Hydration heat regulation composition, as well as preparation method and application thereof
A composition and heat of hydration technology, applied in the field of concrete admixtures, can solve the problems of reduced concrete strength, reduced concrete durability, poor effect, etc., and achieve the effects of reducing corrosion, reducing heating and cooling rates, and improving safety
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0041] Example 1. Preparation of cationic acrylic resin
[0042] A. Mix 9 parts of methyl methacrylate, 7 parts of hydroxyethyl acrylate, 7 parts of isooctyl acrylate and 2 parts of butyl acetate hair agent to obtain a mixture;
[0043] B. Add 1 / 2 of the mixture obtained in step A to 11 parts of n-butanol and stir to dissolve, then heat to 118°C, and after heating for 22 minutes, add the mixture obtained in the remaining step A dropwise at a rate of 0.4g / min. After the addition is complete, the temperature is raised to 120°C and the reaction is kept for 2 hours to obtain the polymer, and the n-butanol is recovered under reduced pressure;
[0044] C. Add 26 parts of diisocyanate to the polymer obtained in step B, raise the temperature to 75°C, keep the temperature for 2h, then cool to 48°C, add 26 parts of pentaerythritol, then add 0.03 part of stannous octoate, heat up to 80°C, keep the temperature for reaction 2h, get the chain-extended prepolymer;
[0045] D When the temperature of...
Example Embodiment
[0047] Example 2. Preparation of modified diatomite
[0048] a. Dry the diatomaceous earth, pass a 100-mesh sieve to obtain a fine powder, and then add it to hydrochloric acid with a volume concentration of 8%. The solid-to-liquid ratio of the fine powder to the hydrochloric acid is 1g:2mL, and the reaction is heated to 110°C for 3h, Cool, wash with water to neutral, and dry to obtain acid diatomaceous earth powder;
[0049] b. Dissolve xylitol in water and stir until it is completely dissolved, then add the acid diatomaceous earth powder obtained in step a and stir, the weight ratio of the xylitol to acid diatomaceous earth powder is 6:1, forming a uniform colloid Shape, dry, grind, and get.
Example Embodiment
[0050] Example 3. A hydration heat control composition
[0051] The hydration heat control composition consists of the following components and their parts by weight:
[0052] 48 parts of cationic acrylic resin, 14 parts of amino resin, 5 parts of epoxy phosphate, 8 parts of tartaric acid and 18 parts of modified diatomaceous earth; the cationic acrylic resin is the cationic acrylic resin prepared in Example 1. The modified diatomaceous earth is the modified diatomaceous earth prepared in Example 2.
[0053] Preparation:
[0054] S1 first take cationic acrylic resin, amino resin and epoxy phosphate and stir evenly to obtain a mixture;
[0055] In S2, the tartaric acid and the modified diatomaceous earth are evenly stirred, and then added to the mixture obtained in step S1 and mixed uniformly, and the granules are sized and passed through 10 to 60 meshes to obtain.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap