A kind of antibacterial cellulose/polypropylene composite material and its preparation method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composite material and cellulose technology, applied in the field of cellulose/polypropylene composite material and preparation, can solve the problem of unsatisfactory antibacterial effect, and achieve the effects of inhibiting breeding, improving mechanical properties and improving antibacterial performance.
Active Publication Date: 2020-06-05
NORTHEAST FORESTRY UNIVERSITY
View PDF5 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] The present invention aims to solve the problem that the existing bacteriostatic agent added to the wood-plastic composite material has an unsatisfactory antibacterial effect, and provides a bacteriostatic cellulose / polypropylene composite material and its preparation method
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment approach 1
[0039]Specific Embodiment 1: The bacteriostatic cellulose / polypropylene composite material in this embodiment includes 10.00 to 74.00 parts by weight of cellulose, 11.00 to 87.00 parts of polypropylene resin, 0.50 to 5.00 parts of bacteriostatic agent, 2.00 parts by weight ~7.00 parts of compatibilizer, 0.10~2.00 parts of coupling agent, 0.10~2.00 parts of antioxidant, 0.10~2.00 parts of dispersant and 0.50~3.00 parts of porous media material; the antibacterial agent includes inorganic Bacteriostatic agent and organic bacteriostatic agent; Wherein the inorganic bacteriostatic agent is zinc oxide, nano-silver, nano-copper salt, silicon dioxide, anatase titanium dioxide or a mixture of several, the organic bacteriostatic The agent is one of 3-amino-1,2,4-triazole, 4-amino-1,2,4-triazole, 3,5-diamino-1,2,4-triazole or a mixture of several.
specific Embodiment approach 2
[0040] Embodiment 2: This embodiment is different from Embodiment 1 in that: the cellulose is one or a mixture of microcrystalline cellulose, cellulose whiskers, and nanocellulose. Others are the same as in the first embodiment.
specific Embodiment approach 3
[0041] Embodiment 3: This embodiment is different from Embodiment 1 or Embodiment 2 in that: the polypropylene resin is random copolymerized polypropylene resin. Others are the same as in the first or second embodiment.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
bending strength
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a bacteriostatic type cellulose / polypropylene composite material and a preparation method, relates to a cellulose / polypropylene composite material and a preparation method, andaims to solve the problem that the bacteriostatic effect is not ideal as an existing bacteriostatic agent is added into a wood-plastic composite material. The composite material is prepared from cellulose, polypropylene resin, a bacteriostatic agent, a compatilizer, a coupling agent, an antioxidant, a dispersant and a multihole dielectric material. The method comprises the following steps: I, weighing the materials; II, adding the coupling agent into an ethanol solution to obtain a hydrolyzed coupling agent, adding the bacteriostatic agent into the hydrolyzed coupling agent for stirring and drying, so as to obtain a bacteriostatic agent compound, adding the bacteriostatic agent compound, polypropylene resin A, the antioxidant and the dispersant into a double-screw extruder, and performinggranulation and drying, so as to obtain bacteriostatic master batch; III, adding the bacteriostatic master batch, the cellulose, the polypropylene resin B, the compatilizer and the multihole dielectric material into the double-screw extruder, performing granulation and drying to obtain composite granules, and performing injection molding to obtain the bacteriostatic type cellulose / polypropylene composite material. The bacteriostatic type cellulose / polypropylene composite material is applied to the field of wood-plastic composite materials.
Description
technical field [0001] The invention relates to a cellulose / polypropylene composite material and a preparation method. Background technique [0002] With the improvement of people's safety awareness, there is a high demand for antibacterial in the use of furniture, food packaging, daily necessities, etc. Therefore, the design, production and application of antibacterial materials have attracted much attention. Composite materials based on commonly used resins such as thermosetting resins (unsaturated polyester, epoxy resin, aminoplast, etc.), thermoplastic resins (polyethylene, polypropylene, polyvinyl chloride, etc.) are the most widely used. Among them, polypropylene (Poyropylene, PP) is cheap, excellent in performance, good in stability and easy to process and shape. However, PP itself does not have antibacterial properties. The composite material based on polypropylene is affected by the environment and easily corroded by microorganisms after long-term use. This not onl...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.