High-performance steel-based copper alloy graphite composite material

A composite material, copper alloy technology, applied in the direction of analyzing materials, testing material hardness, testing wear resistance, etc. It does not have the problems of corrosion resistance, wear resistance and seizure resistance, and achieves the effect of excellent interface, high strength and reduced porosity

Inactive Publication Date: 2018-06-29
ZHEJIANG WANZHONG MACHINERY MFG
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Not only that, but under certain special working conditions, such as high temperature, high vacuum, high load, and conditions that limit the use of lubricants such as damaging grease, the bearing is also required to have a self-lubricating function, which makes copper-based self-lubricating Composite materials have become a research hotspot, but the existing steel-based copper alloy graphite composite materials do not have optimized wear resistance and lubrication resistance, cannot improve the strength and corrosion resistance of the running-in layer, and cannot prevent corrosion and increase The role of mechanical strength cannot improve the performance of copper, cannot prolong its service life, and does not have good corrosion resistance, wear resistance and seizure resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance steel-based copper alloy graphite composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1: as figure 1 Shown, the present invention provides a kind of high performance steel base copper alloy graphite composite material, the preparation raw material of the material in the described steel base copper alloy graphite self-lubricating composite material comprises: Sn, graphite, Ni, Cu, boron and Fe, wherein The mass percentages of the raw materials for the preparation of the steel-based copper alloy graphite self-lubricating composite material are: Sn: 6%, graphite: 9%, Ni: 11%, Cu: 34%, boron: 0.005% and Fe: 48%.

[0020] According to the above technical scheme, the preparation method of the high-performance steel-based copper alloy graphite composite material comprises the following steps:

[0021] 1) Performance analysis: SEM, EDS, XRD, HRTEM and other analytical methods are used to analyze the phase composition of graphite, nickel, and boron, and electronic universal testing machines, hardness testers, density meters, and friction and wear testi...

Embodiment 2

[0029] Embodiment 2: as figure 1 Shown, the present invention provides a kind of high performance steel base copper alloy graphite composite material, the preparation raw material of the material in the described steel base copper alloy graphite self-lubricating composite material comprises: Sn, graphite, Ni, Cu, boron and Fe, wherein The mass percentages of raw materials for the preparation of the steel-based copper alloy graphite self-lubricating composite material are: Sn: 4%, graphite: 7%, Ni: 9%, Cu: 34%, boron: 0.05%wt and Fe: 48%.

[0030] According to the above technical scheme, the preparation method of the high-performance steel-based copper alloy graphite composite material comprises the following steps:

[0031] 1) Performance analysis: SEM, EDS, XRD, HRTEM and other analytical methods are used to analyze the phase composition of graphite, nickel, and boron, and electronic universal testing machines, hardness testers, density meters, and friction and wear testing m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-performance steel-based copper alloy graphite composite material. The steel-based copper alloy graphite self-lubricating composite material is prepared from the following raw materials of, by mass, 4-6% of Sn, 7-9% of graphite, 9-11% of Ni, 34-36% of Cu, 0.005-0.05%wt of boron and 45-48% of Fe. A preparation method comprises the following steps of performance analysis, Ag-Sn particle preparation and composite material preparation. The composite material is mainly composed of copper and alloy elements as main body and the external graphite, the copper-based graphite composite material has the heat conductivity, wear resistance, the high strength, arc erosion resistance and the like of the copper alloy substrate, and has the good lubricating property of the graphite and further has the good lubricating property of the graphite under the high temperature less than or equal to 500 DEG C, the composite material is widely applied to oil-free or oil-less workingcondition conditions, the performance of a copper material can be improved, the service life of the copper material can be prolonged, the problem that the wettability of the graphite and a matrix ispoor is solved through the combination of the graphite, nickel and the boron, the interfaces of the copper alloy graphite and the steel matrix are improved to realized good combination.

Description

technical field [0001] The invention relates to the technical field of steel-based copper alloy graphite composite materials, in particular to a high-performance steel-based copper alloy graphite composite material. Background technique [0002] As people's pace of life becomes faster and faster, the requirements for bearing materials are also higher and higher. In many aspects, low-speed, low-load bearings can no longer meet people's requirements, and high-speed, high-load bearings will inevitably occupy an important role in the future. Therefore, due to its poor wear resistance and fatigue performance, aluminum-based alloys will be greatly restricted in use, and copper-based alloys will show their superiority. Not only that, but under certain special working conditions, such as high temperature, high vacuum, high load, and conditions that limit the use of lubricants such as damaging grease, the bearing is also required to have a self-lubricating function, which makes coppe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C30/04C22C30/02C22C32/00G01N33/00G01N3/40G01N3/56G01N9/00
CPCG01N3/40G01N3/56G01N9/00G01N33/00C22C30/02C22C30/04C22C32/0084C22C38/002C22C38/008C22C38/08C22C38/16G01N33/0003
Inventor 方灿根
Owner ZHEJIANG WANZHONG MACHINERY MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap