method thereof, comprising the following steps:

[0084] (1) Preparation of multifunctional composite additive slurry:

[0085] ① Crush and grind Centella asiatica to obtain powder; weigh Centella asiatica powder and ethanol to meet the mass ratio of 1:10, stir thoroughly, then carry out reflux extraction, and then distill the reflux extraction product , to obtain Centella asiatica essential oil; the active ingredients in Centella asiatica can be fully extracted by reflux extraction;

[0086] ② Weigh Centella Asiatica essential oil and vitamins respectively to meet the mass ratio of 1:9, and then mix them evenly so that the surface of vitamins is coated with Centella Asiatica essential oil to prepare oily vitamin mixed slurry; Centella Asiatica essential oil is mixed with Protect protein and vitamin in water-based system;

[0087] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
quality scoreaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional compound cellulose fiber and a preparation method thereof. By adoption of an advanced microcapsule preparation technique and modification of a cellulose fiber solution preparation process, a cellulose fiber is modified through polyvinyl alcohol, herba centellae, proteins and vitamins to obtain the multifunctional compound cellulose fiber by means of a cellulose fiber wet spinning process. The multifunctional compound cellulose fiber prepared according to the method is capable of meeting people's demands on moisture absorption, bacteria resistance, skin caring and the like of fibers, and a product is excellent in physical and mechanical performance and stable functionally and has a promising development prospect.

Description

technical field [0001] The invention belongs to the field of functional composite fiber materials, and in particular relates to a multifunctional composite cellulose fiber and a preparation method thereof. Background technique [0002] Due to the excellent performance of cellulose fibers and their products, they have been widely used. Therefore, vigorously developing new varieties of cellulose fibers with high performance and differentiation is an important direction for the development of cellulose fibers. After years of development, functional composite fibers and Its textiles have achieved certain results. [0003] In the existing technology, a series of high-performance and differentiated functional composite fibers have been developed, such as a high-strength moisture-absorbing fiber disclosed in the patent document CN201420080990.X. Through the special structure between fiber monofilaments, the fiber has excellent Excellent hygroscopic performance, long life of hygros...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/28D01F1/10
CPCD01F1/10D01F1/103D01F2/28
Inventor 刘曰兴于湖生李付杰孙梦尧莫振恩伍丽丽
Owner 山东欣悦健康科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com