A production process of a metal oxide-loaded borosilicate phenolic resin-based activated carbon tail gas desulfurizer for the production of hydrogen fluoride

A phenolic resin and production process technology, applied in gas treatment, petroleum industry, filter regeneration, etc., can solve the problems of poor desulfurizer effect, inability to recycle and reuse, and achieve the effect of high desulfurization efficiency and large number of holes

Active Publication Date: 2020-01-21
QUZHOU NANGAOFENG CHEM CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the problems in the prior art that the effect of the desulfurizing agent is poor, the holes in the desulfurizing agent are less and cannot be recycled and reused, and provide a kind of desulfurizing agent that can have good desulfurization efficiency, a large number of holes in the desulfurizing agent, and can be recycled and used. A production process for metal oxide-loaded borosilicate phenolic resin-based activated carbon tail gas desulfurizer for hydrogen fluoride production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A kind of production process of metal oxide load-containing borosilicate phenolic resin-based activated carbon tail gas desulfurizer for hydrogen fluoride production, described production process comprises the following steps:

[0027] (a) Take 100 parts by mass of phenol and 90 parts of 37% formaldehyde solution into the reactor, slowly add 3 parts of ammonia water under stirring, heat and reflux for 5 hours, and let stand to separate and remove water Layer, then decompression distillation removes residual moisture, obtains phenolic resin prepolymer;

[0028] (b) Dissolving the obtained phenolic resin prepolymer in absolute ethanol to prepare a 15% phenolic resin prepolymer ethanol solution;

[0029] (c) Take 200 parts by mass of the 15% phenolic resin prepolymer ethanol solution in step (b), add 10 parts of phenyltriacyloxysilane, 3 parts of terminal hydroxyl groups with a relative molecular weight of 800 After the silicone oil and 2 parts of boric acid are evenly st...

Embodiment 2

[0038] A kind of production process of metal oxide load-containing borosilicate phenolic resin-based activated carbon tail gas desulfurizer for hydrogen fluoride production, described production process comprises the following steps:

[0039](a) Take 100 parts by mass of phenol and 100 parts of 37% formaldehyde solution into the reactor, slowly add 8 parts of ammonia water under stirring, heat and reflux for 10 hours, and let stand to separate and remove water Layer, then decompression distillation removes residual moisture, obtains phenolic resin prepolymer;

[0040] (b) Dissolving the obtained phenolic resin prepolymer in absolute ethanol to prepare a 15% phenolic resin prepolymer ethanol solution;

[0041] (c) Take 200 parts of 15% phenolic resin prepolymer ethanol solution in step (b) in parts by mass, add 15 parts of phenyltriacyloxysilane, 8 parts of terminal hydroxyl groups with a relative molecular weight of 2000 After the silicone oil and 6 parts of boric acid are ev...

Embodiment 3

[0050] A kind of production process of metal oxide load-containing borosilicate phenolic resin-based activated carbon tail gas desulfurizer for hydrogen fluoride production, described production process comprises the following steps:

[0051] (a) Take 100 parts by mass of phenol and 95 parts of 37% formaldehyde solution into the reactor, slowly add 4 parts of ammonia water under stirring, heat and reflux for 8 hours, and let stand to separate and remove water Layer, then decompression distillation removes residual moisture, obtains phenolic resin prepolymer;

[0052] (b) Dissolving the obtained phenolic resin prepolymer in absolute ethanol to prepare a 15% phenolic resin prepolymer ethanol solution;

[0053] (c) Take 200 parts by mass of the 15% phenolic resin prepolymer ethanol solution in step (b), add 12 parts of phenyltriacyloxysilane, 5 parts of terminal hydroxyl groups with a relative molecular weight of 1000 After the silicone oil and 4 parts of boric acid are evenly s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production process of a metal oxide supported boron-silicon-containing phenolic resin-based active carbon tail gas desulfurizer for producing hydrogen fluoride. The production process comprises the following steps: firstly introducing boron and silicon atoms into a phenolic resin framework for effectively improving the heat resistance and oxidation resistance of the phenolic resin, then carrying out carbonization to obtain boron-silicon-containing phenolic resin carbon, and then activating the boron-silicon-containing phenolic resin carbon to finally obtain the metaloxide supported boron-silicon-containing phenolic resin-based active carbon tail gas desulfurizer. The production process provided by the invention has the following beneficial effects that (1) the desulfurization efficiency is high; (2) the number of holes in the desulfurizer is large; and (3) the desulfurizer can be recycled and reused.

Description

technical field [0001] The invention relates to a production process of a desulfurizing agent, in particular to a production process of a metal oxide-loaded borosilicate phenolic resin-based activated carbon tail gas desulfurizing agent used for hydrogen fluoride production. Background technique [0002] There are many types of odorous pollutants produced in the hydrogen fluoride production process, such as sulfides, nitrides, fluorides, and various organic solvents. At present, China's emission standard for odor pollutants (GB14554-93) defines 8 types of odorous substances, five of which are sulfur-containing compounds, so sulfur-containing compounds are the main target pollutants for odor control. Sulfur-containing compounds are toxic and corrosive substances, which not only cause direct harm to personal safety, but also cause corrosion of devices, equipment and pipelines, and poison and deactivate catalysts, which in turn leads to increased processing costs and affects th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01D53/48B01D53/81B01D53/96B01D53/02B01J20/20B01J20/04B01J20/06B01J20/30B01J20/34
CPCB01D53/02B01D53/48B01D53/81B01D53/96B01D2251/302B01D2251/402B01D2251/602B01D2253/102B01D2257/302B01J20/041B01J20/06B01J20/20B01J20/3078B01J20/3085B01J20/3483
Inventor 龙绍庭
Owner QUZHOU NANGAOFENG CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products