Full-penetration polished ceramic tiles and preparation method thereof

A ceramic tile and water reducing agent technology, applied in the field of building decoration materials, can solve the problems of impermeability, poor gloss, unobvious surface layer, and not very good simulation effect, etc., to achieve realistic stone-like effect, radioactivity does not exceed the standard, The effect of improving flow properties

Inactive Publication Date: 2018-08-03
HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, at present, the polished tiles are mainly polished after being clothed by traditional cloth distribution equipment. The formula process is relatively simple. , poor gloss

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A fully transparent polished ceramic tile, in parts by weight, the fully transparent polished ceramic tile mainly includes the following components:

[0049] 22 parts of ball soil;

[0050] Albite 12 parts;

[0051] 5 parts of quartz powder;

[0052] 8 parts wollastonite;

[0053] Water ground potassium feldspar powder 4 parts

[0054] 1 part water glass;

[0055] 0.4 parts of water reducer;

[0056] Green body strengthening agent 0.3 parts;

[0057] 44 parts of deionized water.

[0058] Wherein, the water reducer is a polycarboxylate water reducer.

[0059] Wherein, the body strengthening agent is one or more of sodium carboxymethylcellulose, polyvinyl alcohol, polyvinyl butyral and polyethylene glycol.

[0060] The present invention also provides a preparation method of fully transparent polished tiles, comprising the following steps:

[0061] Step 1: Raw material preparation: each raw material is weighed according to the prescribed number of parts, and mixed...

Embodiment 2

[0071]A fully transparent polished ceramic tile, in parts by weight, the fully transparent polished ceramic tile mainly includes the following components:

[0072] 42 parts of ball soil;

[0073] Albite 18 parts;

[0074] 12 parts of quartz powder;

[0075] 15 parts of wollastonite;

[0076] Water ground potassium feldspar powder 7 parts

[0077] 4 parts water glass;

[0078] 0.8 parts of water reducing agent;

[0079] Green body reinforcing agent 0.6 part;

[0080] 70 parts of deionized water.

[0081] Wherein, the water reducer is a polycarboxylate water reducer.

[0082] Wherein, the body strengthening agent is one or more of sodium carboxymethylcellulose, polyvinyl alcohol, polyvinyl butyral and polyethylene glycol.

[0083] The present invention also provides a preparation method of fully transparent polished tiles, comprising the following steps:

[0084] Step 1: Raw material preparation: each raw material is weighed according to the prescribed number of parts, ...

Embodiment 3

[0094] A fully transparent polished ceramic tile, in parts by weight, the fully transparent polished ceramic tile mainly includes the following components:

[0095] 30 parts of ball soil;

[0096] Albite 15 parts;

[0097] 8.5 parts of quartz powder;

[0098] 11.5 parts of wollastonite;

[0099] Water ground potassium feldspar powder 5.5 parts

[0100] 2.05 parts of water glass;

[0101] 0.6 parts of water reducer;

[0102] Green body strengthening agent 0.5 part;

[0103] 57 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flexural strengthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses full-penetration polished ceramic tiles and a preparation method thereof. The full-penetration polished ceramic tiles are mainly prepared from the following components in partsby weight: 22 to 42 parts of ball clay, 12 to 18 parts of soda feldspar, 5 to 12 parts of ground quartz, 8 to 15 parts of wollastonite, 4 to 7 parts of water milled potassium feldspar powder, 1 to 4parts of sodium silicate, 0.4 to 0.8 part of water reducing agent, 0.3 to 0.6 part of blank enhancing agent and 44 to 70 parts of de-ionized water. The preparation method comprises the following steps: preparing raw materials, carrying out ball milling, spraying and granulating, punching and molding, calcining and polishing. According to the full-penetration polished ceramic tiles prepared by thepreparation method, the problems of traditional polished tiles that the surface level, stereoscopic performance and stone-imitating effect are fuzzy and unclear are solved; application of ultra-penetration materials is researched and developed so that the stone-imitating effect is more vivid; meanwhile, the full-penetration polished ceramic tiles have relatively good anti-penetration performance and color and luster; the preparation method is simple and is suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of building decoration materials, in particular to a transparent polished ceramic tile and a preparation method thereof. Background technique [0002] Polished brick is a kind of whole body brick. It is a kind of bright brick made by grinding the surface of the whole body brick body. It is a new decorative ceramic material that is very popular at home and abroad in recent years. The whole body brick is much smoother. [0003] Compared with natural stone, polished tiles have no radioactive elements. Natural stone is mineral and has not been sintered at high temperature, so it contains individual trace radioactive elements. Long-term exposure will be harmful to human body; polished tiles are harmless to human body; The color difference between different shades is large, the polished tiles are carefully prepared, the design and color of the same batch of products are consistent, and there is basically no color...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13
CPCC04B33/13C04B33/1305C04B33/131C04B35/6316C04B35/63416C04B35/6342C04B35/63488C04B35/6365C04B2235/3418C04B2235/3436C04B2235/3472
Inventor 王磊
Owner HEFEI YAKELI NEW BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More