A preparation method of a flexible copper-clad liquid crystal polymer substrate

A liquid crystal polymer and flexible technology, which is applied in the field of preparation of flexible copper-clad liquid crystal polymer substrates, can solve the problem of difficult thinning of LCP films, high production cost and low production capacity of flexible copper-clad liquid crystal polymer substrates and other problems, to achieve the effect of strength improvement, cost reduction, and simple production steps

Active Publication Date: 2021-01-26
CHENGDU DO ITC NEW MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of high production cost of the above-mentioned flexible copper-clad liquid crystal polymer substrate, low production capacity and difficulty in thinning the LCP film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of a flexible copper-clad liquid crystal polymer substrate
  • A preparation method of a flexible copper-clad liquid crystal polymer substrate
  • A preparation method of a flexible copper-clad liquid crystal polymer substrate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with the accompanying drawings and embodiments. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0025] Such as figure 1 with 2 Shown, a kind of preparation method of flexible copper-clad liquid crystal polymer substrate is characterized in that, described method comprises the following steps:

[0026] Step 1: Add the LCP material into the solvent, and then perform sufficient sanding to obtain the LCP glue;

[0027] Step 2: apply the LCP glue obtained in step 1 on a layer of copper foil 2, and then dry it in a tunnel oven to make the LCP glue into an LCP glue layer 1;

[0028] Step 3: Pressing the copper foil 2 with the LCP adhesive layer 1 obtained in step 2 and another layer of copper foi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a flexible copper-clad liquid crystal polymer substrate. First, a layer of LCP glue is coated on a layer of copper foil, and then dried in a tunnel oven, and then the obtained copper foil with an LCP glue layer is The foil is laminated with another layer of copper foil to obtain a substrate, which is then post-cured in a programmed oven to obtain a flexible copper-clad liquid crystal polymer substrate. Through this method, the thickness of the LCP adhesive layer can be easily made ultra-thin, which is conducive to the development of ultra-thin electronic products in the future, and the low-temperature press is used to replace the high-temperature press during lamination, which greatly reduces the cost and improves the production capacity. It has also been improved, and the post-curing step is performed on the laminated substrate to effectively eliminate internal stress, improve the bonding strength and cohesive strength, and improve the strength of the entire flexible copper-clad liquid crystal polymer substrate.

Description

technical field [0001] The invention belongs to the field of copper-clad foil boards, and in particular relates to a preparation method of a flexible copper-clad liquid crystal polymer substrate. Background technique [0002] Liquid crystal polymer, also called liquid crystal polymer, is Liquid Crystal Polymer in English, abbreviated as LCP, is a new type of polymer material, it will generally become liquid crystal in a certain heating state, so it is named after it, liquid crystal Polymer refers to a polymer compound that can exist in a liquid crystal phase under certain conditions, and its characteristic is that the molecule has a relatively high molecular weight and has an ordered orientation. [0003] The current preparation method of flexible copper-clad liquid crystal polymer substrate is: directly purchase LCP film, and then produce it by high-temperature pressing method. However, in this method, LCP film is mostly extruded into film, which is difficult to prepare. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B37/12B32B37/10B32B38/00B32B38/16
CPCB32B37/10B32B37/1284B32B38/00B32B38/164B32B2037/1253B32B2038/0076
Inventor 侯曦月杨刚
Owner CHENGDU DO ITC NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com