Anticorrosive paint for power distribution cabinet and preparation method thereof

A coating and cabinet protection technology, applied in the field of anti-corrosion coatings for power distribution cabinets and their preparation, can solve the problems of short service life, easy to be corroded, rusted, etc., to improve anti-corrosion ability, prevent corrosion and rust, prolong The effect of the service life

Inactive Publication Date: 2018-07-31
NANTONG NINGHAI MACHINE ELECTRIC APPLIANCES CO LTD
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing power distribution cabinet body has poor oxidation resistance and is easily corroded and rusted, resulting in a short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] An anticorrosion coating for a power distribution cabinet, comprising in parts by weight:

[0056] Calcium borophosphate 15 parts;

[0057] 5 parts of bisphenol A / F epoxy emulsion;

[0058] 15 parts of titanium dioxide;

[0059] 20 parts of epoxy acrylate resin;

[0060] 12 parts of polytetrafluoroethylene;

[0061] 5 parts of oxidized polyethylene wax;

[0062] 4 parts of silica powder;

[0063] Potassium octatitanate 12 parts;

[0064] 3 parts of polyethylene terephthalate;

[0065] 8 parts of aluminum tripolyphosphate;

[0066] 6 parts of hydroxyethyl methacrylate;

[0067] 10 parts of talcum powder;

[0068] Sodium hydroxymethyl cellulose 15 parts.

[0069] The coating method of preparing this formula is: comprise the following steps,

[0070] S1. First mix the calcium borophosphate, bisphenol A / F epoxy emulsion, titanium dioxide, epoxy acrylate resin, polytetrafluoroethylene and oxidized polyethylene wax materials in the above formula, and put them into ...

Embodiment 2

[0074] An anticorrosion coating for a power distribution cabinet, comprising in parts by weight:

[0075] Calcium borophosphate 32 parts;

[0076] 17 parts of bisphenol A / F epoxy emulsion;

[0077] 24 parts of titanium dioxide;

[0078] 27 parts of epoxy acrylate resin;

[0079] 19 parts of polytetrafluoroethylene;

[0080] 11 parts of oxidized polyethylene wax;

[0081] 12 parts of silica powder;

[0082] Potassium octatitanate 19 parts;

[0083] 4 parts of polyethylene terephthalate;

[0084] 16 parts of aluminum tripolyphosphate;

[0085] 10 parts of hydroxyethyl methacrylate;

[0086] 15 parts of talcum powder;

[0087] Sodium hydroxymethylcellulose 18 parts.

[0088] The coating method of preparing this formula is: comprise the following steps,

[0089] S1. First mix the calcium borophosphate, bisphenol A / F epoxy emulsion, titanium dioxide, epoxy acrylate resin, polytetrafluoroethylene and oxidized polyethylene wax materials in the above formula, and put them i...

Embodiment 3

[0093] An anticorrosion coating for a power distribution cabinet, comprising in parts by weight:

[0094] Calcium borophosphate 54 parts;

[0095] 25 parts of bisphenol A / F epoxy emulsion;

[0096] 29 parts of titanium dioxide;

[0097] 35 parts of epoxy acrylate resin;

[0098] 19 parts of polytetrafluoroethylene;

[0099] 21 parts of oxidized polyethylene wax;

[0100] 22 parts of silica powder;

[0101] 28 parts of potassium octatitanate;

[0102] 6 parts of polyethylene terephthalate;

[0103]17 parts of aluminum tripolyphosphate;

[0104] 14 parts of hydroxyethyl methacrylate;

[0105] 21 parts of talcum powder;

[0106] 23 parts of sodium hydroxymethyl cellulose.

[0107] The coating method of preparing this formula is: comprise the following steps,

[0108] S1. First mix the calcium borophosphate, bisphenol A / F epoxy emulsion, titanium dioxide, epoxy acrylate resin, polytetrafluoroethylene and oxidized polyethylene wax materials in the above formula, and put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application discloses anticorrosive paint for a power distribution cabinet and a preparation method thereof. The anticorrosive paint is prepared from the following raw materials in parts by weight: 15 to 78 parts of calcium borophosphate, 5 to 28 parts of bisphenol A / F epoxy emulsion, 15 to 35 parts of titanium dioxide, 20 to 40 parts of epoxy acrylate resin, 12 to 24 parts of polytetrafluoroethylene, 5 to 25 parts of oxidized polyethlene wax, 4 to 29 parts of silica powder, 12 to 33 parts of potassium octatitanate, 3 to 8 parts of polyterephthalyl alcohol, 8 to 25 parts of aluminum triphosphate, 6 to 16 parts of hydroxyethyl methylacrylate, 10 to 25 parts of talcum powder and 15 to 25 parts of sodium carboxymethyl cellulose. In this way, the anticorrosive paint for the power distribution cabinet, which is provided by the invention, can be used for being coated on the surface of the power distribution cabinet, and can be used for preventing the power distribution cabinet from beingcorroded and rusting; the anticorrosive capacity of the power distribution cabinet is improved, and the service life is prolonged.

Description

technical field [0001] The invention relates to coatings, in particular to an anti-corrosion coating for a power distribution cabinet and a preparation method thereof. Background technique [0002] The existing power distribution cabinet body has poor oxidation resistance and is easily corroded and rusted, resulting in a short service life. Contents of the invention [0003] The object of the present invention is to provide an anti-corrosion coating for a distribution cabinet and a preparation method thereof, which can solve one or more of the above-mentioned problems in the prior art. [0004] A kind of anticorrosion paint of distribution cabinet of the present invention comprises by weight parts: [0005] Calcium borophosphate 15-78 parts; [0006] Bisphenol A / F epoxy emulsion 5-28 parts; [0007] 15-35 parts of titanium dioxide; [0008] 20-40 parts of epoxy acrylate resin; [0009] 12-24 parts of polytetrafluoroethylene; [0010] 5-25 parts of oxidized polyethyle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D163/00C09D127/18C09D101/28C09D5/08C09D7/61
CPCC09D163/10C08K2003/2241C08L2205/035C09D5/08C09D7/61C08L63/00C08L27/18C08L1/284C08K13/02C08K3/38C08K3/22C08K3/36C08K3/24
Inventor 刘佩来
Owner NANTONG NINGHAI MACHINE ELECTRIC APPLIANCES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com