Sintered water-permeable brick which is not blocked easily and preparation method of sintered water-permeable brick

A permeable brick, a difficult technology, applied in clay products, other household appliances, applications, etc., can solve the problems of many production processes, low limit load, large volume of ball milling equipment, etc., to shorten production time, prolong service life, water permeability excellent effect

Inactive Publication Date: 2018-06-22
KEDA INDUSTRIAL GROUP CO LTD
View PDF2 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And the ultimate load of the binder is low, generally around 64.8N, resulting in low strength of the green body after molding
[0007] In addition, the existing technical process of permeable bricks is relatively complicated, with many production processes, long time consumption and high cost. The process flow chart is as follows figure 1 shown
see figure 1 , the binder of the existing permeable bricks requires a separate ball mill, but the ball milling process takes a long time to operate, the ball milling equipment is bulky and occupies a large area, which will greatly increase the production cost of the permeable bricks
[0008] Moreover, the existing permeable bricks are very easy to block after being used for a certain period of time. This is because the pores of the permeable bricks are small and extremely irregular. Particles or fibrous substances are not easy to pass through the pores of permeable bricks, thereby blocking their pores

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sintered water-permeable brick which is not blocked easily and preparation method of sintered water-permeable brick
  • Sintered water-permeable brick which is not blocked easily and preparation method of sintered water-permeable brick
  • Sintered water-permeable brick which is not blocked easily and preparation method of sintered water-permeable brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach

[0071] As a preferred embodiment of the present invention, the main raw materials of the primer in parts by mass are as follows:

[0072]

[0073] The bonding base material is one or more of bentonite and clay;

[0074] The liquid glue is one or more of silica sol solution, polyacrylamide solution, guar gum solution;

[0075] The main raw materials of the fabric in parts by mass are as follows:

[0076]

[0077] The bonding base material is one or more of bentonite and clay;

[0078] The liquid gel is one or more of silica sol solution, polyacrylamide solution, and guar gum solution.

[0079] As a better embodiment of the present invention, the binder is also added to the frit, that is,

[0080] The main raw materials of the base material in parts by mass are as follows:

[0081]

[0082] The bonding base material is one or more of bentonite and clay;

[0083] The liquid glue is one or more of silica sol solution, polyacrylamide solution, guar gum solution;

[0...

Embodiment 1

[0124] (1) Formula: including lining and base material, wherein, the main raw material of described base material is as follows in parts by mass:

[0125]

[0126]

[0127] The bonding base material is bentonite, the liquid glue is a silica sol solution, and the glaze is raw glaze;

[0128] The main raw materials of the fabric in parts by mass are as follows:

[0129]

[0130] The bonding base material is bentonite, the liquid glue is a silica sol solution, and the glaze is raw glaze;

[0131] (2) Preparation method

[0132] (1) Crushing the aggregate;

[0133] (2) Sieving the crushed aggregate to obtain particles in different particle size ranges;

[0134] (3) Add bonding base material, liquid glue and glaze to the sieved aggregate particles, and stir evenly to obtain a primer; add the sieved aggregate particles to bonding base material, liquid glue, Glaze and pigment, and stir evenly to get fabric;

[0135] (4) The fabric and base material after stirring are di...

Embodiment 2

[0138] (1) Formula: including lining and base material, wherein, the main raw material of described base material is as follows in parts by mass:

[0139]

[0140] The bonding base material is kaolin, the liquid glue is sodium polyacrylate, and the glaze is frit glaze;

[0141] The main raw materials of the fabric in parts by mass are as follows:

[0142]

[0143]

[0144] The bonding base material is kaolin, the liquid glue is sodium polyacrylate, and the glaze is frit glaze;

[0145] (2) Preparation method

[0146] (1) Crushing the aggregate;

[0147] (2) Send the crushed aggregate into the ball mill for dry grinding. There is no ball stone in the ball mill, and the aggregate itself collides and rubs against each other;

[0148] (3) sieving the aggregate after ball milling to obtain particles in different particle size ranges;

[0149] (4) Add bonding base material, liquid glue and glaze to the sieved aggregate particles, and stir evenly to obtain a base materia...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sintered water-permeable brick which is not blocked easily. The brick comprises a surface material and a bottom material, wherein the bottom material comprises the main raw materials of: in parts by mass, 80-100 parts of aggregate, 3-12 parts of a bonding base material, 3-12 parts of liquid glue and 0.1-5 parts of glaze, and the surface material comprises the following main raw materials of: in parts by mass, 0-30 parts of the aggregate, 0-4 parts of the bonding base material, 0-4 parts of the liquid glue, 0-2 parts of the glaze and 0-4 parts of color materials; the bonding base material is one or more of bentonite and clay, and the liquid glue is one or more of a silica sol solution, a polyacrylamide solution and a guar gum solution. Correspondingly, the invention discloses a preparation method of the sintered water-permeable brick. The water-permeable brick has high strength, strong frost resistance and excellent water permeability, particles or fiber substances in rainwater and other sewage are not hung on walls easily, and hole gaps of the water-permeable brick are not easily blocked.

Description

technical field [0001] The invention relates to the technical field of permeable bricks, in particular to a sintered permeable brick which is not easily blocked and a preparation method thereof. Background technique [0002] Permeable bricks are a new century-old environmentally friendly building material that was born to alleviate urban waterlogging, maintain water, maintain urban ecological balance and build a sponge city. It uses solid waste such as waste tiles (waste polished tiles, waste polished glazed tiles, waste tiles, etc.), stone fragments, slag, etc. , fired at high temperature, is a green environmental protection product. [0003] Permeable bricks can consume a large amount of waste tiles (solid waste such as stone fragments or slag), which not only solves the problem of solid waste treatment at this stage, but also greatly reduces environmental pollution. The produced ceramic permeable bricks can be directly used in urban construction, turning waste into trea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/132C04B33/138C04B33/135
CPCC04B33/1321C04B33/1324C04B33/135C04B33/138C04B2235/3418C04B2235/96Y02P40/60
Inventor 林智黄飞
Owner KEDA INDUSTRIAL GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products