Inorganic insulation electromagnetic line and fabrication method thereof

A technology of inorganic insulation and electromagnetic wire, applied in the field of electromagnetic wire, which can solve the problem of inability to use

Active Publication Date: 2018-04-20
安徽天大铜业有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the electromagnetic wire uses organic matter as the insulating layer, and cannot be used in a high temperature environment for a long time (≥500°C, more than 1000h)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The invention relates to an inorganic insulated electromagnetic wire. After the alloy copper wire is treated in a treatment agent, the surface of the alloy copper wire is covered with an insulating layer by means of sol deposition.

[0022] The preparation method of described treating agent comprises the following steps:

[0023] Mix 3 parts by weight of tannic acid, 2 parts by weight of zinc dibutyldithiocarbamate, 14 parts by weight of sodium phosphate, 7 parts by weight of zinc nitrate, and 1 part by weight of ethoxylated alkylphenol ammonium sulfate , adding to deionized water 50 times the weight of the mixture, stirring evenly, adding 16 parts by weight of phosphoric acid dropwise, adjusting the pH to 4, and stirring at 50° C. for 10-14 minutes to obtain the product.

[0024] The concentration of said phosphoric acid is 1.5 mol / l.

[0025] Described sol is made up of the raw material of following weight part:

[0026] Ethyl Tetrasilicate 40, Sucrose Acetate Isobu...

Embodiment 2

[0037] The invention relates to an inorganic insulated electromagnetic wire. After the alloy copper wire is treated in a treatment agent, the surface of the alloy copper wire is covered with an insulating layer by means of sol deposition.

[0038] The preparation method of described treating agent comprises the following steps:

[0039] Mix 2 parts by weight of tannic acid, 1 part by weight of zinc dibutyldithiocarbamate, 10 parts by weight of sodium phosphate, 5 parts by weight of zinc nitrate, and 0.7 parts by weight of ethoxylated alkylphenol ammonium sulfate , added to deionized water 40 times the weight of the mixture, stirred evenly, 10 parts by weight of phosphoric acid was added dropwise, the pH was adjusted to 3, and the mixture was incubated and stirred for 10 minutes at 40°C to obtain the product.

[0040] The concentration of said phosphoric acid is 1mol / l.

[0041] Described sol is made up of the raw material of following weight part:

[0042] Orthoethyl silicat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
breakdown voltageaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inorganic insulation electromagnetic. After an alloy copper wire is processed in a processing agent, and an insulation layer covers a surface of the alloy copper wire afteremploying a sol deposition mode. Tetraethoxysilane and zinc diricinoleate are mixed and dispersed in an alcohol aqueous solution, alloy after phosphating is added into the mixture, ammonia water is used as a hydrolysis promoter, a layer of insulation sol is formed on a surface of the alloy, and the thermal resistant stability of the sol is further improved by the zinc diricinoleate.

Description

technical field [0001] The invention belongs to the field of electromagnetic wires, and in particular relates to an inorganic insulated electromagnetic wire and a preparation method thereof. Background technique [0002] Magnet wire is an insulated wire used to manufacture coils or windings in electrical products. Also known as winding wire, magnet wire must meet a variety of usage and manufacturing process requirements. The former includes its shape, specifications, short-term and long-term work at high temperature, and strong vibration and high-speed centrifugal force in some occasions, corona and breakdown resistance under high voltage, and chemical resistance under special atmosphere. Corrosion, etc., the latter includes the requirements of stretching, bending and abrasion during winding and embedding, as well as swelling and erosion during dipping and drying; [0003] Magnet wire is an indispensable electrical product in the electrical industry. The motor will generat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B13/06C23C22/13C23C22/78
Inventor 何云龙雍金贵陈东李长江李定勇
Owner 安徽天大铜业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap