Acrylamide copolymer as well as preparation method and application thereof

An acrylamide copolymer and acrylamide copolymerization technology are applied in chemical instruments and methods, drilling compositions, etc., and can solve the problems of difficult synthesis of macromonomers, complex synthesis steps, unfavorable polymer migration and movement, etc. Good water solubility and low temperature stability, increasing hydration radius and increasing viscosity

Active Publication Date: 2018-04-03
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this patent, macromonomers are prepared by copolymerization with acrylamide and 2-acrylamide-2-methyl-1-propanesulfonic acid, which has good thickening performance in tertiary oil recovery of high-temperature and high-salt reservoirs, but The synthesis of macromonomers is difficult, the synthesis steps are complicated, and the thickening is obvious at lower temperatures, which is not conducive to the migration of polymers in the formation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylamide copolymer as well as preparation method and application thereof
  • Acrylamide copolymer as well as preparation method and application thereof
  • Acrylamide copolymer as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0028] At the same time, the present invention also provides a method for preparing an acrylamide copolymer, the preparation method comprising the following steps: under the solution polymerization reaction conditions of olefins, in the presence of an initiator, the monomer mixture is polymerized in water , the monomer mixture contains monomer D having the structure shown in formula IV, monomer E having the structure shown in formula V and monomer F having the structure shown in formula VI, and the monomer D, the monomer The weight ratio of body E and said monomer F is 1:(0.01~0.65):(0.01~0.65),

[0029]

[0030] In Formula IV, R 1 ' is any one of H and C1-C4 alkyl; in formula VI, R 2 ', R 3 'are independently selected from any one of H and C1~C12 alkyl groups; R 4 ' is any one selected from H, C1-C12 alkyl groups, and C6-C12 alkyl groups. The C1-C4 alkyl group, the C1-C12 alkyl group, and the C6-C12 aryl group are the same as those described above, and will not be repe...

Embodiment 1

[0061] It is used to illustrate the acrylamide copolymer of the present invention and its preparation method.

[0062] The structure of the adopted α-methylene-γ-lactonate (commercially purchased from Aladdin Reagent Company, the same below) is as follows:

[0063]

[0064] The preparation method of acrylamide copolymer comprises:

[0065] At room temperature, under agitation, add 200g of acrylamide (AM), 25g of maleic acid and 25g of the above-mentioned α-methylene-γ-lactonate and 1000g of deionized water in the beaker; after the raw materials are dissolved, Add sodium hydroxide to the aqueous solution to adjust the pH of the aqueous solution to 7.5; then feed nitrogen into the aqueous solution to remove oxygen for 30min and seal the beaker to form an inert atmosphere; then add 0.01g of ammonium persulfate and 0.01g of sodium bisulfite to the aqueous solution as The oxidation-reduction initiation system was then reacted at normal pressure and constant temperature at 15° C...

Embodiment 2

[0068] It is used to illustrate the acrylamide copolymer of the present invention and its preparation method.

[0069] The α-methylene-γ-lactonate used: the same as in Example 1.

[0070] The preparation method of acrylamide copolymer comprises:

[0071] Add 225g of acrylamide (AM), 50g of maleic acid and 12.5g of the above-mentioned α-methylene-γ-lactonate and 1000g of deionized water to the beaker under room temperature and stirring; , adding sodium hydroxide to the aqueous solution to adjust the pH of the aqueous solution to 6.5; then passing nitrogen into the aqueous solution to remove oxygen for 30 minutes and then sealing the beaker to form an inert atmosphere; then adding 0.02 g of the initiator 2,2'-azobis( 2-methylpropionamidine) hydrochloride (AIBA), and then reacted at normal pressure and 50° C. constant temperature (water bath temperature control) for 4 hours to obtain a colloidal polymer solution product. The colloidal polymer solution product is granulated into 4...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of oil field chemicals and discloses an acrylamide copolymer as well as a preparation method and an application thereof. The acrylamide copolymer contains a structure unit A shown in the formula I, a structure unit B shown in the formula II and a structure unit C shown in the formula III; on the basis of the total weight of the acrylamide copolymer, the content of the structure unit A is 43.5wt%-98wt%, the content of the structure unit B is 0.6wt%-39wt%, and the content of the structure unit C is 0.6wt%-39wt%. The acrylamide copolymer has good water solubility and a thermothickening function and is applicable to three-time oil recovery of a high-temperature and high-salinity reservoir as a thermothickening agent.

Description

technical field [0001] The invention relates to the field of oilfield chemicals, in particular to an acrylamide copolymer and its preparation method and application. Background technique [0002] Polymer flooding technology is an important enhanced oil recovery technology. Its basic principle is to add water-soluble polymers to the injection water to increase the viscosity of the aqueous solution, reduce the water / oil mobility ratio, expand the swept volume, and increase the Sweep efficiency, reducing oil saturation in the swept zone, thereby enhancing oil recovery. Practice has proved that the use of polymer flooding can greatly improve oil recovery, resulting in huge economic and social benefits. For many years, the polymer used in polymer flooding is mainly artificially synthesized partially hydrolyzed polyacrylamide. The limitations of ordinary partially hydrolyzed polyacrylamide are low temperature and salt resistance, high hydrolysis speed under high temperature and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/56C08F222/02C08F220/18C08F220/16C09K8/588
CPCC08F220/56C09K8/588C08F222/02C08F220/18
Inventor 张文龙伊卓方昭胡晓娜刘希杜超祝纶宇
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com