Pre-treatment method for improving inkjet printing definition of polyester fabric

A polyester fabric and inkjet printing technology, which is applied in fiber treatment, dyeing, textiles and papermaking, etc., can solve the problems of synthetic fiber floor mat inkjet printing products bleeding, poor color vividness, poor color vividness, etc. , to achieve the effect of improving water holding capacity and color fastness, overcoming low clarity and improving clarity

Inactive Publication Date: 2018-06-22
JINHUA JIELING HOUSE WARES CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the biggest defect of inkjet printing for synthetic fiber floor mats is that the product has serious bleeding phenomenon, the pattern definition is not high, the color brightness is poor, and the color fastness to washing and rubbing is not ideal.
Due to the smooth surface of polyester fabric and no active groups, ink droplets in inkjet printing can easily diffuse along the fibers, resulting in blurred printing patterns. High, poor color vividness, becoming a bottleneck in the development of textile inkjet printing technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of improved polyester fabric (230g / m 2 The pretreatment method of the clarity of polyester warp-knitted fabric) inkjet printing comprises the steps of: applying the pretreatment agent to the surface of the polyester fabric by a padding method, drying at 100°C after pre-drying at 40°C for 0.5h, and obtaining Pretreated polyester fabrics can be used for inkjet printing.

[0036] The concentration of the pretreatment agent is to apply 800mg pretreatment agent per square meter of polyester fabric.

[0037] The pH value of the pretreatment agent is 9. The squeeze rate of the padding method is 65%.

[0038] The pretreatment agent is composed of the following components by mass percentage: cationic modified nano-oxide dispersion 20%, antistatic agent 1%, defoamer 3%, viscosity regulator 10%, thickener 1%, wetting agent 1%, light fastness improving agent 2%, and the balance is water.

[0039] The cation-modified nano-oxide dispersion is prepared by cation-modifying t...

Embodiment 2

[0050] A kind of improved polyester fabric (230g / m 2A pretreatment method for inkjet printing definition of polyester warp knitted fabric) comprises the steps of: applying a pretreatment agent to the surface of polyester fabric by padding method, pre-drying at 50° C. for 1 hour and then drying at 150° C. to obtain the pretreatment Treated polyester fabrics can be used for inkjet printing.

[0051] The concentration of the pretreatment agent is to apply 1500mg pretreatment agent per square meter of polyester fabric.

[0052] The pH value of the pretreatment agent is 10. The squeeze rate of the padding method is 80%.

[0053] The pretreatment agent is composed of the following components by mass percentage: cationic modified nano-oxide dispersion 35%, antistatic agent 2%, defoamer 4%, viscosity regulator 25%, thickener 5%, wetting agent 5%, light fastness improving agent 3%, and the balance is water.

[0054] The cation-modified nano-oxide dispersion is prepared by cation-mo...

Embodiment 3

[0065] A kind of improved polyester fabric (230g / m 2 The pretreatment method of the clarity of polyester warp-knitted fabric) inkjet printing comprises the following steps: adopting the padding method to apply the pretreatment agent to the surface of the polyester fabric, pre-drying at 45°C for 0.8h and then drying at 130°C to obtain Pretreated polyester fabrics can be used for inkjet printing.

[0066] The concentration of the pretreatment agent is to apply 1100mg pretreatment agent per square meter of polyester fabric.

[0067] The pH value of the pretreatment agent is 9. The squeeze rate of the padding method is 70%.

[0068] The pretreatment agent is composed of the following components by mass percentage: cationic modified nano-oxide dispersion 25%, antistatic agent 1.5%, defoamer 3.5%, viscosity regulator 15%, thickener 3%, wetting agent 3%, light fastness improving agent 2.5%, and the balance is water.

[0069] The cation-modified nano-oxide dispersion is prepared b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a pre-treatment method for improving inkjet printing definition of polyester fabric. The pre-treatment method comprises the following steps: applying pre-treatment agent to thesurface of the polyester fabric by adopting a padding method, pre-baking for 0.5 to 1 hour at 40 to 50 DEG C, and drying at 100 to 150 DEG C to obtain pre-treated polyester fabric which can be used for inkjet printing. The concentration of the pre-treatment agent is that 800 to 1,500 mg pre-treatment agent is applied to each square meter of the polyester fabric; the pH value of the pre-treatmentagent is 9 to 10. The mangle expression of the padding method is 65 to 80 percent; the water holding property and the colour fastness of the polyester fabric can be improved by the pre-treatment method; when a colour is fixed by steaming, imbibing and swelling can be performed effectively, which is beneficial for a dye or a pigment to diffuse to fibres; the defect that the definition of printed patterns is not high caused by the effects, such as ink permeating and bleeding, is overcome; the definition of paint and ink ink-jet printing of the polyester fabric are improved; the hand feeling of the polyester fabric can be maintained; the printed colour is brighter.

Description

technical field [0001] The invention relates to the technical field of digital printing, in particular to a pretreatment method for improving the clarity of polyester fabric inkjet printing. Background technique [0002] Digital printing technology is a relatively promising printing technology. It is possible to transform the traditional textile industry by applying its scientific and technological achievements, and realize leapfrog development. In recent years, digital inkjet printing technology has developed rapidly inside and outside the circle, and it is called "a revolution in printing technology". Dadi satisfies the user's requirements for small batches, multiple designs and fast delivery. Moreover, its product quality and style can fully embody people-oriented, achieve fashion, personalization, high-tech, high-quality level, and meet the requirements of special handicrafts. [0003] At present, the biggest defect of inkjet printing for synthetic fiber floor mats is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/79D06M15/263D06M15/333D06M15/356D06M15/53D06M15/564D06M15/643D06P3/52D06P5/30D06M101/32
CPCD06M11/79D06M15/263D06M15/333D06M15/3562D06M15/53D06M15/564D06M15/643D06M2101/32D06M2200/50D06P3/52D06P5/30
Inventor 金淑兰高宁邓永俊丁琳洪鹏翔陈维国江华郑今欢
Owner JINHUA JIELING HOUSE WARES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap