Aqueous low-energy cold-light-source curing wood floor coating material and manufacturing method thereof

A technology of cold light source curing and manufacturing method, applied in epoxy resin coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of high energy consumption, environmental pollution, and human harm of UV coatings, and achieve fast curing speed , high efficiency and low energy consumption

Inactive Publication Date: 2018-07-20
FOSHAN GAOMING SUN YICAI COATING
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional UV coatings that cure resins through ultraviolet light consume a lot of energy, and UV coatings will generate a lot of ozone during the curing process, which is very polluting to the environment and harmful to the human body.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0066] Described preparation method:

[0067] Put water-soluble aliphatic urethane hexaacrylate, water-soluble modified epoxy acrylate, and water-based dispersant into the container, and disperse with a disperser at a speed of 600-800rpm / min for 3-7min until uniformly mixed; then put in Alcohol, water-based fumed silica, matting powder, water-based wax paste, wear-resistant powder, water-based photoinitiator, water-based defoamer, deionized water, water-based leveling agent, water-based wetting agent and bactericide, with a disperser in the Disperse for 10-20min at a rotational speed of 1200-1500 rpm / min, and take samples for inspection; when the fineness reaches ≤20 microns, scrape the paint on a glass plate without shrinkage and add additives, and disperse at a rotational speed of 600-800rpm / min After 3-7 minutes, after mixing evenly, a water-based low-energy cold light source curing wood floor coating and a manufacturing method thereof are obtained.

[0068] Preferably, in...

Embodiment 1

[0089] The present invention provides a water-based low-energy cold light source curing wood floor coating and a manufacturing method thereof, wherein the water-based low-energy cold light source curing wood floor coating and its manufacturing method are composed of the following components in weight percentage:

[0090] Water-soluble aliphatic polyurethane hexaacrylate: 38%;

[0091] Water-soluble modified epoxy acrylate: 22%;

[0092] Water-based dispersant: 0.3%;

[0093] Alcohol: 10%;

[0094] Aqueous fumed silicon dioxide: 0.3%;

[0095] Matting powder: 3%;

[0096] Water-based wax slurry 2%;

[0097] Wear-resistant powder 5%;

[0098] Water-based photoinitiator: 3.5%;

[0099] Water-based defoamer: 0.3%;

[0100] Water-based leveling agent: 0.3%;

[0101] Water-based wetting agent 0.3%;

[0102] Deionized water: 14.9%;

[0103] Fungicide 0.1%;

[0104] The present invention also provides a water-based low-energy cold light source curing wood floor coating and ...

Embodiment 2

[0108] The present invention provides a water-based low-energy cold light source curing wood floor coating and a manufacturing method thereof, wherein the water-based low-energy cold light source curing wood floor coating and its manufacturing method are composed of the following components in weight percentage:

[0109] Water-soluble aliphatic polyurethane hexaacrylate: 38%;

[0110] Water-soluble modified epoxy acrylate: 22%;

[0111] Water-based dispersant: 0.3%;

[0112] Alcohol: 10%;

[0113] Aqueous fumed silicon dioxide: 0.3%;

[0114] Matting powder: 3%;

[0115] Water-based wax slurry 2%;

[0116] Wear-resistant powder 5%;

[0117] Water-based photoinitiator: 3.5%;

[0118] Water-based defoamer: 0.3%;

[0119] Water-based leveling agent: 0.3%;

[0120] Water-based wetting agent 0.3%;

[0121] Deionized water: 14.9%;

[0122] Fungicide 0.1%;

[0123] Among them, the liquid photoinitiator of the water-based photoinitiator ketone hydrogen abstraction cracking ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous low-energy cold-light-source curing wood floor coating material and a manufacturing method thereof, wherein the aqueous low-energy cold-light-source curing wood floor coating material is prepared from the following raw materials by weight: 38% of water-soluble aliphatic polyurethane hexaacrylate, 22% of water-soluble modified epoxy acrylate, 0.3% of an aqueous dispersant, 10% of alcohol, 0.3% of aqueous gas phase silicon dioxide, 3% of matting powder, 2% of aqueous wax slurry, 5% of wear-resistant powder, 3.5% of an aqueous photoinitiator, 0.3% of an aqueousdefoamer, 0.3% of an aqueous leveling agent, 0.3% of an aqueous wetting agent, 14.9% of deionized water, and 0.1% of a fungicide. According to the present invention, the aqueous low-energy cold-light-source curing wood floor coating material can achieve the low-energy-consumption UV LED (light emitting diode) low-energy curing coating material, does not produce ozone, does not contain mercury, hascharacteristics of no environment pollution, no harm to human body, fast curing and high efficiency, and uses water as the diluent so as to achieve the environmental protection.

Description

technical field [0001] The invention relates to a water-based cold light source curing coating, in particular to a water-based low-energy cold light source curing wood floor coating and a manufacturing method thereof. Background technique [0002] Traditional UV coatings that cure resins through ultraviolet light consume a lot of energy, and UV coatings will generate a large amount of ozone during the curing process, which is very polluting to the environment and harmful to the human body. Contents of the invention [0003] The object of the present invention is to provide a water-based low-energy cold light source curing wood floor coating and a manufacturing method thereof in view of the above-mentioned deficiencies in the prior art. [0004] Technical scheme of the present invention is realized like this: [0005] A water-based low-energy cold light source curing wood floor coating and a manufacturing method thereof are made of the following raw materials in parts by w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D163/10C09D7/61C09D7/65C09D7/20
Inventor 陈友江
Owner FOSHAN GAOMING SUN YICAI COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com