Preparation method of polypyrrole conducting material

A conductive material, polypyrrole technology, applied in cable/conductor manufacturing, circuits, electrical components, etc., can solve the problems of low conductivity stability of materials, poor compatibility between polypyrrole and carbon nanotubes, poor stability and mechanical properties, etc. , to achieve good electrical conductivity, improve oxidation resistance, and high electrical conductivity

Inactive Publication Date: 2018-07-06
宿州市微腾知识产权运营有限公司
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the stability and mechanical properties of conductive polypyrrole materials are poor. In order to improve and enhance the performance of polypyrrole, a large number of researchers have focused on the composite of polypyrrole and other materials. In recent years, the composite of carbon materials such as carbon nanotubes has been widely used. Expanded, the research results show that the composite with carbon nanotubes can greatly improve the performance of supercapacitors, but the compatibility between polypyrrole and carbon nanotubes is poor, and the conductive stability of the composite material is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method of polypyrrole conductive material, comprising the following steps:

[0021] (1) Take 2-mercaptobenzimidazole, add it to 14 times the weight of absolute ethanol, stir evenly, add pyrrole, raise the temperature to 55°C, keep stirring for 30 minutes, distill and remove ethanol to obtain pretreated pyrrole single body;

[0022] (2) Get initiator, join in the deionized water of its weight 40 times, stir;

[0023] (3) Take light calcium carbonate, add it to 13 times its weight in deionized water, add an amination reagent, raise the temperature to 75°C, heat and stir for 2 hours to obtain an amination solution;

[0024] (4) Get zinc acetylacetonate, join in the dimethylformamide of its weight 7 times, stir evenly, obtain amide solution;

[0025] (5) Get p-toluenesulfonic acid, mix it with the pretreated pyrrole monomer, add it to deionized water with 15 times the weight of the mixture, stir evenly, send it into the reaction kettle, add the above-mention...

Embodiment 2

[0029] A preparation method of polypyrrole conductive material, comprising the following steps:

[0030] (1) Take 2-mercaptobenzimidazole, add it to 10 times the weight of absolute ethanol, stir evenly, add pyrrole, increase the temperature to 50°C, keep stirring for 20 minutes, distill and remove ethanol to obtain pretreated pyrrole mono body;

[0031] (2) Get initiator potassium persulfate, join in the deionized water of its weight 30 times, stir;

[0032] (3) Take light calcium carbonate, add it to deionized water 10 times its weight, add an amination reagent, raise the temperature to 60° C., keep stirring for 1 hour, and obtain an amination solution;

[0033] (4) Get zinc acetylacetonate, join in the dimethylformamide of its weight 5 times, stir evenly, obtain amide solution;

[0034] (5) Take p-toluenesulfonic acid, mix it with the pretreated pyrrole monomer, add it to deionized water 10 times the weight of the mixture, stir evenly, send it into the reaction kettle, add...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a polypyrrole conducting material. According to the preparation method, effective dispersion of calcium carbonate in polypyrrole is realized, so that the mechanical stability of a finished-product material is improved. The material has the advantages of light weight, good uniform stability, long service life, high conducting performance and excellentcomprehensive performance.

Description

technical field [0001] The invention belongs to the field of conductive materials, and in particular relates to a preparation method of polypyrrole conductive materials. Background technique [0002] Polypyrrole is a common black, insoluble, infusible, and conductive polymer. Polypyrrole is usually obtained by oxidative polymerization of pyrrole monomers. Electrochemical anodic oxidation of pyrrole is also an effective means of preparing polypyrrole; polypyrrole can be used in biology, ion detection, ultra- Capacitor and antistatic materials, modified electrodes for photoelectrochemical cells, and electrode materials for storage batteries. In addition, it can also be used as electromagnetic shielding material and gas separation membrane material, used in electrolytic capacitors, electrocatalysis, conductive polymer composite materials, etc. It has a wide range of applications and has attracted people's attention since it was discovered. [0003] However, the stability and m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G73/06C08K9/04C08K3/26C08K5/42H01B13/00
CPCC08G73/0611C08K3/26C08K5/42C08K9/04C08K2003/265H01B13/00
Inventor 许美凤
Owner 宿州市微腾知识产权运营有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap