Weather-resistant natural composite material UV (Ultraviolet) large surface plate and preparation method thereof

A composite material and large panel technology, which is applied in the field of weather-resistant natural composite UV large panels and its preparation, can solve the problems of high price and poor quality of integrated wall panels, and achieve long-term decorative aesthetics, long service life, and improved brightness. Effect

Inactive Publication Date: 2018-01-05
宣恩九发科技有限公司
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The problem to be solved by the present invention is to provide an environmentally friendly weather-resistant natural composite UV large panel and its preparation method in order to make up for the high price and poor quality of the existing integrated wall panels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1: A large weather-resistant natural composite material UV panel, the raw materials are composed of the following proportions in parts by weight: 100 parts of heavy calcium carbonate, 50 parts of recycled abrasives, 37.5 parts of SG-8 polyvinyl chloride resin, CS -108 pipe PVC high-efficiency rare earth composite stabilizer 3 parts, ACE PVC processing aid 2 parts, CPE chlorinated polyethylene 1.5 parts, PE WAX PE wax 0.8 parts, 1840 type stearic acid 0.5 parts;

[0022] The preparation method comprises the following steps:

[0023] a. Mixing of raw materials: Weigh the raw materials accurately according to the proportion, put them into the high-powder machine for temperature control and stirring, the temperature is controlled at 120°C, and the stirring time is 30 minutes; then enter the cold mixing equipment, and the temperature is kept at about 40°C;

[0024] b. Plasticization: Put the mixed raw materials into the injection molding machine for plasticization...

Embodiment 2

[0029] Embodiment 2: A large weather-resistant natural composite material UV panel, the raw material components are composed of the following proportions in parts by weight: 100 parts of heavy calcium carbonate, 50 parts of recycled abrasives, 37.5 parts of SG-8 polyvinyl chloride resin, CS -108 pipe PVC high-efficiency rare earth composite stabilizer 3 parts, ACE PVC processing aid 2 parts, CPE chlorinated polyethylene 1.5 parts, PE WAX PE wax 0.8 parts, 1840 type stearic acid 0.5 parts;

[0030] The preparation method comprises the following steps:

[0031] a. Mixing of raw materials: Weigh the raw materials accurately according to the ratio, put them into the high-powder machine for temperature control and stirring, the temperature is controlled at 120°C, and the stirring time is 30 minutes;

[0032] b. Plasticization: Put the mixed raw materials into the injection molding machine for plasticization. The plasticization temperature of the raw materials is controlled at 610°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a weather-resistant natural composite material UV (Ultraviolet) large surface plate which is characterized by consisting of the following raw material components in parts by weight: 100 parts of coarse whiting, 50 parts of a recycled self-wearing material, 37.5 parts of a SG-8 polyvinyl chloride resin, 3 parts of a CS-108 tube PVC (Polyvinyl Chloride) efficient rare-earthcomposite stabilizer, 2 parts of ACE PVC processing aids, 1.5 parts of CPE (Chlorinated Polyethylene), 0.8 part of PE WAX and 0.5 part of 1840 type stearic acid. The plate is not only good in mold andwater resistance, but also the elasticity and the plasticity of a wall are improved, a uniform and attractive construction effect is achieved, and the brightness is remarkably improved. As the raw materials are mostly wastes, the price is low, the purpose of waste recycling is achieved, the environment is protected, and remarkable economic benefits are made.

Description

technical field [0001] The invention relates to a weather-resistant natural composite material UV large panel and a preparation method thereof. Background technique [0002] At present, expensive organic coating materials such as polyvinyl alcohol, titanium dioxide, and lithopone are commonly used in interior wall coatings for general buildings in China, which are easy to fall off, are not washable and moisture-proof, and are likely to cause secondary pollution. In addition, the mortar of lime powder and lime paste has low viscosity, low hardness and wall crack resistance, high cement consumption, and poor moisture-proof and air-permeable properties. Ceramic tiles are widely favored by developers and owners for their solemn texture, durable quality and diverse colors. However, the disadvantages of this material are also obvious: one is expensive, the other is complicated construction, the third is difficult to combine with thermal insulation materials, the fourth is low saf...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L23/28C08L23/06C08K13/02C08K3/26C08K5/09
Inventor 卓发亮李羚境
Owner 宣恩九发科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com